Liquid seashell powder interior wall coating and preparation method thereof

A technology for interior wall paint and shell powder, which is applied in conductive coatings, coatings and other directions, can solve the problems of toxic substances, large errors, and difficulty in construction of dry powder shell powder coatings, so as to extend the shelf life, facilitate construction, Good anti-static effect

Inactive Publication Date: 2019-03-29
JILIN RIHE TECH DEV
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a liquid shell powder interior wall paint and its preparation method, which solves the problem that the common building interior wall paint in the prior art contains toxic substances, and the specific construction of dry powder shell powder paint is difficult and has large errors. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Liquid seashell powder interior wall coating and preparation method thereof
  • Liquid seashell powder interior wall coating and preparation method thereof
  • Liquid seashell powder interior wall coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A liquid shell powder interior wall paint, the paint is based on natural or artificially cultivated shell powder, and simultaneously adds nano-titanium dioxide and nano-tourmaline powder and polymer powdery materials irradiated with cobalt-60 gamma rays, which includes The components in parts by weight are:

[0022]

[0023]

[0024] The particle size of the shell powder is 500 mesh.

[0025] A preparation method of liquid shell powder interior wall paint, comprising the following steps:

[0026] The first step: firstly, the nano-titanium dioxide and nano-tourmaline powder need to be surface-modified, and the nano-titanium dioxide and nano-tourmaline powder are irradiated with cobalt-60 gamma rays. The irradiation dose: 20Mrad; irradiation temperature: 20°C; Down;

[0027] Step 2: Preparation of polymer material powder

[0028] Mix 20 parts of ethylene-vinyl acetate copolymers, 10 parts of acrylic acid copolymers and 5 parts of natural cellulose;

[0029] Step...

Embodiment 2

[0032] A liquid shell powder interior wall paint, the paint is based on natural or artificially cultivated shell powder, and simultaneously adds nano-titanium dioxide and nano-tourmaline powder and polymer powdery materials irradiated with cobalt-60 gamma rays, which includes The components in parts by weight are:

[0033]

[0034] The particle size of the shell powder is 1500 mesh.

[0035] A preparation method of liquid shell powder interior wall paint, comprising the following steps:

[0036] The first step: firstly, the nano-titanium dioxide and nano-tourmaline powder need to be surface-modified, and the nano-titanium dioxide and nano-tourmaline powder are irradiated with cobalt-60 gamma rays. The irradiation dose: 20Mrad; irradiation temperature: 20°C; Down;

[0037] Step 2: Preparation of polymer material powder

[0038] Mix 20 parts of ethylene-vinyl acetate copolymers, 10 parts of acrylic acid copolymers and 5 parts of natural cellulose;

[0039] Step Three: Pre...

Embodiment 3

[0042] A liquid shell powder interior wall paint, the paint is based on natural or artificially cultivated shell powder, and simultaneously adds nano-titanium dioxide and nano-tourmaline powder and polymer powdery materials irradiated with cobalt-60 gamma rays, which includes The components in parts by weight are:

[0043]

[0044] The particle size of the shell powder is 500 mesh.

[0045] A preparation method of liquid shell powder interior wall paint, comprising the following steps:

[0046] The first step: firstly, the nano-titanium dioxide and nano-tourmaline powder need to be surface-modified, and the nano-titanium dioxide and nano-tourmaline powder are irradiated with cobalt-60 gamma rays. The irradiation dose: 20Mrad; irradiation temperature: 20°C; Down;

[0047] Step 2: Preparation of polymer material powder

[0048] Mix 50 parts of ethylene-vinyl acetate copolymers, 40 parts of acrylic acid copolymers and 20 parts of natural cellulose;

[0049] Step Three: Pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A liquid seashell powder interior wall coating is obtained by adding nanometer titanium dioxide and nanometer tourmaline powder which are radiated with cobalt-60 gamma rays and a high-molecular powdermaterial to natural or artificially-cultured seashell powder used as a basic material. The coating includes, by weight, 60-90 parts of water, 30-60 parts of seashell powder, 20 parts of heavy calcium, 10 parts of kaolin, 8 parts of benzalkonium chloride, 1-5 parts of nanometer titanium dioxide, 1-5 parts of the nanometer tourmaline powder and 5-20 parts of the high-molecular powder material, andthe particle size of the seashell powder is 500-1500 meshes. The benzalkonium chloride is medical benzalkonium chloride. The coating further includes 20-80 parts of a plant pigment. The problem of toxic substances in common building interior wall coatings in the prior art and the problems of great difficulty and large error in concrete construction of dry powder type seashell powder coatings in the prior art are solved in the invention.

Description

technical field [0001] The invention relates to the field of liquid wall coatings, in particular to a liquid shell powder interior wall coating and a preparation method thereof. Background technique [0002] The architectural interior wall coatings used in the market are mainly latex paints. Latex paints generally have disadvantages such as soft paint film, long drying time, and poor storage stability. After the latex paint is damp, it is easy to breed bacteria, cause peeling, discoloration, etc., which seriously affects the service life and indoor appearance. At the same time, latex paint consumes a lot of oil. Due to the lack of oil resources in our country, a large amount of oil needs to be imported, and the cost of raw materials is increasing year by year. The development of my country's social economy has increased the demand for coatings and raised people's requirements for the performance of coatings. In the interior decoration process, a large number of decoration ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D1/00C09D7/61C09D7/65C09D7/63C09D5/24
CPCC09D1/00C09D5/24C09D7/61C09D7/63C09D7/65
Inventor 杨健
Owner JILIN RIHE TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com