Preparation method of self-repairing bionic low-friction hydrogel cartilago articularis on basis of agar

A technology of articular cartilage and hydrogel, applied in tissue regeneration, prosthesis, medical science, etc., can solve the problems of insufficient mechanical properties of hydrogel cartilage, no self-healing ability, etc., achieve good clinical application prospects, low cost, Effect of Low Coefficient of Friction

Inactive Publication Date: 2019-08-27
NANJING UNIV OF SCI & TECH
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problems of insufficient mechanical properties and no self-repair ability of traditional hydrogel cartilage, the present invention provides a preparation method of agar-based self-repair bionic low-friction hydrogel articular cartilage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of self-repairing bionic low-friction hydrogel cartilago articularis on basis of agar

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0021] The preparation method of the self-repairing biomimetic low-friction hydrogel articular cartilage based on agar of the present invention comprises the following steps:

[0022] (1) Agar was added into deionized water, and the temperature of the water bath was 97° C., stirred and dissolved to obtain an aqueous agar solution.

[0023] The specific method is: add 0.3363g agar to 15ml deionized water, and stir for 4 hours at a water bath temperature of 97°C;

[0024] 2) Then configure AAc, AAm, Fe 3+ solution, adding a crosslinking agent and a photoinitiator, adding the mixed solution into the agar solution and stirring evenly.

[0025] The specific method is: add AAc (0.6305g-1.3511g) and AAm (1.8659g-3.9983g) to 5ml of deionized water, so that the ratio of the molar weight of agar to the total molar weight of acrylic acid and acrylamide is 1:35-1 :75, the molar ratio of acrylic acid to acrylamide is 1:3, adding Fe(NO 3 ) 3 9H 2 O (0.0177g-0.0758g), so that the amount...

Embodiment 1

[0032] The solution was prepared in such a ratio that the amount of agar to the sum of the amounts of acrylic acid and acrylamide was 1:35, and the amount of iron ions was 0.5% of the amount of acrylic acid. First prepare a 0.05mol / L agar solution, stir in a water bath at 95°C for 4 hours to dissolve, then prepare AAc, AAm, Fe(NO 3 ) 3 9H 2 O, MBAA (0.0054g), KA (0.0051g) solution, shielded from light and stirred for 0.5 hours, then added it to the agar solution and stirred for 0.5 hours to obtain a uniform solution. The resulting mixed solution was injected into a glass mold, cooled to room temperature, and then irradiated with ultraviolet light for 1.5 hours to obtain agar / PAAc-PAAm-Fe 3+ Double network hydrogel articular cartilage. Compared with pure agar hydrogel 7MPa, the compressive modulus is increased by about 85%, the self-healing performance can be realized, the complete self-healing time is 2 days, and the friction coefficient is 0.09.

Embodiment 2

[0034] The solution was prepared in such a ratio that the amount of agar to the sum of the amounts of acrylic acid and acrylamide was 1:50, and the amount of iron ions was 0.75% of the amount of acrylic acid. First prepare a 0.05mol / L agar solution, stir in a water bath at 95°C for 4 hours to dissolve, then prepare AAc, AAm, Fe(NO 3 ) 3 9H 2 O, MBAA (0.0077g), KA (0.0073g) solution, protected from light and stirred for 0.5 hours, then added it to the agar solution and stirred for 0.5 hours to obtain a uniform solution. The resulting mixed solution was injected into a glass mold, cooled to room temperature, and then irradiated with ultraviolet light for 1.5 hours to obtain agar / PAAc-PAAm-Fe 3+ Double network hydrogel articular cartilage. Compared with pure agar hydrogel, the compressive modulus is increased by about 98%, the self-healing performance can be achieved, the complete self-healing time is 3 days, and the friction coefficient is 0.1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of self-repairing bionic low-friction hydrogel cartilago articularis on the basis of agar. The method includes the steps of adopting agar hydrogel as a physical cross-linking network and polyacrylic acid-polyacrylamide hydrogel as a chemical cross-linking network to form a double-layer network structure, and introducing iron ions to achieve a coordination effect with polyacrylic acid to prepare hydrogel with a porous aqueous structure. Dynamic reversible ionic coordination bonds and hydrogen bonds between the networks are utilized to endow the agar / polyacrylic acid-polyacrylamide-iron ion double network hydrogel with high self-repairing capability and mechanical performance. Compared with pure agar hydrogel, the agar / polyacrylic acid-polyacrylamide-iron ion double network self-repairing hydrogel cartilago articularis has the advantages that the compression modulus is increased by 80-120%, and good self-repairing performance is achieved.

Description

technical field [0001] The invention belongs to the technical field of implant devices, and relates to a method for preparing a self-repairing bionic low-friction hydrogel articular cartilage based on agar. Background technique [0002] Hydrogel is a kind of functional polymer material with a three-dimensional network structure formed by connecting hydrophilic polymer chains by means of chemical cross-linking and physical cross-linking. Show "soft" and "wet" characteristics. Due to the properties of hydrophilicity, biocompatibility, softness and toughness, hydrogels have great application prospects in the field of biological tissue engineering. [0003] Natural articular cartilage is mainly composed of water (accounting for 70-80% by weight) and extracellular matrix. The main component of extracellular matrix is ​​collagen that constitutes the fiber network, which endows articular cartilage with high strength and elasticity. The porous network structure can store synovial ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J3/075C08J3/24C08J3/28C08L33/26C08L5/12C08F220/56C08F220/06C08F222/38C08F2/48A61L27/52A61L27/20A61L27/16
CPCA61L27/16A61L27/20A61L27/52A61L2430/24C08F2/48C08F220/56C08J3/075C08J3/246C08J3/28C08J2333/26C08J2405/12C08L5/12C08L33/26C08F220/06C08F222/385
Inventor 许培刘昀彤熊党生
Owner NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com