Roller and preparation method of roller

A roll and molten iron technology, applied in the direction of roll, metal rolling, metal rolling, etc., can solve the problems of large differences in working layer structure, inoculation temperature, time influence, easy segregation, etc., and achieve the ability to maintain the accuracy of the roll surface Strong, eliminate tissue heredity, avoid tissue abnormal effects

Active Publication Date: 2019-05-03
XINGTAI DELONG MACHINERY & MILL ROLL CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 1. Using a large amount of precious alloys, the production cost is high and the resource consumption is large
[0005] 2. Due to the large difference in specific gravity, different alloys are prone to segregation in the working layer, which affects product quality
[0006] 3. The inoculation method and inoculant are greatly affected by the inoculation temperature and time, the inoculation effect is different, and the product quality consistency is poor
[0007] 4. When the working layer with high nickel and chromium is solidified, it is affected by the chilling effect of the mold. The structure of the working layer at different depths is quite different, and the hardness drop is large.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Roller and preparation method of roller

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] It should be noted that, in the case of no conflict, the embodiments of the present invention and the features in the embodiments can be combined with each other.

[0035] The present invention will be described in detail below in conjunction with examples.

[0036] The present embodiment relates to a kind of preparation method of roll, comprises the following steps:

[0037] S1. Use an intermediate frequency furnace to smelt the molten iron required for the outer layer of the roll. The melting temperature is 1300-1400°C. During the smelting process, adjust the composition of the molten iron so that the mass percentage of each element in the molten iron is:

[0038] C: 3.0%-3.5%, Si: 0.8%-1.5%, Mn: 0.8%-1.5%, Cr: 1.5%-2.5%, Ni: 4.0%-5.0%, Mo: 0.2%-1.0%, P< 0.05%, S<0.03%, balance Fe;

[0039] In this process, the smelting raw materials can use 40% high-nickel-chromium return material, 30% pig iron, 20% scrap steel and some alloys for batching, heating and dissolving, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a roller and a preparation method of the roller. The preparation method of the roller comprises the following steps of: firstly, smelting molten iron with qualified ingredientsof the outer layer of the roller, then heating to 1500 to 1550 DEG C, keeping the temperature for 30 minutes; pre-adding a silicon-zirconium alloy and a rare earth ferrosilicon alloy at the bottom ofa ladle; when the temperature of the molten iron drops to 1390 to 1420 DEG C, discharging the molten iron from a furnace into the ladle, and slagging off after discharging from the furnace; when the temperature of the molten iron drops to 1350 plus / minus 5 DEG C, adding a ferrosilicon alloy to the molten iron, and stirring until fully melting; preparing a funnel in advance at a pouring position, and preloading ferrosilicon particles in the funnel; and when the temperature of the molten iron drops to 1330 plus / minus 5 DEG C, transferring the ladle o the pouring position for pouring, and meanwhile uniformly introducing the ferrosilicon particles into a cavity along with the poured molten iron. The preparation method of the roller can improve the uniformity of an outer layer structure of theroller, and enables a working layer of the roller to better maintain the consistency of the structures in different thickness ranges. The roller has small hardness drop, high wear resistance and strong holding capacity of roller surface precision.

Description

technical field [0001] The invention relates to the technical field of roll preparation, in particular to a roll preparation method. Simultaneously, the invention also relates to a roll manufactured by using the roll preparation method. Background technique [0002] The roll is the main working part and tool for continuous plastic deformation of the processed metal on the rolling mill. In the existing roll preparation method, when preparing the outer layer of the roll, high-nickel-chromium molten iron is used, and ferrosilicon particles are used to inoculate the molten iron once or twice when it comes out of the furnace, and the molten iron is added by adding 0.2%- Precious alloys such as 1.0% V, 0.2%-1.5% Nb or 0.2%-1.0% W can improve the structure of the outer layer of the roll, that is, the working layer. [0003] The existing roll preparation method has the following problems: [0004] 1. A large amount of precious alloy is used, the production cost is high, and the r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22D19/16B22D13/02C22C37/08C22C37/10B21B27/00
Inventor 刘杰兵陈兴富刘向军
Owner XINGTAI DELONG MACHINERY & MILL ROLL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products