A kind of preparation method of glass grinding disc

A grinding disc and glass technology, which is used in grinding/polishing equipment, grinding devices, manufacturing tools, etc., can solve the problems of high straightness error and uneven grinding texture, and achieve small elastic deformation and uniform grinding texture. The effect of fineness and meeting the processing requirements

Active Publication Date: 2020-10-16
湖南兴龙环境艺术工程股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention provides a method for preparing a glass grinding disc, which solves the technical problems of high straightness error and uneven grinding lines when the grinding disc prepared by the traditional preparation method grinds glass optical devices

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of glass grinding disc
  • A kind of preparation method of glass grinding disc
  • A kind of preparation method of glass grinding disc

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0020] The invention provides a kind of preparation method of glass grinding disc, and this preparation method comprises the following steps:

[0021] Step 1, slurry preparation: weigh a certain amount of CeCl with a concentration of 4-5mol / L 3 Solution, under the condition of stirring at 400 rev / min, adding concentration is 85% and with the CeCl 3 Phosphoric acid solution with a solution volume ratio of 1:10, stirred for 10-20 minutes to obtain a uniform CeC...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a glass grinding disc. The preparation method comprises the following steps of: 1, preparing slurry; 2, forming a blank body of the grinding disc; 3, sintering; 4, machining. The method has the advantages that: the slurry for forming the grinding disc is obtained by using a chemical copolymerization sedimentation method, the grinding disc has a uniform and fine structure, can achieve highly uniform distribution of CeO2 abrasive in the glass grinding disc, and a glass device grinded by the glass grinding disc has uniform and fine grinding grains on the surface, so that the phenomenon of coarse scratches does not exist; the bonding agent of the grinding disc for bonding the CeO2 abrasive is an AlPO4. nH2O inorganic cementing material, the elastic modulus of the bonding agent is larger than that of a resin material, the elastic deformation amount of the glass grinding disc is small in the process of grinding glass, the straightness error ofthe grinded glass device is less than 3 micrometers / 25 millimeters, the processing requirements of high-precision glass optical devices can be well met.

Description

【Technical field】 [0001] The invention relates to the technical field of abrasive tool preparation, in particular to a method for preparing a glass grinding disc that uses aluminum phosphate gelling material to bond cerium oxide abrasives. 【Background technique】 [0002] CeO 2 Grinding disc for grinding process. The processing method has the advantages of high grinding efficiency and good surface finish of the processed workpiece. At present, the preparation method of grinding discs for glass polishing is to use CeO as abrasive 2 After the powder is mixed with the resin, the resin solidifies under certain conditions to form a resin grinding disc with a certain shape and strength. Commonly used resins include phenolic resin, unsaturated polyester resin, polyamide resin and epoxy resin. According to the shape of the resin, CeO 2 The molding and curing process of the grinding disc is also different. When the resin is liquid, the grinding disc is prepared by pouring and cur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B24B1/00B24D18/00
CPCB24B1/00B24D18/0009
Inventor 伍治东
Owner 湖南兴龙环境艺术工程股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap