Preparation method of high-density anisotropic conductive metalized wood

A high-density, metallized technology, applied in wood treatment, impregnated wood, wood impregnation, etc., can solve the problems of high risk, inconvenient operation, and difficulty in ensuring uniform penetration, so as to improve the permeability and save the penetration process , the effect of maintaining structure and strength

Active Publication Date: 2019-06-14
UNIV OF SCI & TECH BEIJING
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The high-pressure impregnation operation is inconvenient and dangerous, and the permeability of the molten metal in the fiber structure is affected by temperature, pressure, and channel structure characteristics, and the uniformity of penetration is difficult to guarantee

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-density anisotropic conductive metalized wood
  • Preparation method of high-density anisotropic conductive metalized wood
  • Preparation method of high-density anisotropic conductive metalized wood

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] As shown in Figures 1 to 3, what the present embodiment prepared was basswood-tin-bismuth alloyed wood, and the preparation steps were as follows:

[0043] Step (1): The wood and metal used are basswood and tin-bismuth alloy with a melting point of 138° C. respectively. Cut basswood into a size of 35mm*35mm*5mm, put it in a beaker, add 40mL of dilute ammonia water with a mass fraction of 5%, cover the mouth of the beaker with plastic film to prevent volatilization, heat it to 80°C for five hours, and wash off the wood Lignin in the fiber structure. Take out the pretreated wood, put it into the oven, and press it on the upper surface of the wood with a flat steel block to prevent the wood from deforming during drying, then adjust the temperature of the oven to 100°C, bake for 2 hours, and take out the dried wood for use.

[0044] Step (2): Put the tin-bismuth alloy (tin 42%, bismuth 58%) in the beaker, adjust the temperature of the oven to 180° C., and wait for the meta...

Embodiment 2

[0051] What this embodiment needs to prepare is pine-tin-bismuth alloyed wood, and the preparation method adopted is basically the same as that of Example 1, except that:

[0052] The pine wood that adopts and the alloy that melting point is 180 ℃ of tin 62% bismuth 38% are raw materials. The melting point of the metal becomes higher, and the temperature of the vacuum oven needs to be kept at 220°C. In order to make the tin-bismuth alloy have better fluidity, the holding time needs to be increased to 1 hour. The obtained pine-tin-bismuth alloy metallized wood is shown in Figure 3.

[0053] The change in density is obtained as follows:

[0054] Timber specification 35mm*35mm*5mm, melting point: 180°C

[0055]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of preparation of composite performance materials, and provides a preparation method of high-density anisotropic conductive metalized wood, which comprises the following steps: pretreating a wood fiber structure; carrying out vacuum infiltration on metal liquid in a wood fiber channel; and carrying out surface treatment on the metalized wood. In the pretreatmentstep, lignin in a log fiber structure is washed away without destroying the fiber structure by adopting a mixed solvent of dilute ammonia water and an alkali metal halide aqueous solution, a good fiber channel is provided for permeation of molten metal, and meanwhile, nano halide molten salt particles precipitated from the wood fiber structure can achieve a flame retardant effect at a high temperature; the permeated metal is an alloy material, the metal is melt into a liquid state in a constant-temperature vacuum oven, then wood to be permeated is soaked into the molten metal, and permeation is carried out under a vacuum condition; and after the permeation is completed, the surface of the metalized wood finishing the permeation is polished through mechanical polishing equipment, and thus the large-density anisotropic metalized wood with a uniform surface and a good state is obtained.

Description

technical field [0001] The invention mainly belongs to the field of preparation of composite performance materials, and in particular relates to a preparation method of large-density anisotropic conductive metallized wood. Background technique [0002] Wood is widely used in daily life. It is easy to process, has good heat insulation and sound insulation properties, but its defects such as large variability in properties, poor dimensional stability, perishability, and flammability limit the use of wood. After the wood is metallized, the wood has both the characteristics of wood and metal, the density and strength are improved, and the respective advantages of wood and metal are combined. Wood metallization is to fill low-melting point metals into the capillary channels of wood or plate them on the surface of wood. The former increases the density of wood more, and improves the performance of wood more; the surface coating of the latter does not significantly increase the de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/02B27K3/08B27K3/32B27K5/00
Inventor 王敏李岚昕包燕平陈亚楠
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com