Container corner fitting and heat treatment process thereof

A technology for containers and corner fittings, which is applied in heat treatment furnaces, heat treatment equipment, metal material coating processes, etc., can solve problems such as insufficient strength and low-temperature toughness, and achieve the effects of ensuring production costs, ensuring steel properties, and improving low-temperature toughness

Active Publication Date: 2019-07-26
MAANSHAN SHENGLEI WEAR RESISTANT ALLOY MFG
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problem of insufficient strength and low-temperature toughness of container corner fittings in the prior art, the present invention provides a container corner fitting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Container corner fitting and heat treatment process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A container corner fitting in this embodiment, the alloy composition of the container corner fitting is composed of the following elements in terms of mass percentage: 0.09-0.15% C, 0.95-1.40% Mn, 0.27-0.36% Si, 0.19-0.26% Ni , 0.15-0.22% Cr, 0.007-0.015% Al, up to 0.03% P, up to 0.03% S, up to 0.08% Mo, up to 0.17% Cu, up to 0.01% V, and the balance is Fe and unavoidable impurities. Specifically, in this embodiment, it consists of the following element contents: 0.09% C, 0.95% Mn, 0.27% Si, 0.19% Ni, 0.15% Cr, 0.007% Al, 0.01% P, 0.01% S, 0.04% Mo, 0.10% Cu, 0.01% V, the balance being Fe and unavoidable impurities, wherein Ni / Cr=1.27, Mn / Si=3.5, a container corner fitting of this embodiment is treated by the following heat treatment process:

[0047] 1. Carburizing, put the corner fittings of the container into a high-temperature furnace tank at 920°C, add dilute gas methanol and enriched gas ethyl acetate dropwise into the high-temperature furnace tank, and continue c...

Embodiment 2

[0052] A container corner fitting in this embodiment, the alloy composition of the container corner fitting is composed of the following elements in terms of mass percentage: 0.09-0.15% C, 0.95-1.40% Mn, 0.27-0.36% Si, 0.19-0.26% Ni , 0.15-0.22% Cr, 0.007-0.015% Al, up to 0.03% P, up to 0.03% S, up to 0.08% Mo, up to 0.17% Cu, up to 0.01% V, and the balance is Fe and unavoidable impurities. Specifically, in this embodiment, it consists of the following element contents: 0.15% C, 1.40% Mn, 0.36% Si, 0.26% Ni, 0.22% Cr, 0.015% Al, 0.03% P, 0.03% S, 0.08% Mo, 0.17% Cu, 0.01% V, the balance is Fe and unavoidable impurities, wherein Ni / Cr=1.18, Mn / Si=3.9, a container corner fitting of this embodiment is treated by the following heat treatment process:

[0053] 1. Carburizing, put the corner fittings of the container into a high-temperature furnace tank at 940°C, add dilute gas methanol and enriched gas ethyl acetate dropwise into the high-temperature furnace tank, and continue carb...

Embodiment 3

[0058] A container corner fitting according to this embodiment, the alloy composition constituting the container corner fitting is composed of the following elements in terms of mass percentage: 0.09-0.15% C, 0.96-1.37% Mn, 0.32-0.36% Si, 0.19-0.26% Ni , 0.18-0.21% Cr, 0.007-0.015% Al, up to 0.015% P, up to 0.015% S, up to 0.08% Mo, up to 0.17% Cu, up to 0.01% V, and the balance is Fe and unavoidable impurities. Specifically, in this embodiment, it consists of the following element contents: 0.09% C, 0.96% Mn, 0.32% Si, 0.19% Ni, 0.18% Cr, 0.007% Al, 0.01% P, 0.01% S, 0.04% Mo, 0.10% Cu, 0.01% V, the balance being Fe and unavoidable impurities, wherein Ni / Cr=1.06, Mn / Si=3.0, a container corner fitting of this embodiment is treated by the following heat treatment process:

[0059] 1. Carburizing, put the corner fittings of the container into a high-temperature furnace tank at 920°C, add dilute gas methanol and enriched gas ethyl acetate dropwise into the high-temperature furnac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Low temperature impact energyaaaaaaaaaa
Login to View More

Abstract

The invention discloses a container corner fitting, and belongs to the field of container materials. The alloy compositions of the container corner fitting are composed of the following elements, by the mass percent, of 0.09-0.15% of C, 0.95-1.40% of Mn, 0.27-0.36% of Si, 0.19-0.26% of Ni, 0.15-0.22% of Cr, 0.0007-0.015% of Al, being no more than 0.03.% of P, being no more than 0.03% of S, being no more than 0.08% of Mo, being no more than 0.17% of Cu, being no more than 0.01% of V, and the balance Fe and inevitable impurities, wherein Ni / Cr=1.00-1.25, Mn / Si=3.0-3.8, and Ni + Cr + Mo +Cu is equal to or less than 0.72% by the mass percent. The alloy compositions of the container corner fitting are improved, on the premise of guaranteeing the production cost, the strength of the corner fitting is improved, the toughness is greatly improved at the low temperature, and the corner fitting also has good welding performance.

Description

technical field [0001] The invention relates to the field of container materials, in particular to a container corner fitting and a heat treatment process thereof. Background technique [0002] Corner fittings are important parts of the container, and play a key role in the lifting, handling, fixing, stacking and bolting of the container. Most of the force on the box is almost transmitted by the corner fittings. At the same time, As the outermost edge of the box body, the corner fittings also play a role in protecting the container body. [0003] At present, with the development of the transportation industry, the volume of import and export trade has increased sharply. When container transportation is carried out in some high-latitude areas, due to the low temperature, the toughness of the steel made of corner fittings is greatly reduced at low temperatures, and brittleness is very easy to occur. Therefore, the steel of the corner fittings needs to be able to withstand low...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/04C22C38/02C22C38/06C22C38/44C22C38/42C22C38/46C22C38/40C23C8/22C23C8/80C21D1/18C21D9/00B65D90/00
CPCB65D90/00C21D1/18C21D9/0068C22C38/02C22C38/04C22C38/06C22C38/40C22C38/42C22C38/44C22C38/46C23C8/22C23C8/80
Inventor 杨明
Owner MAANSHAN SHENGLEI WEAR RESISTANT ALLOY MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com