pt-ni-cu ternary alloy loading ceo 2 Preparation of Composite Material and Study on Its Catalytic Performance of Formic Acid

A pt-ni-cu, ternary alloy technology is applied in the preparation and application of alloy-supported CeO2 functional materials, which can solve the problems of easy poisoning and low utilization efficiency per unit mass, and achieve improved stability and excellent area ratio activity. , the effect of high mass specific activity

Active Publication Date: 2020-12-08
UNIV OF JINAN
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the above-mentioned technical problems, the present invention solves the technical problems such as low utilization efficiency per unit mass and easy poisoning of current Pt nanostructure catalysts, and prepares a Pt-Ni-Cu ternary alloy loaded with CeO 2 Preparation method to improve the performance of Pt-based nanostructured catalysts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • pt-ni-cu ternary alloy loading ceo <sub>2</sub> Preparation of Composite Material and Study on Its Catalytic Performance of Formic Acid
  • pt-ni-cu ternary alloy loading ceo <sub>2</sub> Preparation of Composite Material and Study on Its Catalytic Performance of Formic Acid
  • pt-ni-cu ternary alloy loading ceo <sub>2</sub> Preparation of Composite Material and Study on Its Catalytic Performance of Formic Acid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A Pt-Ni-Cu Ternary Alloy Supporting CeO 2 The experimental steps of the preparation method are as follows:

[0024] (1) Thoroughly ultrasonically disperse the original solution of 1 mL oleylamine corresponding to 3.44 mg CeO2, add (a) 0 mL (b) 0.07 mL (c) 0.2 mL and (d) 0.3 mL respectively to centrifuge tubes, centrifuge, and use Pipette the supernatant until only the precipitate remains, add 0.7 mL ethanolamine to ultrasonically disperse to make it evenly dispersed;

[0025] (2) Weigh 303.4 mg of glycine, 200 mg of polyvinylpyrrolidone (PVP), and 300 mg of sodium iodide into a clean beaker;

[0026] (3) Add 2 mL of 20 mM H 2 PtCl 6 aqueous solution, 1 mL of 20 mM CuCl 2 aqueous solution, 1 mL of 20mM NiCl 2 The aqueous solution is added into the beaker of the sample in step (2), and the fully dispersed CeO-containing 2 Add ethanolamine to the above beaker, stir for 24 h until the solution is blue and transparent, pipette 600 µL (40%) formaldehyde solution, slowly...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a Pt-Ni-Cu ternary alloy loaded with CeO 2 preparation and catalytic performance studies. The present invention utilizes the microwave thermal method to synthesize Pt-Ni-Cu ternary metal alloy loaded ceria nanoparticles in one step. Specifically, CeO can be synthesized by adding formaldehyde 2 Inducing surface voids during the formation of concave octahedral Pt‑Ni‑Cu alloys not only preserves the morphology of the Pt‑Ni‑Cu ternary metal, but also allows the resulting nanoparticles to continue to exhibit The excellent area specific activity also fully guarantees the utilization efficiency of metal atoms. Surprisingly, it is found that on the basis of the particle size being significantly larger than that of commercial Pt-based catalysts, it can also achieve a higher mass specific activity than commercial catalysts, which significantly improves the catalytic performance of noble metals. The utilization efficiency achieves an unexpected technical effect, and can further improve the anti-poisoning ability and electrocatalytic stability of the prepared metal alloy catalysis.

Description

technical field [0001] The invention belongs to the field of functional composite nanometer materials. Specifically, the present invention relates to an alloy loaded CeO 2 Preparation and application of functional materials. Background technique [0002] So far, proton membrane fuel cells have become an efficient energy supply for cars and other portable devices. Pt-based catalysts are still the best catalysts in PEMFC, but the high price of metal platinum is the main reason why proton membrane fuel cells are difficult to produce on a large scale. Therefore, metals of other transition elements are added to form binary or ternary metal alloys to reduce the oxygen adsorption bond energy and reduce costs. For example, in the patent document CN110380068A, PtCuNi ternary alloys are prepared by adjusting the morphology to improve electrocatalytic performance and stability. However, it still faces the problems of high catalyst cost and low actual utilization efficiency of precio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/86H01M4/92H01M8/1009
CPCH01M4/8647H01M4/921H01M4/925H01M8/1009Y02E60/50Y02P70/50
Inventor 李彬生吕一品高道伟杨绍寒陈国柱
Owner UNIV OF JINAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com