Phosphatized cold-rolled strip steel and manufacturing method thereof

A technology for cold-rolled strip steel and a manufacturing method, which is applied to manufacturing tools, furnaces, heat treatment equipment, etc., can solve the problem of affecting the quality of the upper film and the service life of the phosphating agent, affecting the adhesion and corrosion resistance of the paint film, and phosphating treatment. Problems such as complex process flow, to achieve the effect of improving phosphating effect and efficiency, improving formation speed and uniform density, and ensuring cleanliness

Active Publication Date: 2019-06-28
INST OF RES OF IRON & STEEL JIANGSU PROVINCE +2
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are two main problems. First, after the workpiece is processed and formed, due to the limitation of its geometric size and shape, there will inevitably be dead corners such as grooves that are not easy to clean, which will affect the effect of degreasing and washing, and will hinder The formation of phosphating film, and even after the film is applied, it will affect the adhesion and corrosion resistance of the subsequent paint film. At the same time, it is easy to cause cross grooves between the degreasing tank and the phosphating tank, affecting the quality of the film and the use of phosphating agent Second, phosphating treatment involves the discharge of carcinogenic pollutants such as phosphating wastewater and waste residue. Improper treatment will cause serious environmental pollution. In addition, the phosphating process is complicated and energy-consuming, which brings many problems to customers. stress and inconvenience

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phosphatized cold-rolled strip steel and manufacturing method thereof
  • Phosphatized cold-rolled strip steel and manufacturing method thereof
  • Phosphatized cold-rolled strip steel and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The chemical composition of steel for oil barrels is: C 0.030%, Mn 0.40%, Si 0.01%, Al 0.05%, P 0.018%, S 0.0035%, and the balance is Fe and impurity elements.

[0037] The strip steel whose chemical composition meets the above requirements is subjected to conventional treatments such as decoiling, welding, degreasing cleaning, annealing, leveling and tension leveling on the continuous annealing line. was 1.4%. After the treatment, enter the phosphating treatment area, first enter the phosphating section for phosphating treatment, the phosphating section adopts a spray process, the pH value of the phosphating solution is 2.2, the phosphating time is 41s, and the temperature of the phosphating solution is 42°C. The phosphating solution is composed of the following components: zinc dihydrogen phosphate 80g / L, zinc nitrate 69g / L, phosphoric acid 15g / L, sodium chlorate 1.9g / L, tartaric acid 5.8g / L, sodium fluoride 1.5g / L, sulfuric acid Hydroxylamine 2.2g / L, phytic acid 1.7...

Embodiment 2

[0041] The chemical composition of steel for oil barrels is: C 0.040%, Mn 0.20%, Si 0.018%, Al 0.027%, P 0.005%, S 0.011%, and the balance is Fe and impurity elements.

[0042]The strip steel whose chemical composition meets the above requirements is subjected to conventional treatments such as decoiling, welding, degreasing cleaning, annealing, leveling and tension leveling on the continuous annealing line. was 1.1%. After the treatment, enter the phosphating treatment area, first enter the phosphating section for phosphating treatment, the phosphating section adopts a spray process, the pH value of the phosphating solution is 2.8, the phosphating time is 49s, and the temperature of the phosphating solution is 45°C. The phosphating solution is composed of the following components: zinc dihydrogen phosphate 65g / L, zinc nitrate 78g / L, phosphoric acid 11g / L, sodium chlorate 1.3g / L, tartaric acid 6.8g / L, sodium fluoride 1.9g / L, sulfuric acid Hydroxylamine 1.1g / L, phytic acid 1.2...

Embodiment 3

[0046] The chemical composition of steel for oil barrels is: C 0.035%, Mn 0.30%, Si 0.04%, Al 0.01%, P 0.012%, S 0.0047%, and the balance is Fe and impurity elements.

[0047] The steel strip whose chemical composition meets the above requirements is subjected to conventional treatments such as uncoiling, welding, degreasing cleaning, annealing, leveling and tension leveling on the continuous annealing line. was 1.2%. After the treatment, enter the phosphating treatment area, first enter the phosphating section for phosphating treatment, the phosphating section adopts a spraying process, the pH value of the phosphating solution is 2.5, the phosphating time is 49s, and the temperature of the phosphating solution is 48°C. The phosphating solution is composed of the following components: zinc dihydrogen phosphate 97g / L, zinc nitrate 52g / L, phosphoric acid 18g / L, sodium chlorate 3.0g / L, tartaric acid 5.4g / L, sodium fluoride 1.2g / L, sulfuric acid Hydroxylamine 1.7g / L, phytic acid ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a phosphatized cold-rolled strip steel and a manufacturing method thereof. The phosphatized cold-rolled strip steel is composed of, by mass: 0.01-0.10% of C, 0.1-0.6% of Mn, less than or equal to 0.10% of Si, less than or equal to 0.10% of Al, less than or equal to 0.02% of P, less than or equal to 0.015% of S, and the balance Fe and impurity elements. Phosphating treatmentequipment is additionally arranged between a leveling straightening machine and an oiling machine of a continuous annealing unit; the phosphating treatment equipment consists of a phosphating section,a rinsing section and a drying box; after the strip steel is uncoiled, the strip steel enters a phosphating treatment area after being subjected to conventional treatment such as welding, cleaning, annealing, flattening and tension straightening; and the strip steel after the phosphating treatment is directly coiled into a coil without oiling. According to production of the cold-rolled phosphatized coil, the production process of the client side is simplified, the efficiency is improved, the phosphating quality is improved, and the problem that the phosphating effect is influenced due to unthorough degreasing and cleaning of the client terminal is solved.

Description

technical field [0001] The invention belongs to the technical field of iron and steel production, in particular to a phosphating cold-rolled steel strip and a manufacturing method. Background technique [0002] Cold-rolled strip steel has the advantages of good surface finish, good flatness, high dimensional accuracy, and good mechanical properties. It can be used to make oil barrels and containers, and can also be used to manufacture building panels, office supply cabinets, and electronic machinery. However, after processing and forming and before coating, the cold-rolled strip steel needs to be phosphating. Surface phosphating treatment is an extremely important process in the manufacturing process of steel drums, such as steel coil uncoiling and blanking, stamping and forming of drum bottom cover, welding and forming assembly of drum body, surface phosphating, internal and external coating, etc. Phosphating is the process in which metal reacts with dilute phosphoric acid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C23C22/36C23C22/76C21D1/26C21D6/00C21D9/56
Inventor 李慧岳重祥朱阳林李化龙
Owner INST OF RES OF IRON & STEEL JIANGSU PROVINCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com