Collector for rutile flotation and using method

A collector and rutile technology, applied in flotation, solid separation, etc., can solve the problems of poor selectivity and weak collection ability, and achieve the effects of easy realization, low price, strong collection ability and selectivity

Inactive Publication Date: 2019-01-25
KUNMING UNIV OF SCI & TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems of poor selectivity and weak collection ability of existing rutile collectors, the invention provides a combined collector for rutile flotation, which has better collection ability and selectivity for rutile, A good titanium recovery index can be obtained; the combined collector has the characteristics of strong collection capacity and good selectivity, and only a small amount of addition is needed to achieve the ideal separation effect during flotation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Example 1: The composition and mass percentage of the collector used in this example are: 80wt% salicylic hydroxamic acid, 10wt% linolenic acid, and 10wt% sodium dodecylsulfonate.

[0014] The processing object of this embodiment is: a certain weathered titanium ore raw ore TiO in Yunnan 2 The grade is 9.08%, and titanium mainly exists in the form of rutile; the specific beneficiation method is: the grinding fineness -0.074mm accounts for 40%, then sulfuric acid is used to adjust the pH of the pulp to 5, and then the gangue inhibitor sodium fluorosilicate is added 100g / t , then add collector 30g / t, terpineol oil 100 g / t, pulp concentration 10%, scrape the foam to get titanium concentrate, in which TiO 2 The grade is 36.45%, and the recovery rate is 89.12%.

Embodiment 2

[0016] Example 2: The composition and mass percentage of the collector used in this example are: 10wt% of salicylic hydroxamic acid, 80wt% of linolenic acid, and 10wt% of sodium dodecylsulfonate.

[0017] The processing object of this embodiment is: a certain titanium ore raw ore TiO in Sichuan 2 The grade is 6.42%, and titanium mainly exists in the form of rutile; the specific beneficiation method is: the grinding fineness -0.074mm accounts for 60%, and the inhibitor sodium fluorosilicate 1200g / t is added under the condition of natural pH=8, and then the collection Agent 150g / t, pine alcohol oil 45 g / t, pulp concentration 20%, scrape out the foam to obtain titanium concentrate, in which TiO 2 The grade is 36.45%, and the recovery rate is 89.12%.

[0018] Comparative example: using the collector oleic acid (addition amount: 150g / t) to replace the combined collector, and under the same flotation conditions, TiO in titanium concentrate was obtained 2 The grade is 30.50%, and t...

Embodiment 3

[0019] Example 3: The raw materials and their mass percentages in the combined medicament described in this example are: 40wt% salicylic hydroxamic acid, 20wt% linolenic acid, and 40wt% sodium dodecylsulfonate.

[0020] The processing object of this embodiment is: a titanium ore raw ore TiO in Hebei 2 Grade 10.61%, titanium mainly exists in the form of rutile. The specific beneficiation method is as follows: Grinding fineness -0.074mm accounts for 80%, then adjust the pulp pH=10 with sodium carbonate, then add inhibitor sodium fluorosilicate 2000g / t, then add collector 300g / t, terpineol oil 100 g / t, the pulp concentration is 45%, and the foam is scraped out to obtain titanium concentrate, in which TiO 2 The grade is 35.40%, and the recovery rate is 81.12%.

[0021] Comparative example: using benzyl arsenic acid (addition amount: 300g / t) to replace the combined collector, and under the same flotation conditions, TiO in titanium concentrate was obtained 2 The grade is 30.20%,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a collector for rutile flotation. A compound of salicylhydroxamic acid, linolenic acid and sodium dodecylsulphate is adopted as the collector. The collector comprises, by mass10-80% of the salicylhydroxamic acid, 10-80% of the linolenic acid and 10-40% of the sodium dodecylsulphate. According to a combined drug, the collecting capability and selectivity on rutile are improved through the synergistic action among drugs; compared with a single rutile collector, the rutile collector has the advantages of being less in drug consumption, less in price, soluble under room temperature, free of toxin, efficient and environmental friendly, and the rutile collector has significant meaning in improving the recycling of titanium resources.

Description

technical field [0001] The invention relates to a collector used for rutile flotation and a usage method, belonging to the field of mineral processing chemicals. Background technique [0002] Flotation is an effective method for sorting rutile; most foreign rutile resources are seaside placer, which has coarse particle size and high dissociation degree, and generally does not need grinding and flotation operations, so there are few researches on rutile flotation process abroad. China's rutile reserves are relatively insufficient, and there are relatively more rock-type resources and relatively less placer-type resources. In particular, coarse-grained rutile resources with a high recovery rate of ore dressing are scarcer, and domestic rutile ore rutiles are embedded with fine grain size and veins. The stone symbiosis is closely related, and it is difficult to reselect tailings and sorting. Therefore, the key factor in the development and utilization of rutile resources in my c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B03D1/01B03D1/008B03D1/012B03D1/02B03B1/00B03B1/04B03D101/02B03D103/02
CPCB03B1/00B03B1/04B03D1/008B03D1/01B03D1/012B03D1/025B03D2201/02B03D2203/04
Inventor 江旭罗斌刘全军
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com