Fireproof organic negative ion coating and preparation method thereof

A technology of negative ion coatings and negative ion particles, applied in the direction of fireproof coatings, coatings, etc., can solve the problems of flammability, safety hazards, and low cost performance, and achieve the effects of avoiding poisonous, harmful and easy, preventing agglomeration, and reducing overall costs

Active Publication Date: 2019-06-07
杭州琻泰环境科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] For above-mentioned prior art, the object of the present invention is to provide a kind of fire-proof type organic anion paint and preparation method thereof, to solve the problem that existing organic paint is not only easy to volatilize poisonous and harmful substances, bring influence to human health, and it is flammable in use , causing certain safety hazards, and some fire-resistant inorganic water-based coatings are often not cost-effective, and it is difficult to be widely promoted and used.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fireproof organic negative ion coating and preparation method thereof
  • Fireproof organic negative ion coating and preparation method thereof
  • Fireproof organic negative ion coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0040] The invention provides a kind of preparation method of fireproof type organic anion coating, wherein, comprise the following steps:

[0041] 1) Preparation of negative ion particles:

[0042] A, under the condition of magnetic stirring, tourmaline powder is mixed with water to make tourmaline suspension;

[0043] B, adding rare earth salts to the tourmaline suspension prepared above and mixing to obtain a mixed solution;

[0044] C. After adding a precipitating agent to the above mixed solution for precipitation, take the precipitate and dry it to obtain negative ion particles;

[0045] 2) Preparation of fireproof particles:

[0046] D, graphite is placed in the mixed solution of hydrogen peroxide and nitric acid and stirred and mixed to obtain oxidized graphite;

[0047] E. Mix the oxidized graphite with water, then add glacial acetic acid dropwise therein and stir to prepare fireproof particles;

[0048] 3) Preparation of fireproof organic anion coating:

[0049]...

Embodiment 1

[0067] 1) Preparation of negative ion particles:

[0068] A, under the condition of magnetic stirring, tourmaline powder is mixed with water to make tourmaline suspension;

[0069] B. Add 0.005mol cerium nitrate to the 10mL tourmaline suspension prepared above (the content of tourmaline powder is 20% by weight) and magnetically stir and mix for 1h to prepare a mixed solution;

[0070] C. After adding ammoniacal liquor with a concentration of 25% to the above mixed solution at a rate of 80 drops / min for precipitation, take the precipitate and rinse it with clear water several times, then dry it at 100°C to obtain negative ion particles;

[0071] 2) Preparation of fireproof particles:

[0072] D, in ice-water bath condition, 10g graphite is placed in the mixed solution of 1mL hydrogen peroxide and 20mL fuming nitric acid and stirs and mixes, then adopt concentration to be the aqueous solution washing of 35% nitric acid, make the graphite after oxidation;

[0073] E. Mix 5g of ...

Embodiment 2

[0078] 1) Preparation of negative ion particles:

[0079] A, under the condition of magnetic stirring, tourmaline powder is mixed with water to make tourmaline suspension;

[0080] B. Add 0.015mol cerium nitrate to the 10mL tourmaline suspension prepared above (the content of tourmaline powder is 30% by weight) and magnetically stir and mix for 3h to obtain a mixed solution;

[0081] C. After adding ammoniacal liquor with a concentration of 25% to the above-mentioned mixed solution at a rate of 120 drops / min for precipitation, take the precipitate and rinse it with clear water several times, then dry it at 130° C. to obtain negative ion particles;

[0082] 2) Preparation of fireproof particles:

[0083] D, in ice-water bath condition, 10g graphite is placed in the mixed solution of 5mL hydrogen peroxide and 30mL fuming nitric acid and stirs and mixes, then adopt concentration to be the aqueous solution washing of 35% nitric acid, make the graphite after oxidation;

[0084] E...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of a fireproof organic negative ion coating, which comprises the following steps: preparing negative ion particles: mixing tourmaline powder and water underthe condition of magnetic stirring to obtain tourmaline suspension; adding rare earth salts into the tourmaline suspension and mixing to obtain a mixed solution; adding a precipitant into the mixed solution to precipitate, drying the precipitate to obtain negative ion particles; preparation of fireproof particles: graphite is mixed with a mixture solution of hydrogen peroxide and nitric acid by stirring to obtain oxidized graphite; mixing the oxidized graphite with water, and then adding glacial acetic acid into the oxidized graphite dropwise and stirring to obtain fireproof particles; preparation of fireproof organic anion coating: mixing and grinding PVC and fire-retardant particles to obtain abrasive; preparing the fireproof organic negative ion coating by adding negative ion particlesand processing aid into the abrasive and stirring. The fireproof organic negative ion coating has the advantages of high performance-price ratio, effective removal of organic hazards and good fireproofing performance.

Description

technical field [0001] The invention relates to the field of organic anion coatings, in particular to a fireproof organic anion coating and a preparation method thereof. Background technique [0002] Organic polymer materials are the main components of latex paints. As film-forming substances, they can bond other components in the paint to form a whole, adhere to the surface of the coated base layer, and form a film through its easy drying and curing characteristics. Continuous and tough film. Especially as a synthetic material, its high cost performance and other factors make it widely used. [0003] However, when in use, since it is an organic polymer material, it is easy to emit organic poisonous and harmful substances. And coating is often used for interior decoration etc., therefore, above-mentioned organic coating can bring great harm to human health when actually using. [0004] At the same time, the vast majority of organic polymers are flammable and other propert...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/06C09D5/18C09D7/62
Inventor 赖继平赖裕杰周梦娇
Owner 杭州琻泰环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com