A kind of positive electrode material of lithium ion battery and preparation method thereof

A technology for lithium ion batteries and cathode materials, applied in battery electrodes, secondary batteries, circuits, etc., can solve the problems of structural stability of lithium ion diffusion, restricting large-scale commercial applications, poor cycle stability, etc., and achieve excellent cycle. Stability, excellent high rate performance, the effect of improving electronic conductivity

Active Publication Date: 2021-06-04
HENAN INST OF SCI & TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, LiMn 2 o 4 Mn in cathode material 3+ The Jahn-Teller effect, oxygen deficiency and the dissolution of manganese in the electrolyte, for LiMn 2 o 4 The structural stability and Li-ion diffusion have a severe impact, leading to LiMn 2 o 4 Poor cycle stability and low rate of cathode materials in the charge and discharge process restrict the large-scale commercial application of the material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of positive electrode material of lithium ion battery and preparation method thereof
  • A kind of positive electrode material of lithium ion battery and preparation method thereof
  • A kind of positive electrode material of lithium ion battery and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The present invention also provides a preparation method for the above-mentioned lithium-ion battery cathode material, comprising the following steps:

[0035] (1) Mix Li source, Mn source and dopant according to stoichiometric ratio to obtain mixed slurry; said dopant includes Mg source, Zn source, Cu source, Ni source, Co source, Cr source, Al source , Ga source, In source, Tl source, Ti source, Si source or Zr source;

[0036] The mixed slurry is sequentially dried, pre-calcined and final-calcined to obtain doped modified lithium manganate;

[0037] (2) refine the doped modified lithium manganate obtained in the step (1), to obtain nanoscale doped modified lithium manganate;

[0038] (3) Granulating after mixing the nano-scale doped modified lithium manganese oxide and carbon nanotubes obtained in the step (2), obtaining a micron-scale spherical core based on carbon nanotube three-dimensional contact consolidation;

[0039] (4) Dispersing the conducting polymer mon...

Embodiment 1

[0054] Embodiment 1 prepares the flow chart of lithium-ion battery cathode material as figure 1 shown, according to figure 1 The method shown prepares the positive electrode material of lithium ion battery.

[0055] Aluminum nitrate, electrolytic manganese dioxide and lithium carbonate were mixed according to the molar ratio of Li, Mn and Al of 1.05:1.95:0.05, and wet ball milled for 3 hours under the action of anhydrous ethanol grinding aid. After ball milling, the obtained mixed slurry was transferred to an evaporating dish for drying. Finally, grind the dried mixture evenly and place it in a muffle furnace for pre-calcination at 450°C for 4h, then grind it again and place it in a muffle furnace for final firing at 800°C for 12h to obtain LiMn 1.95 al 0.05 o 4 .

[0056] LiMn prepared by ball milling 1.95 al 0.05 o 4 Grinding into nano-sized particles, the dispersant is absolute ethanol, the rotating speed is 300r / min, and the time is 10h. Then 10 g of the obtained ...

Embodiment 2

[0061] Mix magnesium nitrate, trimanganese tetraoxide and lithium hydroxide according to the molar ratio of Li, Mn and Mg of 1.05:1.95:0.05, and wet ball mill for 3 hours under the action of absolute ethanol grinding aid. After ball milling, the obtained mixed slurry was transferred to an evaporating dish for drying. Finally, the dried mixture was ground evenly and placed in a muffle furnace for pre-calcination at 400°C for 6 hours, and then ground again and placed in a muffle furnace for final firing at 780°C for 15 hours to obtain LiMn 1.95 Mg 0.05 o 4 .

[0062] LiMn prepared by ball milling 1.95 Mg 0.05 o 4 Grinding into nano-sized particles, the dispersant is absolute ethanol, the rotating speed is 300r / min, and the time is 10h. Then 12 g of the obtained nanoparticles and 1 g of MWCNT were mixed, 15 mL of deionized water was added, and the resulting solution was spray-dried at 180 ° C to obtain the core LiMn 1.95 Mg 0.05 o 4 @MWCNT, and dried at 150°C.

[0063] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
retention rateaaaaaaaaaa
Login to View More

Abstract

The invention provides a lithium ion battery cathode material and a preparation method thereof, which belong to the field of cathode materials. The anode material of the lithium ion battery provided by the present invention has a core-shell structure, which is composed of a core and a coating layer; the core includes doped modified lithium manganate and carbon nanotubes, and the carbon nanotubes are three-dimensionally connected and consolidated with The hetero-modified lithium manganese oxide forms a micron-scale spherical material; the cladding layer includes a dual-phase flexible polymer. The positive electrode material of lithium ion battery provided by the present invention has excellent cycle stability and large rate performance, and after 200 cycles, the capacity retention rate can be as high as 98.9%; and the positive electrode material of lithium ion battery provided by the present invention still has a large When the charge rate is increased from 0.5C to 30C, the first discharge specific capacity retention rate is 84.5%.

Description

technical field [0001] The invention relates to the field of positive electrode materials, in particular to a lithium ion battery positive electrode material and a preparation method thereof. Background technique [0002] spinel LiMn 2 o 4 As a cathode material for lithium-ion batteries, it has the advantages of high voltage platform, good thermal stability, rich manganese resources, mature preparation technology, low production cost, good safety performance, and no pollution to the environment. Compared with lithium iron phosphate and ternary materials, the overall cost performance of this material is relatively high, and it has an outstanding cost advantage. [0003] However, LiMn 2 o 4 Mn in cathode material 3+ The Jahn-Teller effect, oxygen deficiency and the dissolution of manganese in the electrolyte, for LiMn 2 o 4 The structural stability and lithium ion diffusion have a severe impact, leading to LiMn 2 o 4 Cathode materials have problems such as poor cycle ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/505H01M4/525H01M4/485H01M4/62H01M10/0525
CPCH01M4/362H01M4/366H01M4/485H01M4/505H01M4/525H01M4/62H01M4/624H01M4/625H01M4/628H01M10/0525Y02E60/10
Inventor 赵红远高欣扬苏建修李勇峰赵二庆张明明张亚奇吴婷婷冯宜鹏王占奎
Owner HENAN INST OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com