A kind of porous cross-linked polystyrene light diffusion agent and PC light diffusion plate and preparation method thereof

A technology of cross-linked polystyrene and light diffusing agent, used in lighting and heating equipment, light sources, semiconductor devices of light-emitting elements, etc. Effect

Active Publication Date: 2021-02-19
BEIJING UNIV OF CHEM TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a porous cross-linked polystyrene light diffusing agent and PC light diffusing plate and its preparation method, to solve the problem of glare caused by the characteristics of high directivity and high color temperature of LED light emitting in the prior art, Under the premise of minimizing the loss of light transmittance, improve the light uniformity of LED lighting fixtures and make the light softer, thereby eliminating glare and improving the comfort of indoor LED lighting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of porous cross-linked polystyrene light diffusion agent and PC light diffusion plate and preparation method thereof
  • A kind of porous cross-linked polystyrene light diffusion agent and PC light diffusion plate and preparation method thereof
  • A kind of porous cross-linked polystyrene light diffusion agent and PC light diffusion plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Co-porogen: a mixed solvent of toluene and low-density liquid paraffin, low-density liquid paraffin accounts for 0% of the total volume of the co-porogen, and the co-porogen accounts for 50% of the total volume of the mixed oil phase.

[0036] Emulsifier, co-emulsifier and deionized water (the mass fraction of emulsifier accounting for deionized water is 8%, and co-emulsifying agent accounts for 30% of the mass fraction of emulsifier) ​​is added in the reactor, under ice-bath condition, mechanical Stir for 20 minutes, add styrene, divinylbenzene, and initiator (wherein the volume fraction of styrene and divinylbenzene is 3:2, and the mass fraction of the initiator in the mixed oil phase is 4%) into the beaker and sonicate for 10 minutes, Until it dissolves, add the co-porogen into the monomer mixture and disperse ultrasonically for 10 minutes until it is uniform to obtain a mixed oil phase. Put the mixed oil phase in a constant pressure funnel, drop it into the reactor,...

Embodiment 2

[0038] Co-porogen: a mixed solvent of toluene and low-density liquid paraffin. The low-density liquid paraffin accounts for 50% of the total volume of the co-porogen, and the co-porogen accounts for 50% of the total volume of the mixed oil phase.

[0039] Emulsifier, co-emulsifier and deionized water (the mass fraction of emulsifier accounting for deionized water is 8%, and co-emulsifying agent accounts for 30% of the mass fraction of emulsifier) ​​is added in the reactor, under ice-bath condition, mechanical Stir for 20 minutes, add styrene, divinylbenzene, and initiator (wherein the volume fraction of styrene and divinylbenzene is 3:2, and the mass fraction of the initiator in the mixed oil phase is 4%) into the beaker and sonicate for 10 minutes, Until it dissolves, add the co-porogen into the monomer mixture and disperse ultrasonically for 10 minutes until it is uniform to obtain a mixed oil phase. Put the mixed oil phase in a constant pressure funnel, drop it into the rea...

Embodiment 3

[0041] Co-porogen: a mixed solvent of toluene and low-density liquid paraffin, low-density liquid paraffin accounts for 70% of the total volume of the co-porogen, and the co-porogen accounts for 50% of the total volume of the mixed oil phase.

[0042]Emulsifier, co-emulsifier and deionized water (the mass fraction of emulsifier accounting for deionized water is 8%, and co-emulsifying agent accounts for 30% of the mass fraction of emulsifier) ​​is added in the reactor, under ice-bath condition, mechanical Stir for 20 minutes, add styrene, divinylbenzene, and initiator (wherein the volume fraction of styrene and divinylbenzene is 3:2, and the mass fraction of the initiator in the mixed oil phase is 4%) into the beaker and sonicate for 10 minutes, Until it dissolves, add the co-porogen into the monomer mixture and disperse ultrasonically for 10 minutes until it is uniform to obtain a mixed oil phase. Put the mixed oil phase in a constant pressure funnel, drop it into the reactor ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

A porous cross-linked polystyrene light diffusion agent, a PC light diffusion plate and a preparation method thereof belong to the technical field of polymer materials. The light diffusing agent is a random copolymer of styrene and divinylbenzene with micropores on the surface. The components and percentages of the PC light diffusing plate are: polycarbonate 95% to 99%, and the light diffusing agent 1% to 5%, the percentage content of the above components is 100%. The refractive index of porous cross-linked polystyrene microspheres is different from that of PC materials, and the existence of micropores on the surface of the microspheres. When the light passes through the material, the light will undergo multiple reflections and refractions, and finally the light passing through the light diffusion plate will be The point light source becomes a surface light source, making the light bright and soft. The PC light diffusion plate prepared by the present invention has excellent light transmittance and light diffusivity, and can be used in LED lighting fixtures, liquid crystal displays, advertising light boxes, etc., to achieve softer and more uniform irradiation effects.

Description

technical field [0001] The invention relates to a porous cross-linked polystyrene light diffusion agent, a PC light diffusion plate and a preparation method thereof, belonging to the technical field of polymer materials. Background technique [0002] As a new type of solid-state light source, LED has been widely used in various fields, realizing another technological revolution in the history of human lighting. However, in practical applications, there are still many imperfections in LEDs, for example, the characteristics of its point light source are easy to cause light pollution and low luminous efficiency. Light diffusing agent is a kind of material with special optical characteristics, which has excellent light diffusing effect and light transmission. It effectively solves the problems of glare and low light extraction efficiency of LED light sources. [0003] At present, the light scattering particles used in LED lighting mainly include CaCO 3 , SiO 2 Such as inorga...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F212/08C08F212/36C08J9/28C08L25/06F21V5/08F21Y115/10
CPCC08F212/08C08J9/28C08J2201/0502C08J2325/06F21V5/08F21Y2115/10C08F212/36
Inventor 王洪任飞飞密建国杜中杰张晨邹威
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com