Smoke-free aromatherapy candle and manufacturing technology thereof

A manufacturing process and technology of smokeless incense, applied in candles, candle ingredients, fatty acid production, etc., can solve the problems of insufficient combustion of silicone-modified epoxy resins, increased flame retardancy of epoxy resins, indoor air pollution, etc. To achieve the effect of reducing toxic gas carbon monoxide, reducing the generation of combustion smoke, and improving hardness

Active Publication Date: 2019-04-19
蔓莎(苏州)工艺制品有限公司
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Methacrylic acid is a colorless crystal or transparent liquid with a pungent smell. It is soluble in hot water and most organic solvents such as ethanol and ether. It is easy to polymerize into a water-soluble polymer. , thermal decomposition can produce toxic gases; while epoxy resin is a high ignition point resin, the flame retardancy of epoxy resin modified by organosilicon resin increases, which makes it easy to appear insufficient combustion of organosilicon modified epoxy resin when burning
Therefore, if methacrylic acid and silicone-modified epoxy resin are added to the candle, the combustion chamber will easily produce a large amount of toxic gas carbon monoxide and carbon-containing smoke due to thermal decomposition or insufficient combustion, which will not only affect the aromatherapy effect, but also have a negative effect on the candle. indoor air pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Smoke-free aromatherapy candle and manufacturing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] A smokeless scented candle,

[0051] The raw materials are: coconut wax 80kg, soybean wax 50kg, palm wax 10kg, rose essential oil 1kg, nanometer calcium carbonate 1kg, aluminum ethyl acetate complex 2kg, octanol 2kg;

[0052] refer to figure 1 , its manufacturing method includes the following steps,

[0053] Mixed wax preparation: Put coconut wax, soybean wax and palm wax into wax melting tanks, heat until melted into a liquid state, and keep stirring during the heating process to obtain a mixed wax liquid;

[0054] Essential oil pretreatment: Put the weighed rose essential oil and nano-calcium carbonate into a high-speed mixer, and mix at a high speed of 3500rpm for 10 minutes; then put in the weighed octanol, and continue to mix at a high speed of 3500rpm for 20 minutes to obtain a rose essential oil mixture ;

[0055] Mixing: stop heating, when the temperature of the mixed wax liquid drops to 75°C, add aluminum ethyl acetate complex and rose essential oil mixture ...

Embodiment 2

[0059] A smokeless scented candle,

[0060] The raw materials are as follows: coconut wax 85kg, soybean wax 60kg, palm wax 15kg, rose essential oil 2kg, nano calcium carbonate 2kg, aluminum ethyl acetate complex 2kg, octanol 2kg;

[0061] refer to figure 1 , its manufacturing method includes the following steps,

[0062] Mixed wax preparation: Put coconut wax, soybean wax and palm wax into wax melting tanks, heat until melted into a liquid state, and keep stirring during the heating process to obtain a mixed wax liquid;

[0063] Essential oil pretreatment: Put the weighed rose essential oil and nano-calcium carbonate into a high-speed mixer, and mix at a high speed of 4000rpm for 10 minutes; then put in the weighed octanol, and continue to mix at a high speed of 4000rpm for 20 minutes to obtain a rose essential oil mixture ;

[0064] Mixing: stop heating, when the temperature of the mixed wax liquid drops to 75°C, add aluminum ethyl acetate complex and rose essential oil mi...

Embodiment 3

[0068] A smokeless scented candle,

[0069] The raw materials are: coconut wax 95kg, soybean wax 70kg, beeswax 15kg, rose essential oil 3kg, nano calcium carbonate 3kg, aluminum ethyl acetate complex 2kg, octanol 2kg;

[0070] refer to figure 1 , its manufacturing method includes the following steps,

[0071] Mixed wax preparation: Put coconut wax, soybean wax and beeswax into wax melting tanks, heat until melted into a liquid state, keep stirring during the heating process, and obtain a mixed wax liquid;

[0072] Essential oil pretreatment: Put the weighed rose essential oil and nano-calcium carbonate into a high-speed mixer, and mix at a high speed of 4500rpm for 10 minutes; then put in the weighed octanol, and continue to mix at a high speed of 4500rpm for 20 minutes to obtain a rose essential oil mixture ;

[0073] Mixing: stop heating, when the temperature of the mixed wax liquid drops to 75°C, add aluminum ethyl acetate complex and rose essential oil mixture in turn, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a smoke-free aromatherapy candle and belongs to the technical field of candles. The candle is characterized by being prepared from, by weight, 80-100 parts of carnauba wax, 50-80 parts of soy wax, 0-30 parts of beewax, 0-15 parts of palm wax, 1-5 parts of fragrant essential oil, 1-5 parts of nano inorganic filler, 1-3 parts of a burning promotion agent and 1-3 parts of C8-C10 fatty alcohol. The smoke-free aromatherapy candle burns thoroughly, generates few harmful substances such as smoke, and has good storage stability. The invention correspondingly discloses a manufacturing technology of the smoke-free aromatherapy candle. The technology comprises the steps of making of mixed wax, pretreatment of essential oil, mixing, filling and formation. The made smoke-free aromatherapy candle has the advantages of being low in burning smoke amount and environmentally friendly.

Description

technical field [0001] The invention relates to the technical field of candles and their manufacture, more specifically, to a smokeless scented candle and its manufacturing process. Background technique [0002] Scented candles feature a fresh and pleasant scent. Different from candles in the traditional sense, aromatherapy candles are a kind of craft candles, with rich and colorful appearance and beautiful colors. The natural plant essential oils contained in them emit a pleasant fragrance when burned, which has the functions of beauty care, soothing nerves , Purify the air, eliminate the effect of peculiar smell. [0003] The Chinese patent application publication number CN105316115A in the prior art discloses a scented candle, which is made of the following raw materials in parts by weight: 8-16 parts of geranium, 4-7 parts of dried orange peel, 2-5 parts of modifier 7-15 parts of methacrylic acid, 10-20 parts of silicone modified epoxy resin, 4-8 parts of surfactant, 6...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C11C5/00
CPCC11C5/002
Inventor 马振国
Owner 蔓莎(苏州)工艺制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com