Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Environment-protecting water-based all-plastic track construction method and environment-protecting water-based all-plastic track

A construction method and an environment-friendly technology, which is applied to the construction method of the environment-friendly water-based all-plastic runway and the field of the environment-friendly water-based all-plastic runway, can solve the problems of soil environment and groundwater pollution, and the adhesive is prone to cracking, etc., so as to achieve firm bonding and good performance. Resilience and impact absorption, the effect of not easy to crack

Active Publication Date: 2020-02-11
苏州大乘环保新材有限公司
View PDF11 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the raw materials in the above-mentioned environmentally friendly adhesives use a large amount of solvents and aromatic diisocyanates. When encountering hot weather or strong ultraviolet radiation, the release of aromatic poisons will be accelerated, and heavy metals such as lead and mercury will remain, which have strong chronic toxicity to the human body. And it will also cause continuous pollution to the soil environment and groundwater; moreover, a large amount of silicon dioxide is added to the above-mentioned adhesive, and as the content of silicon dioxide increases, the adhesive is prone to cracking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-protecting water-based all-plastic track construction method and environment-protecting water-based all-plastic track
  • Environment-protecting water-based all-plastic track construction method and environment-protecting water-based all-plastic track
  • Environment-protecting water-based all-plastic track construction method and environment-protecting water-based all-plastic track

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0064] 1) Preparation of water-based all-plastic runway adhesive Ⅰ:

[0065] Water-based all-plastic runway adhesive I is made by mixing component A and component B at a mass ratio of 100:3.5, wherein component B is 2-methylpentamethylenediamine, and component A is prepared by the following process,

[0066] P1. Add 0.3kg of dispersant BYK-154, 1kg of 2-methyl-2,4-pentanediol, 2kg of isothiazolinone and 0.175kg of silicone defoamer D-10X to 23.5kg of deionized In water, stir at a speed of 500rpm for 10min;

[0067] P2. Continue to add 1 kg of hydroxyethyl cellulose ether, and disperse for 25 minutes at a speed of 300 rpm;

[0068] P3. Continue to add 40kg of acrylic polymer emulsion, 4kg of acrylic functionalized silicone prepolymer Silmer ACRD208 and 1kg of 2-amino-2methyl-1-propanol, and disperse at a speed of 500rpm for 25min; The polymer emulsion is made by mixing epoxy / acrylic hybrid emulsion DOW MAINCOTE AEH-20 and pure acrylic elastic emulsion PRIMAL™ AC-855 at a mass...

Embodiment 1

[0083] An environment-friendly water-based all-plastic runway construction method, with reference to figure 1 , which includes the following steps:

[0084] S1. Mix the water-based all-plastic runway adhesive I and EPDM powder evenly according to the mass ratio of 1:1.2, then scrape the construction base surface, use the special material rake disclosed by CN108166355A and CN207904720U to pull the applied mixture into strips, and maintain it until Dry to form an elastic layer with striped lines, and control the thickness of the elastic layer to 2mm;

[0085] S2. Mix the water-based all-plastic runway adhesive Ⅰ and EPDM powder evenly according to the mass ratio of 1:0.9, then scrape them on the elastic layer, and use the leather rake to make the mixture fill the strip-shaped gaps of the elastic layer, and maintain it until dry to form a leveling Base layer, control leveling base layer thickness to 1mm;

[0086] S3. After mixing the water-based all-plastic runway adhesive Ⅰ an...

Embodiment 2

[0089] An environment-friendly water-based all-plastic runway construction method, based on Example 1, the difference between this example and Example 1 is:

[0090] In step S1, control the thickness of the elastic layer to 1.5mm; in step S2, control the thickness of the leveling base to 1.5mm; in step S3, control the thickness of the leveling layer to 2.0mm; in step S4, epoxy / acrylic hybrid emulsion The mass ratio of DOW MAINCOTE AEH-20, 2-methylpentamethylenediamine and EPDM powder is 100:5:30.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-protecting water-based all-plastic track construction method. According to the technical scheme, the method is characterized by comprising the following steps ofS1, applying water-based all-plastic track adhesive and rubber powder to a construction base surface after uniformly mixing the water-based all-plastic track adhesive and the rubber powder accordingto the mass ratio of 1 to 1.2, and carrying out curing until drying to form an elastic layer; S2, applying the water-based all-plastic track adhesive and the rubber powder to the elastic layer after uniformly mixing the water-based all-plastic track adhesive and the rubber powder according to the mass ratio of 1 to 0.9, and carrying out curing until drying to form a levelling base layer; S3, applying the water-based all-plastic track adhesive and the rubber powder to the levelling base layer after uniformly mixing the water-based all-plastic track adhesive and the rubber powder according to the mass ratio of 1 to 0.8, and carrying out curing until drying to form a levelling surface layer; and S4, spraying water-based acrylic hybrid emulsion, a curing agent and the rubber powder to the levelling surface layer after uniformly mixing the water-based acrylic hybrid emulsion, the curing agent and the rubber powder according to the mass ratio of 100 to (4 - 6) to (25 - 35), and carrying outcuring until drying to form an anti-slip surface layer. According to the environment-protecting water-based all-plastic track construction method, the constructed water-based all-plastic track has theadvantages of being non-toxic, environment-protecting, good in resilience and not prone to crack. The invention further correspondingly discloses an environment-protecting water-based all-plastic track obtained by applying the method.

Description

technical field [0001] The invention relates to the technical field of plastic runway, more specifically, it relates to an environment-friendly water-based all-plastic runway construction method and an environment-friendly water-based all-plastic runway. Background technique [0002] The plastic runway is composed of polyurethane prepolymer, mixed polyether, waste tire rubber, EPDM rubber particles or PU particles, pigments, additives, fillers, etc. The plastic runway has the characteristics of good flatness, high compressive strength, appropriate hardness and elasticity, and stable physical properties. It is conducive to athletes' speed and technical performance, effectively improving sports performance and reducing the rate of falls. It is an internationally recognized outdoor sports venue. Ping material. [0003] But there are many negative reports about plastic track in real life. According to reports, the news that "toxic plastic track" appeared in many schools in a c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E01C13/06E01C11/24C08L23/16C08L33/04C08K13/02C08K3/36C08J9/32C08J9/10
CPCE01C13/06E01C13/065E01C11/24C08J9/103C08J9/32C08J9/0061C08J9/0095C08J2203/22C08J2203/04C08J2333/04C08J2323/16C08J2423/16C08J2433/04
Inventor 卢相志张尊杰单秀军刘洋陈建勇张越
Owner 苏州大乘环保新材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com