Combined method and device for cracking and desulfurization and combined process of catalytic cracking and adsorptive desulfurization

A catalytic cracking and desulfurization catalyst technology, applied in hydrotreating process, petroleum industry, processing hydrocarbon oil, etc., can solve the problem of inability to meet the quality standard of clean fuel

Active Publication Date: 2019-05-07
CHINA PETROLEUM & CHEM CORP +1
View PDF14 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the continuous increase of sulfur content in catalytic cracking raw materials, the sulfur content of catalytic cracking products is also relatively high, which cannot meet the quality standards of clean fuels and must be post-treated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Combined method and device for cracking and desulfurization and combined process of catalytic cracking and adsorptive desulfurization
  • Combined method and device for cracking and desulfurization and combined process of catalytic cracking and adsorptive desulfurization
  • Combined method and device for cracking and desulfurization and combined process of catalytic cracking and adsorptive desulfurization

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0074] In one embodiment, the hydrocarbon oil desulfurization catalyst contains boron nitride, which has desulfurization and dehydrogenation properties and can improve the wear resistance of the catalyst. Reactions such as dehydrogenation and aromatization of naphthenic hydrocarbons generate hydrogen while generating high-octane aromatic components, reducing the consumption of hydrogen supply in the hydrocarbon oil desulfurization process, reducing the operation and application costs of the process, and the desulfurized gasoline produced. Quality has also been improved. Compared with desulfurization catalysts that do not use boron nitride, they have higher stability.

[0075] According to the present invention, the hydrocarbon oil desulfurization catalyst preferably contains 5-40% by weight of boron nitride, more preferably contains 12-25% by weight of boron nitride. According to the present invention, the hydrocarbon oil desulfurization catalyst contains the boron nitride, a...

Embodiment 1

[0110] 1. Preparation of hydrocarbon oil desulfurization catalyst

[0111] 4.43kg of zinc oxide powder (Headhorse company, purity 99.7% by weight) was mixed with 6.57kg of deionized water, and stirred for 30 minutes to obtain a mixed slurry of zinc oxide;

[0112] Take 1.81kg of pseudo-boehmite (Sinopec Catalyst Nanjing Branch, containing 1.36kg on a dry basis) and 2.4kg of hexagonal boron nitride (purity>99.0%, Qinhuangdao Yinuo High-tech Material Development Co., Ltd.) and stir and mix, then add After mixing 4.6kg of deionized water evenly to form a slurry, add 360ml of 30% by weight hydrochloric acid (chemically pure, produced by Beijing Chemical Factory) to make the slurry pH = 2.1, stir and acidify for 1 hour, then heat up to 80°C for aging for 2 hours, and then add zinc oxide The mixed slurry was mixed and stirred for 1 h to obtain a carrier slurry with a pH value of 3.5;

[0113] The resulting carrier slurry was used in Niro Bowen Nozzle Tower TM The model spray dryer...

Embodiment 2

[0129] 1. Preparation of hydrocarbon oil desulfurization catalyst

[0130] 3.21kg of tin tetrachloride (SnCl 4 ·5H 2 (2, Alfa company, 99%) slowly add the deionized water of 4.6kg, and add the nitric acid solution of 5% by weight of 4.6kg, stir slowly to avoid tin oxide crystallization, obtain colorless and transparent tin sol pH=2.1; Add 1.60 kg hexagonal boron nitride (purity>99.0%, Qinhuangdao Yinuo High-tech Material Development Co., Ltd.) was stirred and mixed, then 8.2 kg of deionized water was added and mixed evenly to form a slurry, and then 260 ml of 30% by weight hydrochloric acid was added to make the slurry pH=1.9 , stirred and acidified for 1 hour, then heated to 80°C for 2 hours of aging. After the temperature dropped, 5.52 kg of zinc oxide powder was added, and stirred for 1 hour to obtain a carrier slurry with a pH value of 3.5.

[0131] Referring to the method of Example 1, the catalyst carrier slurry was spray-dried and shaped, and the active component nic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a combined method and device for cracking and desulfurization and a combined process of catalytic cracking and adsorptive desulfurization. The method comprises the steps: (1)performing contact of heavy oil with a catalytic cracking catalyst so as to obtain a cracking product, (2) performing separation on the cracking product so as to obtain light fractions with final boiling points of 215-365 DEG C, (3) performing contact of the light fractions with a desulfurization catalyst at a hydrogen-oil volume ratio of 50-250 so as to obtain a desulfurized product, wherein thecomposition of the desulfurization catalyst comprises at least one sulfur-storing metal oxide, and (4) performing separation on the desulfurization product so as to obtain a liquefied petroleum gas fraction, a gasoline fraction and an optional light diesel fraction. Adsorptive desulfurization is performed directly on the liquefied gas and / or the gasoline and / or the diesel oil without separation, and separation is conducted on the LPG and the gasoline and / or the diesel oil after desulfurization is performed, so that the separation cost is reduced.

Description

technical field [0001] The invention relates to a cracking and desulfurization combined method and device and a combined process of catalytic cracking and adsorption desulfurization. Background technique [0002] With the increasing scarcity of crude oil resources, how to effectively utilize limited resources to produce light products in a large amount has become the goal pursued by refinery technology developers. On the other hand, with the continuous improvement of environmental protection requirements, environmental protection regulations are becoming increasingly strict. The current gasoline quality standard GB17930-2013 requires that the sulfur content in gasoline must be less than 10ppm from January 1, 2017. Therefore, the clean product production technology that can simultaneously increase the yield of the target product has become the choice of many refiners. [0003] In my country, catalytic cracking has been widely used due to its good operational flexibility, hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10G67/06
Inventor 宋烨林伟田辉平王磊刘俊
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com