Production method for improving yield-strength ratio and stretch-flange-formability of cold-rolled DP980 steel

A production method and yield-strength ratio technology are applied in the production field of improving the yield-strength ratio and hole-enlarging performance of cold-rolled DP980 steel, and can solve the problems of inability to satisfy hole-enlarging, flanging, cracking, etc.

Inactive Publication Date: 2019-07-12
SD STEEL RIZHAO CO LTD
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to produce high yield ratio and hole expansion rate by regulating the key process parameters of each process section on the basis of the chemical composition design of the existing 980MPa grade cold-rolled DP steel, and at the same time have good drawing Featured cold-rolled DP980 steel to solve the problem that the traditional low-yield-ratio cold-rolled DP980 steel cannot meet the requirements of hole expansion and flanging during the cold forming process, which inevitably leads to defects such as cracking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method for improving yield-strength ratio and stretch-flange-formability of cold-rolled DP980 steel
  • Production method for improving yield-strength ratio and stretch-flange-formability of cold-rolled DP980 steel
  • Production method for improving yield-strength ratio and stretch-flange-formability of cold-rolled DP980 steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～3

[0019] Embodiments 1-3: A production method for improving the yield ratio and hole expansion performance of cold-rolled DP980 steel according to the present invention is as follows.

[0020] The chemical composition of steel slabs in Examples 1-3 of the present invention includes C: 0.080-0.130%, Si: 0.28-0.50%, Mn: 2.00-2.50%, Alt: 0.040-0.070%, Cr: 0.40-0.70% by weight percentage , Mo: 0.20~0.30%, Nb: 0.020~0.050%, and limit N≤0.005%, P≤0.008%, S≤0.005%, O≤0.003%, and the balance is Fe and other unavoidable impurities. The chemical composition of the tapping molten steel of the billet in specific embodiments 1-3 is shown in Table 1, and the thickness of the billet is 230mm.

[0021] The actual smelting composition (mass percentage, %) of the embodiment of table 1

[0022]

[0023] In Examples 1 to 3 of the present invention, the thickness of the hot-rolled base material is 2.00mm

[0024] The technical proc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method for improving the yield-strength ratio and stretch-flange-formability of cold-rolled DP980 steel. On the basis of the chemical composition design of existing cold-rolled DP980 steel, through control over the process parameters of a slab heating procedure, a hot rolling procedure and a cooling and coiling procedure, hot-rolled initial structures comprisepearlite, medium temperature bainite mixed structures and equiaxial ferrite structures, wherein all the grain sizes are no more than 5.0 [mu]m, and the average grain size is no more than 3.2 [mu]m. The volume fraction of martensite in the microstructure of the cold-rolled DP980 steel prepared with the production method provided by the invention is larger than 30.0%, and the yield-strength ratio islarger than 0.70; the hole expanding rate is no less than 55%, and meanwhile the elongation reaches 12.9% and above; and the production method is especially applicable for automobile structural members and stiffeners with the requirements for 980 MPa high tensile strength and excellent drawing characteristic as well as reaming and flanging requirements.

Description

technical field [0001] The invention belongs to the technical field of cold-rolled high-strength steel for automobiles, and in particular relates to a production method for improving the yield ratio and hole-expanding performance of cold-rolled DP980 steel. Background technique [0002] In recent years, the rapid development of the automobile industry has strongly promoted the medium-to-high speed development of my country's national economy, but the resulting high energy consumption and high emissions are seriously polluting the environment and having many negative impacts on people's daily life. It can be seen that in order to realize the sustainable development of the automobile industry, the problems of energy saving, emission reduction and low-carbon environmental protection must be solved. This is also the primary problem that the automobile industry of various countries must solve. The new demand for integration, comfort and energy saving requires not only to achieve ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/38C22C38/06C22C38/22C22C38/26C21D8/02
CPCC21D8/0226C21D8/0236C21D8/0247C22C38/02C22C38/06C22C38/22C22C38/26C22C38/38
Inventor 侯晓英李洪翠胡华东金光宇康华伟郝亮亢业峰张磊梁亚王乐
Owner SD STEEL RIZHAO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More