A kind of high-temperature high-strength adhesive wear-resistant material and its preparation method

A wear-resistant material, high-strength technology, used in the field of adhesive wear-resistant materials, can solve problems such as failure to take into account, damage and peeling of the adhesive coating, and achieve the effect of avoiding difficult control, reducing area, and excellent wear-resistant performance.

Active Publication Date: 2022-02-01
洛阳耐普特新材料科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The adhesive coating obtained by this invention is temperature-resistant and wear-resistant, but its disadvantages are also obvious. On the one hand, it also considers the particle size of the filler from the perspective of the densest space; on the other hand, it does not consider the adhesive coating. When the temperature shock is severe, its internal structure may undergo destructive changes, causing the adhesive coating to be damaged and peeled off from the inside, thus failing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-temperature high-strength adhesive wear-resistant material and its preparation method
  • A kind of high-temperature high-strength adhesive wear-resistant material and its preparation method
  • A kind of high-temperature high-strength adhesive wear-resistant material and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] A high-temperature high-strength adhesive wear-resistant material, composed of A and B components.

[0051] The composition of A component and the parts by weight of each composition are as follows:

[0052] Mixture of E44 and E51 100 parts

[0053] Nano-SiC, Nano-SiO 2 Fiber Blend 10 parts

[0054] 10 parts dibutyl phthalate

[0055] ZrO 2 Spherical particles 300 parts

[0056] 3 parts graphite powder

[0057] Mixture of tungsten and molybdenum carbide powder 7 parts

[0058] 10 parts of aluminum powder;

[0059] The composition of B component and the parts by weight of each composition are as follows:

[0060] Dicyandiamide 100 parts

[0061] Vapor SiO 2 1 copy

[0062] KH550 5 copies;

[0063] Among them, ZrO 2 The purity of spherical particles is above 95%, and its particle size specifications are composed of: 90 parts by weight of 2.0mm, 120 parts by weight of 1.0mm, and 90 parts by weight of 0.5mm; nano-SiC, nano-SiO 2 The particle size range of the...

Embodiment 2

[0071] A high-temperature high-strength adhesive wear-resistant material, composed of A and B components.

[0072] The composition of A component and the parts by weight of each composition are as follows:

[0073] E51 120 copies

[0074] Nano-ZrO 2 , Nano TiO 2 Fiber Blend 5 parts

[0075] CTBN 30 copies

[0076] al 2 o 3 Spherical particles 200 parts

[0077] 5 parts of graphite powder and talcum powder mixture

[0078] Mixture of titanium and iron carbide powder 5 parts

[0079] 15 parts of aluminum powder;

[0080] The composition of B component and the parts by weight of each composition are as follows:

[0081] 20 parts of 2-ethyl-4 methylimidazole

[0082] Vapor SiO 2 5 copies

[0083] 1 copy of KH560;

[0084] Among them, Al 2 o 3 The purity of the spherical particles is above 95%, and its particle size specifications are composed of: 3.5mm 60 parts by weight, 2.0mm 80 parts by weight, 1.0mm 60 parts by weight; nano ZrO 2 , Nano TiO 2 The particle si...

Embodiment 3

[0092] A high-temperature high-strength adhesive wear-resistant material, composed of A and B components.

[0093] The composition of A component and the parts by weight of each composition are as follows:

[0094] E44 110 copies

[0095] Nano-TiO 2 Fiber 7 servings

[0096] Qishi toughening agent 20 parts

[0097] SiC particles 250 parts

[0098] Quartz powder 4 parts

[0099] Mixture of tungsten and titanium carbide powder 6 parts

[0100] 13 parts of aluminum powder;

[0101] The composition of B component and the parts by weight of each composition are as follows:

[0102] Mixture of dicyandiamide and 2-ethyl-4 methylimidazole 60 parts

[0103] Vapor SiO 2 3 copies

[0104] KH560 3 copies;

[0105] Among them, the particle size specifications of SiC particles are composed of: 60 parts by weight for 5 mesh, 80 parts by weight for 6 mesh, 60 parts by weight for 8 mesh, 37.5 parts by weight for 30 mesh, 12.5 parts by weight for 100 mesh; 2 The particle size range...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
compressive strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature high-strength adhesive wear-resistant material and a preparation method thereof. The high-temperature high-strength adhesive wear-resistant material is composed of A and B components, and A component includes epoxy resin, nano filler fiber, toughening agent, hard filler, self-lubricating filler, metal carbide filler Material, aluminum powder, B component includes curing agent, thixotropic agent, silane coupling agent. The present invention covers the adhesive components of wear-resistant materials by using hard fillers with specific specifications to prevent the adhesive components from being directly eroded and peeled off by the erosion medium, and also adds nano filler fibers to ensure that the adhesive components can be Form a network structure to prevent the adhesive components from being eroded. At the same time, the formula also contains aluminum powder, which prevents static electricity accumulation while being anti-corrosion. The curing agent is dicyandiamide or 2‑ethyl‑4‑methylimidazole The material also has good adhesion and wear resistance at -60°C-250°C.

Description

technical field [0001] The invention belongs to the technical field of adhesive wear-resistant materials, and in particular relates to a high-temperature, high-strength adhesive wear-resistant material and a preparation method thereof. Background technique [0002] With the development of economy and society, people are more and more aware of the importance of reducing the wear of machinery and equipment, and the wear-resistant adhesive coating has been widely used and developed at home and abroad. Wear-resistant adhesive coating refers to a surface that mixes thermosetting polymer adhesive matrix and hard wear-resistant particles (reinforcing phase) according to a certain process and ratio, and coats it on the cleaned workpiece surface to obtain the required wear resistance. technology. This kind of wear-resistant coating has simple coating process, low cost, and small curing shrinkage. It can be used not only for corrosion-resistant and wear-resistant preset coatings on t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L63/00C08K13/04C08K7/10C08K7/18C08K3/08C08K3/14C08K7/08C08G59/40C08G59/50
CPCC08L63/00C08G59/4021C08G59/5073C08K13/04C08K7/08C08K7/18C08K3/14C08K3/08C08K2201/014C08K2201/003C08K2003/0812C08L2201/08C08L2205/025C08K7/10
Inventor 董德新柴秋芳董文琪任江川陈红雨
Owner 洛阳耐普特新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More