Anti-flaming phase change microcapsule and preparation method thereof

A phase-change microcapsule and flame-retardant technology, which is applied in the direction of microcapsule preparation, microsphere preparation, chemical instruments and methods, etc., can solve the problem of low mechanical strength of the polymer wall of phase-change microcapsules, phosphonate monomers, etc. The reaction process is difficult to control, and the phase change microcapsule wall cross-linking density is low, so as to make up for the effects of flammability, easy industrial production, and high packaging efficiency.

Inactive Publication Date: 2019-01-18
SICHUAN UNIV
View PDF10 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Chinese patent CN 105542721A discloses a method for preparing flame-retardant phase-change microcapsules. The flame-retardant phase-change microcapsules are prepared by mixing flame retardant chlorinated paraffin into organic phase-change materials, but the flame-retardant and organic phase-change materials Physical blending reduces the content of phase-change substances in the microcapsules, thereby reducing the energy storage density of the phase-change microcapsules
[0006] Chinese patent CN 105112020A discloses another method for preparing flame-retardant phase-change microcapsules. A polymer capsule wall with certain flame-retardant properties is obtained by co-polymerizing reactive phosphonate monomers and acrylic acid monomers. However, phosphonate The monomer reaction process is difficult to control, and the polymer wall of phase change microcapsules has low mechanical strength
[0007] Chinese patent CN 103740337A prepares a phosphonate functional monomer, and prepares another flame-retardant microcapsule material by radical polymerization with acrylic acid monomer, but the preparation process of the microcapsule is cumbersome and the free radical polymerization The process is difficult to control, and the prepared phase change microcapsules have low cross-linking density

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-flaming phase change microcapsule and preparation method thereof
  • Anti-flaming phase change microcapsule and preparation method thereof
  • Anti-flaming phase change microcapsule and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A preparation method of flame-retardant phase-change microcapsules, comprising the steps of:

[0040] S1. Mix 5mol 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide and 1mol 4,4'-diaminobenzophenone evenly and add them to the round bottom flask, heat up to Stir at 170°C for 5 hours;

[0041] S2. Cool down to 100°C, add 4kg of toluene to the round bottom flask and stir evenly, filter the reaction solution to obtain a filter cake and wash it with toluene;

[0042] S3. Dissolving the filter cake prepared in S2 in tetrahydrofuran and recrystallizing at -20°C, after filtering, drying the filter cake in a vacuum oven to obtain a phosphorus-containing diamine monomer;

[0043] S4. Mix 0.3kg of phosphorus-containing diamine monomer prepared in S3 with 1kg of melamine, 1.7kg of formaldehyde solution, and 3kg of deionized water, and adjust the pH value to 8.5 with triethanolamine, and stir and react at 70°C for 2h to obtain the prepared Polymer solution; wherein, in terms of w...

Embodiment 2

[0057] A preparation method of flame-retardant phase-change microcapsules, comprising the steps of:

[0058] S1. Mix 2mol 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide and 1mol 4,4'-diaminobenzophenone evenly and add to the round bottom flask, heat up to Stir at 150°C for 12 hours;

[0059] S2. Cool down to 80°C, add 1.3kg of toluene into the round bottom flask and stir evenly, filter the reaction solution to obtain a filter cake and wash it with toluene;

[0060] S3. Dissolving the filter cake prepared in S2 in tetrahydrofuran and recrystallizing at -20°C, after filtering, drying the filter cake in a vacuum oven to obtain a phosphorus-containing diamine monomer;

[0061] S4. Mix 0.1 kg of phosphorus-containing diamine monomer prepared in S3 with 1 kg of melamine, 1.5 kg of formaldehyde solution, and 1.5 kg of deionized water, adjust the pH value to 8.0 with triethanolamine, and stir and react at 60° C. for 4 hours to obtain Prepolymer solution; wherein, in terms of wei...

Embodiment 3

[0066] A preparation method of flame-retardant phase-change microcapsules, comprising the steps of:

[0067] S1. Mix 10mol 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide and 1mol 4,4'-diaminobenzophenone evenly and add them to the round bottom flask, heat up to Stir at 180°C for 1 hour;

[0068] S2. Cool down to 120°C, add 11.5kg of toluene to the round bottom flask and stir evenly, filter the reaction solution to obtain a filter cake and wash it with toluene;

[0069] S3. Dissolving the filter cake prepared in S2 in tetrahydrofuran and recrystallizing at -20°C, after filtering, drying the filter cake in a vacuum oven to obtain a phosphorus-containing diamine monomer;

[0070] S4. Mix 0.8 kg of phosphorus-containing diamine monomer prepared in S3 with 1 kg of melamine, 1.8 kg of formaldehyde solution, and 5 kg of deionized water, and adjust the pH value to 9.0 with triethanolamine, and stir and react at 80° C. for 1 hour to obtain the prepared Polymer solution; wherein, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-flaming phase change microcapsule and a preparation method thereof and relates to the technical field of energy-saving materials. The anti-flaming phase change microcapsule comprises an organic phase change material and a capsule wall for wrapping the organic phase change material; the organic phase change material is one or more of straight-chain paraffin or branched paraffin with general formula of CnH2n+2, higher aliphatic acid with general formula of CnH2nCOOH and higher aliphatic alcohol with general formula of CnH2nOH; n=12-32; the capsule wall is made from phosphorous diamine monomer, melamine, formaldehyde solution, emulgator and deionized water. Phosphorous melamine-formaldehyde resin is taken as a capsule wall material of the anti-flaming phase change microcapsule disclosed by the invention, so that the flame resistance of the phase change microcapsule is greatly promoted, the defect of flammability of the organic phase change material is overcome, the direct mixing of fire retardant and organic phase change material can be avoided and higher energy density of the phase change microcapsule can be guaranteed.

Description

technical field [0001] The invention relates to the technical field of energy-saving materials, in particular to a flame-retardant phase-change microcapsule and a preparation method thereof. Background technique [0002] Energy is the basis for the survival and development of human society. With the increasing energy demand of human society and the increasing shortage of traditional energy, how to develop new energy and improve energy utilization has become an urgent task for scientists at home and abroad. Phase change materials (PCMs) are a class of functional materials that use the phase change process to absorb and release heat, and realize energy storage and temperature regulation during the phase change process. Phase-change energy storage materials can store unnecessary heat and release it when needed, thereby improving energy utilization. Therefore, phase-change energy storage materials are widely used in energy-saving buildings, solar energy storage, textile chemical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J13/18C09K5/06
CPCB01J13/18C09K5/06
Inventor 杜晓声杜宗良成煦王海波王双
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com