Preparation method of 2,2,4-trimethyl-3-hydroxypentanoate, waterborne industrial paint for steel structure and preparation method of waterborne industrial paint

A technology of methyl hydroxyvalerate and hydroxyvaleric acid, which is used in the synthesis and application of organic compounds, can solve the problems of strong taste, low VOC content, and high VOC content of water-based industrial paint for steel structures, and achieve low production costs and simplified production The effect of high process and reaction rate

Active Publication Date: 2020-02-04
RUNTAI CHEM TAIXING CO LTD +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Steel is an important structural material in modern buildings. Many large-scale convention and exhibition centers, stadiums, airport terminals, and TV towers have adopted steel structures as the main structural form. Steel structures are mainly used in the coating design of steel structure buildings. Anticorrosion with water-based industrial paints; however, the coalescents used in the existing water-based industrial paints for steel structures are mainly dodecyl alcohol esters (2,2,4-trimethyl-1,3-pentanediol-monoiso Butyrate) and benzyl alcohol, ethylene glycol butyl ether composition, wherein dodecyl alcohol ester mainly plays a film-forming role, and benzyl alcohol and ethylene glycol butyl ether mainly play the role of helping volatilization, which is mainly due to ten The volatilization rate of dicarbonyl alcohol ester is relatively slow, and benzyl alcohol and butyl glycol ether need to be used to increase the volatilization rate. However, due to the relatively strong smell of benzyl alcohol and butyl glycol ether, the film-forming efficiency is low, which leads to the steel structure Water-based industrial paint has a relatively strong smell and high VOC content. Therefore, it is necessary to develop a film-forming aid with low VOC content, high film-forming efficiency and fast volatilization speed. At the same time, it is necessary to develop a steel film-forming aid containing this film-forming aid Structural water-based industrial paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of 2,2,4-trimethyl-3-hydroxypentanoate, waterborne industrial paint for steel structure and preparation method of waterborne industrial paint
  • Preparation method of 2,2,4-trimethyl-3-hydroxypentanoate, waterborne industrial paint for steel structure and preparation method of waterborne industrial paint
  • Preparation method of 2,2,4-trimethyl-3-hydroxypentanoate, waterborne industrial paint for steel structure and preparation method of waterborne industrial paint

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] A preparation method of 2,2,4-trimethyl-3 hydroxyvaleric acid methyl ester, comprising the following steps:

[0032] 1) Preparation of 2,2,4-trimethyl-3-hydroxypentanoic acid

[0033] Isobutyraldehyde undergoes an aldol condensation reaction under the action of a basic catalyst to generate 2,2,4-trimethyl-3-hydroxypentanal. The reaction formula is as follows:

[0034] 2

[0035] The 2,2,4-trimethyl-3-hydroxypentanal obtained above was mixed with H 2 o 2Oxidation reaction occurs to obtain 2,2,4-trimethyl-3 hydroxypentanoic acid, the reaction formula is as follows:

[0036]

[0037] 2) Preparation of 2,2,4-trimethyl-3-hydroxypentanoic acid methyl ester

[0038] The 2,2,4-trimethyl-3 hydroxyvaleric acid and methanol obtained in step 1) are reacted under the action of a strong acid catalyst to obtain 2,2,4-trimethyl-3 hydroxyvaleric acid methyl ester, and the reaction formula is as follows :

[0039]

[0040] In the step 1), the basic catalyst is NaOH, KOH, Ca...

Embodiment 1

[0048] The preparation method of the 2,2,4-trimethyl-3 hydroxyvaleric acid methyl ester of the present embodiment comprises the following steps:

[0049] 1) Preparation of 2,2,4-trimethyl-3-hydroxypentanoic acid

[0050] With 600g isobutyraldehyde and 45 grams, mass fraction is 40% Ba(OH) 2 Add the solutions into the reaction kettle respectively, stir and raise the temperature to 55°C. After reacting for 7 hours, take samples for gas chromatography test at intervals of 30 minutes. When 2,2,4-trimethyl-3-hydroxypentanal Stop the reaction when the content of isobutyraldehyde no longer increases, then distill off the unreacted isobutyraldehyde at 70°C and -0.1MPa, then wash with water, separate the oil phase product, and obtain 520g of 2,2,4-trimethyl- 3-Hydroxypentanal.

[0051] Add the 2,2,4-trimethyl-3-hydroxyvaleraldehyde obtained above into the reaction kettle, raise the temperature to 80°C, and add hydrogen peroxide dropwise while reacting. 2 o 2 The mass fraction of th...

Embodiment 2

[0057] The preparation method of the 2,2,4-trimethyl-3 hydroxyvaleric acid methyl ester of the present embodiment comprises the following steps:

[0058] 1) Preparation of 2,2,4-trimethyl-3-hydroxypentanoic acid

[0059] Add 700g of isobutyraldehyde and 60g of KOH solution with a mass fraction of 35% into the reaction kettle respectively, stir and raise the temperature to 65°C, after reacting for 2 hours, take samples at 30-minute intervals for gas chromatography test, when two consecutive chromatographic tests Stop the reaction when the content of 2,2,4-trimethyl-3-hydroxypentanal no longer increases, then distill off the unreacted isobutyraldehyde at 65°C and -0.05MPa, then wash with water, and separate the oil phase product, 620g of 2,2,4-trimethyl-3-hydroxypentanal was obtained.

[0060] Add the 2,2,4-trimethyl-3-hydroxyvaleraldehyde obtained above into the reaction kettle, raise the temperature to 50°C, and add hydrogen peroxide dropwise while reacting. 2 o 2 The mass ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
boiling pointaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of organic compound synthesis and application and in particular relates to a preparation method of 2,2,4-trimethyl-3-hydroxypentanoate, a waterborne industrial paint for a steel structure and a preparation method of the waterborne industrial paint. The preparation method of the 2,2,4-trimethyl-3-hydroxypentanoate comprises the following steps: 1) performing a hydroxyaldehyde condensation reaction on iso-butyraldehyde under the action of an alkaline catalyst so as to produce 2,2,4-trimethyl-3-hydroxypentanaldehyde, and performing an oxidation reaction on the obtained 2,2,4-trimethyl-3-hydroxypentanaldehyde with H2O2 so as to obtain 2,2,4-trimethyl-3-hydroxypentanoic acid; and 2) enabling the 2,2,4-trimethyl-3-hydroxypentanoate obtained in the step 1) and methanol to react under the action of a strong acid catalyst, so as to obtain 2,2,4-trimethyl-3-hydroxypentanoate. The preparation method of the 2,2,4-trimethyl-3-hydroxypentanoate, which isprovided by the invention, is single in reaction product, needs no multiple steps of separation and is simple to operate. The invention further provides the waterborne industrial paint with the 2,2,4-trimethyl-3-hydroxypentanoate for the steel structure and the preparation method of the waterborne industrial paint.

Description

technical field [0001] The invention relates to the technical field of synthesis and application of organic compounds, in particular to a method for preparing 2,2,4-trimethyl-3-hydroxypentanoic acid methyl ester, a A water-based industrial paint for steel structures based on methyl ester and a preparation method thereof. Background technique [0002] Steel is an important structural material in modern buildings. Many large-scale convention and exhibition centers, stadiums, airport terminals, and TV towers have adopted steel structures as the main structural form. Steel structures are mainly used in the coating design of steel structure buildings. Anticorrosion with water-based industrial paints; however, the coalescents used in the existing water-based industrial paints for steel structures are mainly dodecyl alcohol esters (2,2,4-trimethyl-1,3-pentanediol-monoiso Butyrate) and benzyl alcohol, ethylene glycol butyl ether composition, wherein dodecyl alcohol ester mainly pla...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07C67/08C07C69/675C09D133/04C09D5/08C09D5/02C09D7/63
CPCC07C67/08C07C51/285C07C45/72C09D133/04C09D5/08C09D5/024C07C69/675C07C59/01C07C47/19C08K13/02C08K5/101
Inventor 卢小松张世元姜明秋王永成张润赟
Owner RUNTAI CHEM TAIXING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com