A kind of refining method of scrap copper containing tin and lead

A technology for scrapping miscellaneous copper and tin-lead, applied in the direction of lead halide, tin chloride, tin halide, etc.

Active Publication Date: 2020-08-11
UNIV OF SCI & TECH BEIJING
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the technical problem of high lead and tin in the above-mentioned complex and multi-component waste copper recycling raw materials, and propose an economical and effective method for refining lead and tin, which realizes the purpose of multi-level utilization of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] In the waste miscellaneous copper raw material, tin content (weight percentage) 3.5%, lead content (weight percentage) 4.3%, waste miscellaneous copper raw material is through sorting pretreatment, after shredding, get 20g sample and mix into 10% powdery cupric chloride And mix evenly, place in the tube, vacuum 0.15atm, 1000 ℃ high temperature treatment 1h, natural cooling, tin content (weight percentage) 0.45% in the scrap miscellaneous copper sample after processing, lead content (weight percentage) 0.21%.

Embodiment 2

[0024] In the waste miscellaneous copper raw material, tin content (weight percentage) 3.5%, lead content (weight percentage) 4.3%, waste miscellaneous copper raw material is through sorting pretreatment, after shredding, get 20g sample and mix into 10% powdery cupric chloride And mix evenly, place in the tube furnace, vacuum 0.3atm, 1100 ℃ of high temperature treatment 1h, natural cooling, tin content (weight percentage) 0.43% in the scrap miscellaneous copper sample after processing, lead content (weight percentage) 0.32% .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a refining method of tin-lead contained scrap copper, and belongs to the technical field of reclaimed copper refining. The content of copper in the scrap copper raw material ranges from 80 to 90%, the content of tin-lead ranges from 6 to 10%, and a main treatment process comprises sorting pre-treatment, shearing, mixing, and controlled pressure high-temperature treatment.The scrap copper raw material is firstly subjected to sorting pre-treatment, a shearing machine is used for shearing, copper chloride is added in a high-temperature vacuum furnace for treatment underthe controlled-pressure condition that the pressure ranges from 0.01 to 0.8 atm at the temperature of 700 to 1100 DEG C, volatile matter is subjected to two-segment cooling, lead chloride and tin chloride are obtained, the tin-lead impurity content in the treated scrap copper can be greatly reduced, and the aim of purifying reclaimed copper is achieved.

Description

technical field [0001] The invention belongs to the technical field of secondary copper refining, and in particular relates to a refining method of scrap copper containing tin and lead. [0002] technical background [0003] Commonly used copper alloys include brass, bronze, and white copper. However, in order to meet different effects during use, the three types of copper alloys are often doped with other elements to improve the different properties of the alloy. With the end of the service life of copper alloys, and in order to alleviate the contradiction between the consumption and production of copper resources in my country, the proportion of scrap copper recycling is becoming more and more obvious. Because of the diversity of elements in the copper alloy, the complexity of the elements in the recycled raw materials is caused, which contains a grade of copper of 80-90% and a content of lead and tin of 6-10%. Due to the high content of lead and tin in the raw material, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B7/00C22B15/00C01G19/08C01G21/16
CPCC01G19/08C01G21/16C22B7/001C22B15/006Y02P10/20
Inventor 王成彦刘伟赵洪亮刘风琴郭淑梅黄腾杨东超
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com