Ramming material for ladle lining and preparation method thereof

A technology for ramming material and molten iron ladle, which is applied in the field of ramming material for lining of molten iron ladle and its preparation, can solve the problems of hidden dangers of personal and equipment safety, serious sticking of molten iron ladle, low safety factor, etc. The effect of sufficient material and enhanced material properties

Active Publication Date: 2020-01-03
鄂尔多斯市瀚博科技有限公司
View PDF12 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The ladle structure used in traditional ferrosilicon production is composed of steel shell and lining refractory material. The lining refractory material is usually built with clay bricks. There are many disadvantages in the process of use: for example, the safety factor is low, and ladle accidents or even leakage may occur from time to time. In the ladle accident, the loss of each leaking ladle is at least 10,000 yuan, which brings great hidden dangers to the safety of people and equipment around the molten iron ladle lifting process. At the same time, the molten iron sticks to the ladle seriously. a great waste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ramming material for ladle lining and preparation method thereof
  • Ramming material for ladle lining and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] The raw material composition in the embodiment of the present invention 1-4 is shown in Table 1;

[0038] The preparation method of ramming material for ladle lining described in the embodiment of the present invention 1-4, the steps are:

[0039] (1) Weigh sodium silicate and aluminum polyphosphate according to weight percentage, add 3 times the weight of water according to the weight ratio of 1:3, and heat to 50°C and stir until sodium silicate and aluminum polyphosphate are completely dissolved. In water, form admixture solution;

[0040] (2) Take clay, graphite, fly ash, silicon carbide powder, and chromium slag powder by weight percentage and carry out pre-mixing first, then add silica, high-alumina bauxite and mix to form a batch material, and in the process of mixing, mist Add the admixture solution;

[0041] (3) Take tap water according to batch: the weight ratio of water is 9:1, add in the batch while stirring, the stirring time is 6 minutes, forms wet base r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a ramming material for a ladle lining and a preparation method thereof. The ramming material comprises the following raw materials: 52 to 57 percent of silica, 20 to 23 percent of high-alumina bauxite, 5 to 10 percent of clay, 5 to 15 percent of graphite, 0.1 to 5 percent of fly ash, 0.2 to 5 percent of silicon carbide power, 0.1 to 3 percent of chromium slag powder, 0.1 to 1 percent of sodium silicate and 0.1 to 1 percent of aluminum polyphosphate. Advantages of the invention are as follow: as that structure strength is high in the use process, it will not cause ladleleakage accidents due to loosening, peeling and other damages in the use process, thus ensuring the safety of people and equipment around the ladle during lifting and transporting, preventing molteniron from sticking to the ladle, preventing wrapping of molten iron in slag, improving the recovery rate of molten iron, and greatly improving the safety and economy.

Description

technical field [0001] The invention belongs to the technical field of ferrosilicon production, and in particular relates to a ramming material for ladle inner lining and a preparation method thereof. Background technique [0002] In the production of ferrosilicon, the ladle containing molten iron is the main equipment. The quality of the ladle, especially the quality of the internal refractory material, directly affects the safety of the ladle during use (especially the occurrence of ladle wear accidents). , the recovery rate of molten iron and the workload of repairing packages. The ladle structure used in traditional ferrosilicon production is composed of steel shell and lining refractory material. The lining refractory material is usually built with clay bricks. There are many disadvantages in the process of use: for example, the safety factor is low, and ladle accidents or even leakage may occur from time to time. In the ladle accident, the loss of each leaking ladle i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/66C04B35/14
CPCC04B35/66C04B35/14C04B35/62204C04B2235/3217C04B2235/349C04B2235/425C04B2235/3826C04B2235/3427C04B2235/447C04B2235/9676C04B2235/9615C04B2235/96
Inventor 李胜春宋永宏刘坤仑牛强邸俊明华永才
Owner 鄂尔多斯市瀚博科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products