Preparation method for macromolecular plastic hollow plate

A polymer and plastic technology, applied in the field of polymer plastic hollow board preparation, can solve the problems of easy damage, endangering human health, uneven quality of plastic middle board, etc., to achieve simple use, rich colors and renewable resources. Effect

Inactive Publication Date: 2019-07-23
佛山市仁享精密五金塑料制品有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the composition and raw materials of the existing plastic panels are uneven, resulting in uneven quality of the plastic panels, making some plastic panels easily damaged during use, and some plastic panels may also endanger the health of the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A polymer plastic hollow board, comprising the following raw materials in parts by weight: 30-40 parts of mixed resin, 20-40 parts of polyethylene, 3-5 parts of leveling agent, 5-7 parts of polyethylene low molecular wax dispersant, powder 3-5 parts of solid coloring agent, 35-40 parts of ethanol solvent, 10-20 parts of organic pigment, 16-18 parts of color control agent, 30-50 parts of modified nano activated carbon, 12-15 parts of isooctyl ester, reactive diluent 20-50 parts, 10-15 parts of polyetheramine, 10-15 parts of toughening agent, 10-15 parts of curing agent.

[0020] A method for preparing a polymer plastic hollow plate, comprising the following steps:

[0021] S1. Grinding and mixing: Invert the equal amount of mixed resin, polyethylene and modified nano-activated carbon into a pulverizer for pulverization to form a mixed powder;

[0022] S2. Add auxiliary agent: Pour the mixed powder formed by S1 into a high-temperature melting furnace for high-temperature...

Embodiment 2

[0027] A polymer plastic hollow board material, comprising the following raw materials in parts by weight: 30 parts of mixed resin, 20 parts of polyethylene, 3 parts of leveling agent, 5 parts of polyethylene low molecular wax dispersant, 3 parts of powdery colorant, ethanol 35 parts of solvent, 10 parts of organic pigment, 16 parts of color control agent, 30 parts of modified nano-activated carbon, 12 parts of isooctyl ester, 20 parts of reactive diluent, 10 parts of polyetheramine, 10 parts of toughening agent, 10 parts of curing agent .

[0028] The preparation method is consistent with Example 1.

Embodiment 3

[0030] A polymer plastic hollow board material, comprising the following raw materials in parts by weight: 35 parts of mixed resin, 30 parts of polyethylene, 4 parts of leveling agent, 6 parts of polyethylene low molecular wax dispersant, 6 parts of powdery colorant, ethanol 37 parts of solvent, 15 parts of organic pigment, 17 parts of color control agent, 40 parts of modified nano-activated carbon, 14 parts of isooctyl ester, 35 parts of reactive diluent, 13 parts of polyetheramine, 13 parts of toughening agent, and 13 parts of curing agent .

[0031] The preparation method is consistent with Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a macromolecular plastic hollow plate which comprises the following raw materials in parts by weight: mixed resin, polyethylene, flatting agent, polyethylene low-molecular waxdispersing agent, powdered colorant, ethyl alcohol solvent, organic pigment, color control agent, modified nanometer activated carbon, diisooctyl, reactive diluent, polyether amine, flexibilizer and curing agent. A preparation method for the macromolecular plastic hollow plate comprises the following steps: S1) smashing and mixing the raw materials; S2) adding additives; S3) pre-plasticizing; S4)setting under the conditions of pressurizing and cooling; S5) molding the product. The produced macromolecular plastic hollow plate is a green environment-friendly product, is non-toxic, non-pollution, waterproof, shake-proof, anti-aging, anti-corrosion and rich in color, is pollution-free to environment, is simple in use, is recyclable, and is reasonably utilized so as to realize renewable resources.

Description

technical field [0001] The invention relates to the field of plate materials, in particular to a method for preparing a polymer plastic hollow plate. Background technique [0002] Plastic middle board is also called hollow partition board, wanton board, double wall board, corrugated board, and is made of plastic material. Compared with cardboard structure products, hollow board has the advantages of moisture resistance, corrosion resistance and lighter weight instead of cardboard. Compared with injection molding products, hollow panels have the advantages of shock resistance, flexible structure design, and no need to open injection molds. However, the composition and raw materials of the existing plastic panels are uneven, resulting in uneven quality of the plastic panels, making some plastic panels easily damaged during use, and some plastic panels may also endanger human health. . [0003] Therefore, developing a kind of graphene macromolecule masterbatch composite mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L33/00C08L23/06C08L71/00C08K9/00C08K7/24C08K5/10
CPCC08L23/06C08L33/00C08L2201/08C08L2205/025C08L2205/035C08L71/00C08K9/00C08K7/24C08K5/10
Inventor 唐爱华
Owner 佛山市仁享精密五金塑料制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com