Iron oxide-nitrogen-doped carbon microtube composite wave-absorbing material and preparation method thereof

A composite absorbing material and iron oxide technology, applied in the field of absorbing materials, can solve the problems of narrow absorbing frequency range, high density of absorbing materials, poor absorbing performance, etc., achieve excellent absorbing performance, overcome high density , the effect of good application prospects

Active Publication Date: 2022-01-11
SHANDONG UNIV OF SCI & TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] In view of this, the object of the present invention is to provide an iron oxide-nitrogen-doped carbon microtube composite absorbing material and its preparation method, which solves the problems of high density, narrow absorbing frequency range and absorbing problems of traditional iron oxide absorbing materials. The problem of poor performance, and the problem of cumbersome operation during the preparation of carbon-iron oxide composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Iron oxide-nitrogen-doped carbon microtube composite wave-absorbing material and preparation method thereof
  • Iron oxide-nitrogen-doped carbon microtube composite wave-absorbing material and preparation method thereof
  • Iron oxide-nitrogen-doped carbon microtube composite wave-absorbing material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Weigh 0.80g NiCl with electronic balance 2 ·6H 2 O(3.35×10 -3 mol) and 1.36g FeCl 2 4H 2 O(6.75×10 -3 mol), dissolved in 30 mL of deionized water, stirred evenly and then ultrasonicated for 30 minutes. Weigh 0.01 g of melamine foam, soak it in the above metal salt solution, and perform ultrasonic adsorption for 20 minutes. After letting the melamine foam dry naturally, see figure 1 , placed in a tube furnace, and calcined at 850°C for 2 hours in a mixed atmosphere of 99.5% nitrogen + 0.5% oxygen to obtain NiFe 2 o 4 - Nitrogen-doped carbon microtube composites. NiFe 2 o 4 The content in the composite material is 90%. figure 2 For the scanning electron micrograph of composite material synthesized in this embodiment, it can be seen that NiFe 2 o 4 Nanoparticles are uniformly supported on nitrogen-doped carbon microtubes. Adopt X-ray diffractometer to characterize the NiFe that the present invention prepares 2 o 4 -Crystal structure of nitrogen-doped carbo...

Embodiment 2

[0048] Weigh 0.67g Co(NO 3 ) 2 ·6H 2 O(2.3×10- 3 mol) and 1.87g Fe(NO 3 ) 2 9H 2 O(4.6×10- 3 mol), dissolved in 30 mL of deionized water, stirred evenly and then ultrasonicated for 30 minutes. Weigh 0.05 g of melamine foam, soak it in the above metal salt solution, and perform ultrasonic adsorption for 20 minutes. After the melamine foam is naturally dried, it is placed in a tube furnace and calcined at 850°C for 2 hours in a mixed atmosphere of 99.5vol% nitrogen + 0.5vol% oxygen to obtain CoFe 2 o 4 - Nitrogen-doped carbon microtube composites. The content of iron oxide in the composite material is 75%. CoFe 2 o 4 -The nitrogen-doped carbon microtube composite absorbing material has good absorbing performance. At 5.6GHz, the reflection loss peak of the 4mm composite material sample is -30.5dB, and the effective bandwidth of RL<-10dB is 3.9GHz, which can effectively absorb electromagnetic waves in this frequency band.

Embodiment 3

[0050] Weigh 0.33g CuSO with an electronic balance 4 (1.3×10- 3 mol) and 1.05g Fe 2 (SO 4 ) 3 (2.6×10- 3 mol), dissolved in 30 mL of deionized water, stirred evenly and then ultrasonicated for 30 minutes. Weigh 0.05 g of melamine foam, soak it in the above metal salt solution, and perform ultrasonic adsorption for 20 minutes. After the melamine foam is naturally dried, it is placed in a tube furnace and calcined at 750°C for 3 hours in a mixed atmosphere of 99.5vol% nitrogen + 0.5vol% oxygen to obtain CuFe 2 o 4 - Nitrogen-doped carbon microtube composites. The content of iron oxide in the composite material is 80%. The iron oxide-nitrogen-doped carbon microtube composite absorbing material has good absorbing properties. At 4.4GHz, the reflection loss peak of the 4mm composite material sample is -29.5dB, and the effective bandwidth of RL<-10dB is 2.9GHz, which can effectively absorb electromagnetic waves in this frequency band.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an iron oxide-nitrogen-doped carbon microtube composite wave-absorbing material and a preparation method thereof. The preparation method comprises the following steps: S1. dissolving a metal salt containing M ions and iron ions in deionized water, stirring Ultrasonic treatment after homogenization, where the M ion is Cu 2+ 、Ni 2+ 、Co 2+ , Mn 2+ , Zn 2+ , Fe 2+ One or more of them; S2. the melamine foam is placed in the metal salt solution in S1, and the melamine foam is ultrasonically adsorbed to the metal salt solution; S3. the melamine foam that has adsorbed the metal salt is naturally dried, and then placed It is calcined in a tube furnace under a mixed atmosphere containing inert gas and oxygen. The iron oxide-nitrogen-doped carbon microtube composite wave-absorbing material prepared by the invention has excellent wave-absorbing performance, and has good application prospects in the field of electromagnetic wave absorbing materials.

Description

technical field [0001] The invention relates to an iron oxide-nitrogen-doped carbon microtube composite wave-absorbing material and a preparation method thereof, belonging to the field of wave-absorbing materials. Background technique [0002] The application of electromagnetic technology in human's daily life is increasing day by day, and the resulting electromagnetic radiation pollution cannot be ignored, and it has already been included in the ranks of five major pollutions - water pollution, air pollution, solid waste pollution, noise pollution, and electromagnetic radiation pollution. Electromagnetic radiation can induce gene mutations in the human body, leading to the occurrence of various diseases including cancer. In addition, it will seriously affect human's daily communication and some sophisticated electronic systems, which will greatly threaten national information security. Therefore, both military and civilian aspects, electromagnetic radiation pollution must ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G49/00C01G53/00C01B32/168C01B32/158C09K3/00
CPCC01G49/0081C01G53/00C01B32/168C01B32/158C09K3/00C01P2002/72C01P2004/03C01P2006/40C01P2006/42
Inventor 付民陈伟
Owner SHANDONG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com