Paper cigarette filter stick containing collagen fibers and preparation method thereof

A technology of collagen fibers and cigarette filter rods, which is applied in the manufacture of cigarettes, fiber chemical characteristics, organic non-cellulose fibers, etc., can solve the problems affecting paper quality and performance, collagen fiber bundles cannot be fully opened, and fiber interstitial cannot be completely Eliminate and other problems to achieve the effect of increasing the added value of the product, improving the sweetness, reducing the content of tar and harmful ingredients

Active Publication Date: 2019-03-01
CHINA TOBACCO SICHUAN IND CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent CN101050602A provides a paper made of collagen fibers and its processing method, which can solve the problems of poor quality of paper made from plant fibers and damage to natural resources, as well as the high price of chemical fiber paper; at the same time, it can also solve the problem of skin or leather waste the reuse problem
However, in the above patents, either due to the use of chromium-containing leather waste, dechrome removal is required, resulting in complex production processes; or due to insufficient treatment, the collagen fiber bundles cannot be fully opened, and the fiber matrix cannot be completely removed, which affects the paper quality and quality. Performance
At the same time, there is no report on the use of paper containing collagen fibers for the preparation of cigarette filter rods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paper cigarette filter stick containing collagen fibers and preparation method thereof
  • Paper cigarette filter stick containing collagen fibers and preparation method thereof
  • Paper cigarette filter stick containing collagen fibers and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] (1) Preparation of collagen fiber: liming: make the two-layer gray skin sheet of cowhide into 1.5mm thick, put it into the drum, add water with 100% to 200% gray skin weight and 1% to 4% slaked lime, and rotate it for 12 hours at room temperature. ~18 hours; deliming: control water, add 200% water of gray skin weight and 0.1%~0.5% ammonium sulfate, rotate for 20~24 hours; control water, add water 100%~150% gray skin weight, 0.1 %~0.5% non-ionic degreaser and 2%~3% ammonium sulfate, rotate for 1.5 hours; softening: control water, add 50% water of gray skin weight, 0.5% ammonium sulfate and 1.0%~1.5% softening Enzyme, rotate for 30 minutes; water washing: control water, add 200% to 300% water, wash with water for 20 minutes; demineralization: control water, add deionized water with 100% gray leather weight, and rotate for 4 to 6 hours; Add water, add absolute ethanol with 100% gray skin weight, and rotate for 2 hours. This operation must be carried out several times, and ...

Embodiment 2

[0021] (1) Preparation of collagen fiber: liming: make the two-layer gray skin sheet of cowhide into 1.5mm thick, put it into the drum, add water with 100% to 200% gray skin weight and 1% to 4% slaked lime, and rotate it for 12 hours at room temperature. ~18 hours; deliming: control water, add 200% water of gray skin weight and 0.1%~0.5% ammonium sulfate, rotate for 20~24 hours; control water, add water 100%~150% gray skin weight, 0.1 %~0.5% non-ionic degreaser and 2%~3% ammonium sulfate, rotate for 1.5 hours; softening: control water, add 50% water of gray skin weight, 0.5% ammonium sulfate and 1.0%~1.5% softening Enzyme, rotate for 30 minutes; water washing: control water, add 200% to 300% water, wash with water for 20 minutes; demineralization: control water, add deionized water with 100% gray leather weight, and rotate for 4 to 6 hours; Water, add absolute ethanol with 100% weight of the gray hide, and rotate for 2 hours. This operation must be carried out several times, a...

Embodiment 3

[0025] (1) Preparation of collagen fiber: liming: make the two-layer gray skin sheet of cowhide into 1.5mm thick, put it into the drum, add water with 100% to 200% gray skin weight and 1% to 4% slaked lime, and rotate it for 12 hours at room temperature. ~18 hours; deliming: control water, add 200% water of gray skin weight and 0.1%~0.5% ammonium sulfate, rotate for 20~24 hours; control water, add water 100%~150% gray skin weight, 0.1 %~0.5% non-ionic degreaser and 2%~3% ammonium sulfate, rotate for 1.5 hours; softening: control water, add 50% water of gray skin weight, 0.5% ammonium sulfate and 1.0%~1.5% softening Enzyme, rotate for 30 minutes; water washing: control water, add 200% to 300% water, wash with water for 20 minutes; demineralization: control water, add deionized water with 100% gray leather weight, and rotate for 4 to 6 hours; Water, add absolute ethanol with 100% weight of the gray hide, and rotate for 2 hours. This operation must be carried out several times, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a paper cigarette filter stick containing collagen fibers and a preparation method thereof. The paper cigarette filter stick is prepared from the following raw materials in percentage by weight: 1-90% of the collagen fibers and 10-99% of fibers used for papermaking. The preparation method of the paper cigarette filter stick containing the collagen fibers comprises the following steps that collagen fiber paper is prepared; the collagen fiber paper is subjected to roll-in, rolling and wrapping shaping by adopting a paper filter stick conventional shaping technology, so that the paper cigarette filter stick containing the collagen fibers is prepared. According to the paper filter stick prepared through the method, tar and other harmful components in cigarette smoke canbe effectively reduced, and meanwhile, effects of a common paper filter stick on absorbing a cigarette smoke flavor are improved.

Description

technical field [0001] The invention relates to the technical field of cigarette filter rod preparation, in particular to a paper cigarette filter rod containing collagen fibers and a preparation method thereof. Background technique [0002] In the modern cigarette industry, cigarette filter sticks, as an indispensable part of cigarettes, undertake the important function of reducing tar and harm. At present, the filter element of the filter rod is mainly made of acetate fiber or polypropylene fiber. These fibers may enter the human body with the smoking of cigarettes and cause damage to human health. As people continue to pay attention to smoking and health issues, the emerging paper filter sticks cater to the development needs of the industry. Paper filter sticks have a good interception effect on flue gas, and at the same time, its raw materials are naturally renewable and low in cost, and paper filter sticks are more likely to be degraded. However, the paper filter rod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H15/10D21H13/34A24D3/18D01F4/00
CPCA24D3/18D01F4/00D21H13/34D21H15/10
Inventor 周建李东亮施丰成黄馨
Owner CHINA TOBACCO SICHUAN IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com