Thermal insulation coating for waterborne acrylic finishing coat and preparation method thereof

An acrylic type, heat-insulating paint technology, applied in the direction of coating, can solve the problem of little development of heat-insulating paint, and achieve the effect of smooth appearance and good thermal conductivity.

Inactive Publication Date: 2019-02-22
佛山市顺德区巴德富实业有限公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] It is suitable for acrylic topcoats on architectural coatings or metal surfaces. Use heat-insulating coatings to block the contact and conduction of ultraviolet heat and substrates by insulating heat conduction on the surface of the substrate. It can be applied to ordinary building exterior walls and metal storage tanks, Metal containers and other industries, due to technical limitations, there is little domestic development of heat-insulating coatings, which has a relatively good market prospect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A heat-insulating coating for water-based acrylic topcoat, comprising the following raw materials in parts by weight: 20 parts of acrylic emulsion resin, 10 parts of hollow glass microspheres, 10 parts of pigment, 10 parts of filler, and 0.1 part of wetting agent , 0.1 part of antifreeze, 0.1 part of thickener, 0.1 part of dispersant, 0.1 part of neutralizer, 0.1 part of defoamer, 0.1 part of leveling agent, 0.1 part of coalescent, 10 parts of water.

[0035] For the heat-insulating paint used for water-based acrylic topcoats, water, wetting agent, antifreeze, thickener and dispersant are added to the disperser in sequence under low-speed stirring, and hollow glass microspheres are added after the low-speed dispersion is uniform, and then Add pigments and fillers, stir at a low speed with a disperser, add acrylic emulsion resin, and then add film-forming aids, neutralizers, defoamers, and leveling agents, and then disperse for 15 minutes to control the viscosity to obtai...

Embodiment 2

[0037] A heat-insulating coating for water-based acrylic topcoat, comprising the following raw materials in parts by weight: 40 parts of acrylic emulsion resin, 12 parts of hollow glass microspheres, 13 parts of pigment, 20 parts of filler, and 1 part of wetting agent , 1 part of antifreeze, 1 part of thickener, 1 part of dispersant, 1 part of neutralizer, 1 part of defoamer, 1 part of leveling agent, 3 parts of coalescent, 20 parts of water.

[0038] For the heat-insulating paint used for water-based acrylic topcoats, water, wetting agent, antifreeze, thickener and dispersant are added to the disperser in sequence under low-speed stirring, and hollow glass microspheres are added after the low-speed dispersion is uniform, and then Add pigments and fillers, stir at a low speed with a disperser, add acrylic emulsion resin, and then add film-forming aids, neutralizers, defoamers, and leveling agents, and then disperse for 15 minutes to control the viscosity to obtain the required ...

Embodiment 3

[0040] A heat-insulating coating for water-based acrylic topcoat, comprising the following raw materials in parts by weight: 60 parts of acrylic emulsion resin, 15 parts of hollow glass microspheres, 15 parts of pigment, 30 parts of filler, and 2 parts of wetting agent , 2 parts of antifreeze, 2 parts of thickener, 2 parts of dispersant, 2 parts of neutralizer, 2 parts of defoamer, 2 parts of leveling agent, 5 parts of coalescent, 30 parts of water.

[0041] For the heat-insulating paint used for water-based acrylic topcoats, water, wetting agent, antifreeze, thickener and dispersant are added to the disperser in sequence under low-speed stirring, and hollow glass microspheres are added after the low-speed dispersion is uniform, and then Add pigments and fillers, stir at a low speed with a disperser, add acrylic emulsion resin, and then add film-forming aids, neutralizers, defoamers, and leveling agents, and then disperse for 15 minutes to control the viscosity to obtain the re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses thermal insulation coating for waterborne acrylic finishing coat. The thermal insulation coating contains the following raw materials in parts by weight: 20-60 parts of acrylicemulsion resin, 10-15 parts of hollow glass microspheres, 10-15 parts of pigment, 10-30 parts of filler, 0.1-2 parts of wetting agent, 0.1-2 parts of antifreezing agent, 0.1-2 parts of thickening agent, 0.1-2 parts of dispersing agent, 0.1-2 parts of neutralizing agent, 0.1-2 parts of antifoaming agent, 0.1-2 parts of leveling agent, 0.1-5 parts of coalescing agent and 10-30 parts of water. The thermal insulation coating for waterborne acrylic finishing coat has smooth appearance, glass microspheres therein, good thermal conductivity isolation, flexibility, weather resistance, water resistance, easy application property, stain resistance, and bonding strength possessed by an outer wall.

Description

technical field [0001] The invention relates to a heat-insulating coating for water-based acrylic topcoat and a preparation method thereof. Background technique [0002] Acrylic topcoat is a one-component quick-drying topcoat composed of thermoplastic acrylic resin, pigments, additives, solvents, etc. The paint has good color retention and construction performance. Provide protection and decoration for outdoor walls, steel structures, mechanical equipment, motors, etc., and can also be used as a topcoat for relief coating systems. [0003] It is suitable for acrylic topcoats on architectural coatings or metal surfaces. Use heat-insulating coatings to block the contact and conduction of ultraviolet heat and substrates by insulating heat conduction on the surface of the substrate. It can be applied to ordinary building exterior walls and metal storage tanks, For metal container and other industries, due to technical limitations, there is little domestic development of heat-i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D7/61
CPCC08K2003/2241C08K2003/265C09D7/61C09D7/70C09D133/00C08K7/28C08K3/22C08K3/346C08K3/26
Inventor 李晨鸽韩舟
Owner 佛山市顺德区巴德富实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com