Novel UV-LED ultraviolet crosslinked polyethylene cable material and preparation method thereof

Inactive Publication Date: 2018-12-25
合肥光冉高分子材料科技有限公司
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, the embodiment of the present invention provides a new type of UV-LED ultraviolet crosslinked polyethylene cable material and its preparation method, the main purpose of which is to solve the problem of low crosslinking efficiency of ultraviolet crosslinked polyethylene under UV-LED irradiation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel UV-LED ultraviolet crosslinked polyethylene cable material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Each raw material is prepared according to the following formula: 100 parts of linear low density polyethylene (7042), 1.8 parts of TPO, 1.2 parts of TAC, 1.3 parts of epoxybutane, 0.2 part of antioxidant 1010 and 0.1 part of DLTP; Stir in the feeder at a speed of 250rpm for 5 minutes to obtain the mixture; preheat the extruder to 170°C, put in the above mixture, make the mixture fully plasticized, extrude and enter the water tank to cool, and then enter the UV-LED ultraviolet light Irradiation is carried out in the irradiation cross-linking equipment, and the irradiation time is 3s to obtain ultraviolet light irradiation cross-linked polyethylene wires and cables.

Embodiment 2

[0023] Prepare raw materials according to the following formula: 80 parts of high-density polyethylene (5000s), 20 parts of linear low-density polyethylene (7042), 1.2 parts of ITX, 1.2 parts of TMPTA, 1.0 parts of epoxybutane, 0.3 parts of antioxidant 1010 and 0.1 part of DLTP; the above raw materials were stirred in a mixer at a speed of 250rpm for 5 minutes to obtain a mixture; the extruder was preheated to 165°C, and the above mixture was put in to make the mixture fully plasticized, extruded and entered The water tank is cooled, and then enters the UV-LED ultraviolet light irradiation crosslinking equipment for irradiation, and the irradiation time is 3s to obtain ultraviolet light irradiation crosslinked polyethylene wires and cables.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel UV-LED ultraviolet crosslinked polyethylene cable material and a preparation method thereof and relates to the technical field of chemical materials. Crosslinked polyethylene for ultraviolet radiation comprises, by weight, 100 parts of polyethylene, 0.1-0.3 part of free radical photoinitiator, 0.1-3.0 parts of polyfunctional group crosslinking agent, 0.1-3.0 parts of initiation adjuvant and 0.1-2.0 parts of composite antioxidant. Crosslinked polyethylene is quite suitable for ultraviolet radiation and forming ultraviolet crosslinked polyethylene, crosslinking degree of crosslinked polyethylene is increased, crosslinking time is shortened, and production efficiency is improved.

Description

technical field [0001] The invention relates to the technical field of chemical materials, in particular to a novel UV-LED ultraviolet light cross-linked polyethylene cable material and a preparation method thereof. Background technique [0002] Polyethylene has excellent electrical insulation, chemical resistance and good processing performance, so it is widely used in various fields of national production. However, in some special occasions, polyethylene cannot fully meet people's requirements for material properties, such as heat resistance and so on. Therefore, it is necessary to carry out a series of modifications to polyethylene materials, and the most effective way is to crosslink polyethylene. After polyethylene is cross-linked, its molecular structure becomes linear into a three-dimensional network structure, and its mechanical strength, heat resistance, environmental resistance and chemical resistance have been improved to varying degrees, expanding the scope of p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08K13/02C08J7/18H01B3/44C08F255/02C08F226/06C08F2/46
CPCC08F2/46C08F255/02C08J7/18C08L23/06C08L2203/202C08L2207/062C08L2312/06H01B3/441C08L23/0815C08F226/06
Inventor 叶磊叶繁吴强华
Owner 合肥光冉高分子材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com