A kind of sodium ion battery anode material and preparation method thereof of reduced graphene oxide loaded with antimony

A sodium-ion battery and negative electrode material technology, which is applied in the field of electrochemical energy storage, can solve the problems of easy pulverization of electrode materials, poor cycle performance, and battery capacity attenuation, and achieve the effect of simple method, low cost, and excellent cycle rate performance

Active Publication Date: 2021-07-20
BEIHANG UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to overcome the volume change of the antimony-based negative electrode material of the sodium ion battery in the prior art during the removal / intercalation of sodium, the electrode material is easy to pulverize after repeated charge and discharge, resulting in battery capacity attenuation and poor cycle performance. The present invention provides a reduction oxidation Graphene-loaded antimony sodium ion battery negative electrode material and preparation method thereof, the method uses antimony trichloride, ammonia water, flake graphite as raw materials, utilizes chemical oxidation method and exfoliation method to prepare graphene oxide, improves liquid phase synthesis method in oxidation Antimony precursor particles are loaded on the graphene sheet, and the anode material of sodium ion battery with antimony loaded on reduced graphene oxide is finally obtained by thermal reduction treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of sodium ion battery anode material and preparation method thereof of reduced graphene oxide loaded with antimony
  • A kind of sodium ion battery anode material and preparation method thereof of reduced graphene oxide loaded with antimony
  • A kind of sodium ion battery anode material and preparation method thereof of reduced graphene oxide loaded with antimony

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The preparation method of the sodium ion battery negative electrode material of reduced graphene oxide loaded with antimony:

[0030] Step 1: Preparation of graphene oxide.

[0031] Step 101. Weigh 10g flake graphite and 7.5g NaNO 3 In the beaker, slowly add 300ml of concentrated sulfuric acid (98%), and magnetically stir until uniform; slowly add 40g of potassium permanganate under magnetic stirring, and continue to stir for 96 hours to obtain a black gelatinous substance.

[0032]Step 102. Add 800ml of deionized water and 60ml of hydrogen peroxide (30%) to the black colloidal substance in turn, stir until uniform, and obtain a yellow solution; centrifuge the obtained yellow solution at 6000rpm at a high speed for 5 minutes to obtain a high-speed centrifuge Product; further preferably, the high-speed centrifugation process is repeated 3 to 5 times, and the high-speed centrifugation product is taken after washing with water until the supernatant is neutral.

[0033] S...

Embodiment 2

[0043] Preparation method of reduced graphene oxide loaded antimony negative electrode material:

[0044] Step 1: with embodiment 1.

[0045] Step 2: Weigh 2g of antimony trichloride in a glass bottle, add 10ml of ethanol dropwise, and obtain 10ml of 0.8M colorless and clear antimony trichloride ethanol solution after ultrasonication for 0.5h; Graphene oxide was dispersed in 40ml ethanol solution by ultrasound for 1h to obtain a dark brown solution; 0.18ml of ammonia water (25%) was added dropwise to the graphene oxide ethanol solution, and magnetically stirred for 3h; ml colorless and clear solution, connect the syringe to the extension tube, exhaust and check that there are no bubbles, fix it on the syringe pump fixing plug, start the syringe pump, add the colorless and clear solution dropwise at a flow rate of 0.1mL / min, and continue to stir for 12h. Obtain a dark gray solution; centrifuge the dark gray solution at 8500rpm for 8min and dry the precipitate at 80°C for 10h t...

Embodiment 3

[0050] Step 1: Graphene oxide preparation:

[0051] Take 8g of flake graphite and weigh NaNO according to the mass ratio of 4:3 3 , the two are mixed in a beaker, and slowly add 200ml of concentrated sulfuric acid (mass percentage concentration is 98%) in the beaker, and magnetically stir until uniform;

[0052] Slowly add 30g potassium permanganate under magnetic stirring condition, and continue to stir for 96 hours, obtain black colloidal substance; In black colloidal substance, add 800ml deionized water and 70ml hydrogen peroxide (the mass percent concentration of hydrogen peroxide is 30%) successively, Stir until uniform to obtain a yellow solution;

[0053] Centrifuge the obtained yellow solution at high speed, and wash with water until the supernatant is neutral; add the high-speed centrifuged product to deionized water again and stir evenly, after ultrasonic treatment, place it in a centrifuge, centrifuge at low speed, and collect the gray-brown viscous liquid in the u...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
current efficiencyaaaaaaaaaa
current efficiencyaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sodium ion battery anode material for reducing graphene oxide and supporting antimony and a preparation method thereof, and relates to the technical field of electrochemical energy storage. The invention uses antimony trichloride, ammonia water and flake graphite as raw materials, uses chemical oxidation method and exfoliation method to prepare graphene oxide, improves liquid phase synthesis method to load antimony precursor particles on the graphene oxide sheet layer, and finally conducts thermal reduction treatment The anode material of sodium ion battery supported by reduced graphene oxide with antimony is obtained. The sodium ion battery negative electrode material of the reduced graphene oxide supported antimony of the present invention has excellent cycle rate performance; at 2A g ‑1 After 100 cycles at high current density, Sb‑rGO still maintains 140mAh g ‑1 The above capacity is maintained, and the coulombic efficiency is maintained at more than 97%; the preparation method provided by the present invention does not need to add surfactants and reducing agents, the method is simple, the cost is low, and it is suitable for large-scale preparation.

Description

technical field [0001] The invention relates to the technical field of electrochemical energy storage, and mainly relates to a sodium ion battery negative electrode material with antimony supported on reduced graphene oxide and a preparation method thereof. Background technique [0002] With the depletion of fossil energy such as petroleum, coal, and natural gas, and the increasing environmental problems caused by the excessive application of fossil energy, the rapid development of science, technology and economic construction has an imminent demand for renewable and clean energy. Energy storage technology, especially for electric energy storage technology, is particularly important in solving the problem of energy crisis. Recyclable charge-discharge lithium-ion has higher energy density and power density than traditional chemical batteries, and has excellent properties such as slow self-discharge rate and high working voltage. However, lithium resources are unevenly distri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/38H01M4/62H01M4/134
CPCH01M4/134H01M4/38H01M4/625Y02E60/10
Inventor 毕晓昉钟志鹏李进
Owner BEIHANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com