Lavender high molecular composite material and preparation method thereof

A composite material, lavender technology, applied in the field of composite materials, can solve problems such as poor perspiration ability, insufficient ventilation, and damage to the environment, and achieve the effect of reducing production costs and protecting the natural environment

Inactive Publication Date: 2019-03-01
广东腾克体育发展有限公司
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the field of daily necessities and sports equipment, EVA (ethylene-vinyl acetate copolymer) rubber and plastic products are new environmentally friendly plastic foam materials, which have good cushioning, shock resistance, heat insulation, moisture resistance, chemical corrosion resistance, non-toxic, non-absorbent, etc. Advantages, so it is often used in slippers, insoles, cushions, cushions, basketballs, footballs, etc. However, products made of EVA foam have shortcomings such as insufficient ventilation and poor perspiration ability during use, and EVA foam When foaming, it is necessary to add calcium carbonate or talcum powder as a filler. Calcium carbonate or talc powder is collected in the natural environment. Using too much will not only damage the environment but also increase the cost of foaming. Therefore, it is necessary to develop a green and environmentally friendly foaming agent. , Composite materials with better performance are used for daily necessities and sports equipment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039]The embodiment 1 of lavender polymer composite material preparation method comprises the following steps:

[0040] ① After the natural lavender is harvested, it is stored at 80°C-95°C for 20-25 hours for drying treatment, and the lavender is made into lavender powder, and the lavender powder reaching the standard of 2000-3000 mesh is screened out;

[0041] ②Choose 1.8~2.2 parts of lavender powder, 0.8~1.2 parts of rubber and plastic materials, store them at 115℃~125℃ for 18~20 minutes, add sulfur for vulcanization treatment, and then enter the mixer, and the mixer is fully mixed After refining the vulcanized raw materials, they are transported to the granulator, and the granulator produces lavender masterbatch;

[0042] ③Choose 23%-27% of lavender masterbatch, 55%-65% of rubber and plastic materials, and 8%-12% of resin, mix for 14-16 minutes, then add 4%-6% of cross-linking agent and mix for 4-6 minutes Lavender foaming raw material;

[0043] ④Put the lavender foaming...

Embodiment 2

[0044] The embodiment 2 of lavender polymer composite material preparation method comprises the following steps:

[0045] ① After the natural lavender is harvested, it is stored at 90°C for 24 hours for drying treatment, and the lavender is made into lavender powder, and the lavender powder reaching the standard of 2500 mesh is screened out;

[0046] ②Choose 1.8-2.2 parts of lavender powder and 0.8-1.2 parts of rubber and plastic materials, store them at 120°C for 20 minutes and add sulfur for vulcanization treatment, then enter the mixer, and the mixer fully mixes the vulcanized raw materials Finally, it is transported to the granulator, and the granulator produces the lavender masterbatch;

[0047] ③Choose 23%~27% of lavender masterbatch, 55%~65% of rubber and plastic materials, and 8%~12% of resin and mix them for 15 minutes, then add 4%~6% of cross-linking agent and mix for 5 minutes to make lavender foaming raw materials ;

[0048] ④Put the lavender foaming raw material...

Embodiment 3

[0049] The embodiment 3 of lavender polymer composite material preparation method comprises the following steps:

[0050] ①The natural lavender is harvested and stored at 85°C for 25 hours for drying, and the lavender is made into lavender powder, and the lavender powder reaching the standard of 3000 mesh is screened out;

[0051] ②Choose 1.8-2.2 parts of lavender powder and 0.8-1.2 parts of rubber and plastic materials, store them at 123°C for 19 minutes, add sulfur for vulcanization treatment, and then enter the mixer, which fully mixes the vulcanized raw materials Finally, it is transported to the granulator, and the granulator produces the lavender masterbatch;

[0052] ③Choose 23%~27% of lavender masterbatch, 55%~65% of rubber and plastic materials, and 8%~12% of resin and mix for 14 minutes, then add 4%~6% of cross-linking agent and mix for 6 minutes to make lavender foaming raw material ;

[0053] ④Put the lavender foaming raw material into the Lena machine for cross-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a lavender high molecular composite material and a preparation method thereof. The lavender high molecular composite material is prepared from the following components in percentage by mass: 23 to 27 percent of lavender master batch, 55 to 65 percent of a rubber-plastic material, 8 to 12 percent of resin and 4 to 6 percent of a cross-linking agent, wherein the lavender master batch is prepared from 1.8 to 2.2 parts of lavender powder and 0.8 to 1.2 parts of the rubber-plastic material; lavender is used as a base material of the lavender high molecular composite material; properties including long aroma, sedative and hypnotic effects, spasmolysis, antibacterial effect, nerve protection, lipid lowering, neurosis treatment and the like of the lavender are sufficientlyutilized; when being used, the lavender high molecular composite material can be used for refreshing, enhancing the memory, alleviating nerves, building characters and promoting blood circulation andcan be used for treating whelk, nourishing hairs, inhibiting hypertension and allergic rhinitis asthma and regulating physiological functions; the lavender high molecular composite material can be used for enhancing immunity, keeping functions of respiratory tracts, has a very good curative effect on nose and throat mucositis, and is especially applicable to articles for daily use and sports equipment.

Description

technical field [0001] The invention relates to the field of composite materials, in particular to a lavender polymer composite material and a preparation method thereof. Background technique [0002] In the field of daily necessities and sports equipment, EVA (ethylene-vinyl acetate copolymer) rubber and plastic products are new environmentally friendly plastic foam materials, which have good cushioning, shock resistance, heat insulation, moisture resistance, chemical corrosion resistance, non-toxic, non-absorbent, etc. Advantages, so it is often used in slippers, insoles, cushions, cushions, basketballs, footballs, etc. However, products made of EVA foam have shortcomings such as insufficient ventilation and poor perspiration ability during use, and EVA foam When foaming, it is necessary to add calcium carbonate or talcum powder as a filler. Calcium carbonate or talc powder is collected in the natural environment. Using too much will not only damage the environment but als...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L101/00C08L99/00C08K3/06C08J9/00
CPCC08J9/00C08J2300/00C08J2499/00C08K3/06
Inventor 李上权张浩源李小冰
Owner 广东腾克体育发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com