Mixed spinning method for three-dimensional crimp acrylic fiber

An acrylic fiber, three-dimensional crimping technology, applied in the field of spinning, can solve the problems of restricting the application of three-dimensional crimping acrylic fibers, poor sliver cohesion, easy to straighten, etc., and achieves good application prospects, lasting crimp shape, and improving the effect of cohesion.

Inactive Publication Date: 2019-02-19
SHANGHAI RISOO TECH TEXTILE
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] As we all know, the bulking degree of bulked yarn is the degree of expansion of the original yarn after heat and humidity treatment. It is the main factor determining the bulkiness, softness and elasticity of the finished fabric. However, it is difficult to control the shrinkage of each batch, so The stability of product quality is difficult to guarantee, and it can only be washed in warm and cold water with low temperature. The yarn stability is poor, which limits the further application of three-dimensional crimped acrylic fiber
[0004] In the existing technology, the three-dimensional crimped fiber has been prepared by melt spinning method. If the crimp is high, the fiber is easy to shrink into a small ball, which is not conducive to the smooth opening and drafting, resulting in many neps on the yarn. Affect the quality of yarn; if the degree of crimp is too low, the fiber can hardly withstand the drafting of multiple processes, it is easy to straighten and lose its important characteristics, the sliver cohesion is poor, the spinnability and yarn quality are not good, and the process requirements are too harsh

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Raw materials: 1. Three-dimensional curly acrylic fiber: 40%, 2.0dtex*51mm;

[0024] 2. Wool fiber: 60%, main body length 55-60mm.

[0025] Routing:

[0026] Three-dimensional crimped acrylic fiber: plucking machine-opener-lapping machine-carding machine-pre-doubling-A strip;

[0027] Wool ball: wool top stretching machine-pre-merging-B strip;

[0028] A and B are carried out according to the weight ratio of 40% and 60%: mixed head-mixed two-mixed three-roving-spun yarn-self-winding.

[0029] Twist factor: 220-300.

[0030] Adopt the technological parameters of above-mentioned process to form yarn quality index:

[0031] Breaking strength: 15cN / tex; evenness cv%: 13; details: 17 pieces / km; thick places: 15; neps: 21.

[0032] The obtained fabric (30s) shows the comfort and fineness of wool and the fluffy and weightless feeling of three-dimensional curly acrylic fibers, which endows traditional sweaters with a strong sense of warmth and lightness, making the product...

Embodiment 2

[0034] Raw materials: 1. Three-dimensional curly acrylic fiber: 40%, 2.0dtex*51mm;

[0035] 2. Viscose fiber or modal fiber: 60%.

[0036] Routing:

[0037] Cotton boxes are used to mix, and then go through plucking machine-opener-lapping machine-carding machine-head doubling-two doubling-three doubling-roving-spun yarn-self-winding.

[0038] Twist factor: 300-330.

[0039] Adopt the technological parameters of above-mentioned process to form yarn quality index:

[0040] Breaking strength: 13cN / tex; evenness cv%: 14; details: 19 pieces / km; thick places: 11; neps: 26.

[0041] The obtained knitted fabric (40s) is soft to the touch. Due to the addition of three-dimensional curly acrylic fiber, the fabric overcomes the defect of wool-free and not fluffy enough for sweaters made of regenerated cellulose fiber, and it is more prominent in warmth and lightness. It can be made into high-end clothing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
twist factoraaaaaaaaaa
twist factoraaaaaaaaaa
Login to View More

Abstract

The invention relates to a mixed spinning method for three-dimensional crimp acrylic fiber. The mixed spinning method comprises the steps that (1) maintenance treatment is carried out on the three-dimensional crimp acrylic fiber, and then blowing and cotton carding are carried out to form slivers; (2) the three-dimensional crimp acrylic fiber is mixed with other textile fiber, lastly, roving, spinning and spooling are carried out, and the three-dimensional crimp acrylic fiber is obtained. The mixed spinning method for the three-dimensional crimp acrylic fiber has the advantages that own crimpcharacter of the fiber is utilized, the fiber is not influenced easily in subsequent processing and use process and loses the three-dimensional crimp feature, fabric has a memory effect through mixedspinning, and the crimp form is durable; the fluffiness and the heat retention are stronger, the hand feeling is more comfortable, the cohesive force of the fiber during processing and the size stability of the fabric are improved, and the application prospect is good.

Description

technical field [0001] The invention belongs to the field of spinning, in particular to a mixed spinning method of three-dimensional crimped acrylic fibers. Background technique [0002] Three-dimensional crimped acrylic fiber is a composite acrylic fiber developed by Japan Toyobo. It is similar to the principle of bulked yarn. The three-dimensional crimped fiber is formed due to the different shrinkage rates of different components in the raw material. The fabric made of this fiber has a plump hand feeling, which is closer to wool fabric, and has good elasticity. [0003] As we all know, the bulking degree of bulked yarn is the degree of expansion of the original yarn after heat and humidity treatment. It is the main factor determining the bulkiness, softness and elasticity of the finished fabric. However, it is difficult to control the shrinkage of each batch, so The stability of the product quality is difficult to guarantee, and it can only be washed in warm and cold wat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04
CPCD02G3/04D10B2201/22D10B2201/24D10B2211/02D10B2321/10
Inventor 曹文
Owner SHANGHAI RISOO TECH TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products