Method for preparing SiO2-Al2O3 composite aerogel material from fly ash

A technology of composite airgel and fly ash, applied in the field of mesoporous materials, achieves the effect of low cost, short process and short process

Active Publication Date: 2020-01-10
UNIV OF SCI & TECH BEIJING
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, no research has been reported on this

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing SiO2-Al2O3 composite aerogel material from fly ash
  • Method for preparing SiO2-Al2O3 composite aerogel material from fly ash
  • Method for preparing SiO2-Al2O3 composite aerogel material from fly ash

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Example 1 (see the process figure 2 )

[0032] (1) Mix the fly ash and sodium hydroxide (mass ratio 1:0.8) uniformly, place them in a muffle furnace, and calcine at 350°C for 2 hours.

[0033] (2) Grind the alkali fusion mixture obtained in step (1), take 5 g of the alkali fusion mixture, add 30 ml of hydrochloric acid (5 mol / L) and 40 ml of deionized water, and stir until the reaction is complete.

[0034] (3) Filter the mixed solution in step (2) to obtain a solution containing silicon and aluminum.

[0035] (4) Add ammonia water (0.25 mol / L) to the solution obtained in step (3) to control the pH of the solution to be 2.7.

[0036] (5) After aging the gel obtained in step (4) for 1 day, wash it twice with deionized water.

[0037] (6) The gel obtained in step (5) is replaced with absolute ethanol for solvent replacement, and dried in an oven at 45°C for 3 hours and at 75°C for 12 hours.

Embodiment 2

[0038] Example 2 (see the process figure 2 )

[0039] (1) Mix the fly ash and sodium hydroxide (mass ratio 1:1) uniformly, and place them in a muffle furnace at 400°C for 1.5 hours.

[0040] (2) Grind the alkali fusion mixture obtained in step (1), take 6 g of the alkali fusion mixture, add 25 ml of hydrochloric acid (5 mol / L) and 30 ml of deionized water, and stir until the reaction is complete.

[0041] (3) Filter the mixed solution in step (2) to obtain a solution containing silicon and aluminum.

[0042] (4) Add ammonia (0.35 mol / L) to the solution obtained in step (3) to control the pH of the solution to be 2.9.

[0043] (5) After aging the gel obtained in step (4) for 2 days, wash it with deionized water three times.

[0044] (6) The gel obtained in step (5) is replaced with absolute ethanol for solvent replacement, and dried in an oven at 45°C for 3 hours, 65°C for 12 hours, and 75°C for 12 hours.

Embodiment 3

[0045] Example 3 (see the process figure 2 )

[0046] (1) Mix the fly ash and sodium hydroxide (mass ratio 1:1.2) uniformly, and place them in a muffle furnace at 500°C for 1 hour.

[0047] (2) Grind the alkali fusion mixture obtained in step (1), take 4 g of the alkali fusion mixture, add 35 ml of hydrochloric acid (5 mol / L) and 35 ml of deionized water, and stir until the reaction is complete.

[0048] (3) Filter the mixed solution in step (2) to obtain a solution containing silicon and aluminum.

[0049] (4) Add ammonia water (0.5 mol / L) to the solution obtained in step (3) to control the pH of the solution to be 3.1.

[0050] (5) After aging the gel obtained in step (4) for 3 days, wash it with deionized water 4 times.

[0051] (6) The gel obtained in step (5) is replaced with absolute ethanol for solvent replacement, dried in an oven at 45°C for 3 hours, 55°C for 6 hours, 65°C for 12 hours, and 75°C for 12 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing SiO2-Al2O3 composite aerogel from fly ash, and belongs to the field of mesoporous materials. The preparation method comprises the following steps: uniformly mixing fly ash, used as a raw material, with sodium hydroxide, calcining the obtained mixture in a muffle furnace for a certain time to obtain an alkali fusion mixture, mixing and stirring the alkali fusion mixture and a hydrochloric acid solution, and carrying out solid-liquid separation to obtain a liquid phase containing silicon and aluminum; dropwise adding ammonia water into the liquid phase containing silicon and aluminum at normal temperature under a continuous stirring condition to promote a gel reaction of the liquid phase in order to obtain a wet gel; and ageing the wet gel, washing the aged wet gel with deionized water, and carrying out solvent replacement and normal-pressure drying to obtain the SiO2-Al2O3 composite aerogel. The whole technological process has the advantages of realization of high-added-value utilization of solid waste fly ash, low cost, short process, and realization of the whole preparation period of only 3 days; the specific surface area of the synthesized SiO2-Al2O3 composite aerogel is about 900 m <2> / g; and after the composite aerogel is calcined at 900 DEG C for 2 h, the amorphous structure is still maintained, and the good thermal stabilityis achieved.

Description

Technical field [0001] The invention belongs to the field of mesoporous materials, and particularly relates to the synthesis of SiO with fly ash as a raw material 2 -Al 2 O 3 Method of composite aerogel materials. Background technique [0002] Aerogel is a porous solid material formed by a three-dimensional network structure composed of nanoparticles and filled with air. The porosity can reach 80%-99.8%, the typical pore diameter is 1-100nm, and the specific surface area is usually 200-1200m. 2 / g, the range of density is 0.003-0.5g / m 3 ((1) A. Soleimani Dorcheh, M.H. Abbasi, Journal of Materials Processing Tech, 2008, 199(1-3): 10-26.). Due to these characteristics, aerogels have great application potential in heat insulation materials, heat insulation materials, separation materials, and low dielectric constant materials. [0003] With SiO 2 Or Al 2 O 3 Compared with aerogel, Al 2 O 3 -SiO 2 The composite aerogel has better high temperature performance and thermal stability, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B33/158C01F7/06
CPCC01B33/1585C01F7/0693C01P2004/82
Inventor 郭敏申满满张梅
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com