Non-toxic antiseptic and mildewproof water-based coating and preparation and application method thereof

A water-based coating, anti-corrosion and mildew-proof technology, applied in the preparation of non-toxic anti-corrosion and anti-mildew water-based coatings, the application of non-toxic anti-corrosion and anti-mildew water-based coatings, in the field of non-toxic anti-corrosion and anti-mildew water-based coatings, it can solve the problems affecting the health of users. It is easy to produce a large amount of harmful substances, complex formulations of water-based coatings and other problems, to achieve the effects of reducing viscosity, adjusting volatilization speed, and reducing production costs

Inactive Publication Date: 2018-12-28
清远市承明新材料科技有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Existing water-based coatings have complex formulas and unscrupulous production processes, which are prone to produce a large amount of harmful substances and affect the health of users. At the same time, the product has poor anti-corrosion performance, which greatly shortens the service life of the product and cannot prevent mildew. Significantly reduced fields of application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-toxic antiseptic and mildewproof water-based coating and preparation and application method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The invention provides a technical solution: a non-toxic, anti-corrosion and mildew-proof water-based coating, comprising the following components by weight: 100-130 parts of water-based resin, 2 parts of anti-mold agent, 5-10 parts of preservative, and 2 parts of silicone leveling agent 2-8 parts of surfactant, 30-40 parts of water, 20-30 parts of pigment.

[0026] The pigments include the following components by weight: 20-30 parts of lead chrome yellow, 10-15 parts of iron yellow, 18-25 parts of lead silicochromate, 10-15 parts of strontium calcium yellow, 8-10 parts of transparent yellow, 2 parts of benzidine yellow -10 parts, Hansa yellow 1-8 parts, lemon yellow 5-7 parts.

[0027] A preparation method of a non-toxic, anti-corrosion and mildew-proof water-based paint, comprising the following steps:

[0028] S1: Weigh the ratio, weigh all the required raw materials, and store them for use. The ratio is as follows: 100-130 parts of water-based resin, 2 parts of ant...

Embodiment 2

[0034] The invention provides a technical solution: a non-toxic, anti-corrosion and mildew-proof water-based coating, comprising the following components by weight: 100-130 parts of water-based resin, 2 parts of anti-mold agent, 5-10 parts of preservative, and 2 parts of silicone leveling agent 2-8 parts of surfactant, 30-40 parts of water, 20-30 parts of pigment.

[0035] The pigments include the following components by weight: 20-30 parts of lead chrome yellow, 10-15 parts of iron yellow, 18-25 parts of lead silicochromate, 10-15 parts of strontium calcium yellow, 8-10 parts of transparent yellow, 2 parts of benzidine yellow -10 parts, Hansa yellow 1-8 parts, lemon yellow 5-7 parts.

[0036] A preparation method of a non-toxic, anti-corrosion and mildew-proof water-based paint, comprising the following steps:

[0037] S1: Weigh the ratio, weigh all the required raw materials, and store them for use. The ratio is as follows: 100-130 parts of water-based resin, 2 parts of ant...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a non-toxic antiseptic and mildewproof water-based coating and a preparation and application method thereof. The non-toxic antiseptic and mildewproof water-based coating includes, by weight parts, 100-130 parts of water-based resin, 2 parts of anti-mold agent, 5-10 parts of preservative, 2 parts of organosilicone flatting agent, 2-8 parts of surfactant, 30-40 parts of waterand 20-30 parts of pigment, wherein the pigment comprises, by weight parts, 20-30 parts of lead chrome yellow, 10-15 parts of iron yellow, 18-25 parts of lead silicate chromate, 10-15 parts of (strontium-calcium) chrome yellow, 8-10 parts of transparent yellow, 2-10 parts of benzidine yellow, 1-8 parts of Hansha yellow and 5-7 parts of lemon yellow. The preparation method includes step S1 of weighing the raw materials in proportion, step S2 of obtaining a first mixture by mixing, step S3 of obtaining a second mixture by mixing, and step S4 of adding a surfactant at a ratio to obtain a finished product. The non-toxic antiseptic and mildewproof water-based coating is applied to architectural interior wall decorative coatings and exterior wall waterproof coatings. Application fields are widewhile a production process is simple, the production cost is greatly reduced, no toxic substance is generated in the product production and using process, and the non-toxic antiseptic and mildewproofwater-based coating can also play the role of anticorrosion and mildew prevention.

Description

technical field [0001] The invention relates to the field of water-based coatings, in particular to a non-toxic, anti-corrosion and mildew-proof water-based coating. [0002] The invention relates to the field of water-based paint, in particular to a preparation method of a non-toxic, anti-corrosion and mildew-proof water-based paint. [0003] The invention relates to the field of water-based paint, in particular to an application method of a non-toxic, anti-corrosion and mildew-proof water-based paint. Background technique [0004] Water-based coatings usually refer to coatings that use water as a solvent or as a dispersion medium. Water-based coatings have emerged in recent years, and their environmental protection is much higher than that of paint. [0005] In the Chinese invention patent application publication specification CN107353733A, a non-toxic and environmentally friendly water-based paint and its preparation method are disclosed, including the following componen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D175/04C09D167/08C09D5/14C09D5/08C09D7/61C09D7/41C09D7/65
CPCC09D133/00C09D5/08C09D5/14C09D7/41C09D7/61C09D7/65C09D167/08C09D175/04C08L83/04C08K13/02C08K5/18C08K3/16
Inventor 吕松春
Owner 清远市承明新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap