2.7-3 micrometer band intermediate infrared Yb-Er-Dy tri-doped lead fluoride laser crystal and preparation method thereof

A laser crystal, lead fluoride technology, applied in chemical instruments and methods, lasers, crystal growth and other directions to achieve the effect of improving pump absorption efficiency

Active Publication Date: 2018-12-18
JINAN UNIVERSITY
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no mid-infrared ytterbium, erbium, dysprosium, and three-doped PbF in the 2.7-3 micron band at home and abroad. 2 Related reports on laser crystals

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 2.7-3 micrometer band intermediate infrared Yb-Er-Dy tri-doped lead fluoride laser crystal and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Growth of PbF by the Bridgeman method 2 Crystal, raw material is PbF 2 (99.99%), YbF 3 (99.99%), ErF 3 (99.99%) and DyF 3 (99.99%), where Yb 3+ The doping concentration is 1at.%, Er 3+ The doping concentration is 1at.%, Dy 3+ The doping concentration is 0.5 at.%. Before crystal growth, the raw materials are homogenized in a platinum crucible at a high temperature of 950-1050°C for 8 hours, and kept warm for 4-6 hours to fully melt the raw materials; during the crystal growth period, the crucible is lowered at a rate of 1-2mm / h to enter the crystal growth After the crystal growth is completed, in order to prevent the crystal from cracking, the temperature is slowly lowered to room temperature at a rate of 20-40°C / h during the cooling process. The entire crystal growth process is carried out in a closed state, and the grown PbF 2 The crystal is transparent and has good optical properties. Under 970nm LD excitation, the mid-infrared fluorescence emission spectrum ...

Embodiment 2

[0023] Select the raw material PbF that purity is greater than 99.99% in the present embodiment 2 , YbF 3 , ErF 3 and DyF 3 , using the Bridgeman method for crystal growth, successfully grown ytterbium erbium dysprosium three-doped PbF 2 Mid-infrared laser crystal, where Yb 3+ The doping concentration of ions is 5at.%, Er 3+ The doping concentration is 10at.%, Dy 3+ The doping concentration is 3at.%. Before crystal growth, the raw material is homogenized in a platinum crucible at a high temperature of 1000-1100°C for 10 hours, and kept warm for 3-5 hours to fully melt the raw material; during the crystal growth period, the crucible is lowered into the crystal at a rate of 1.5-2.5mm / h Crystals are carried out in the growth area; after the crystal growth is completed, during the cooling process, in order to prevent the crystal from cracking, the temperature is slowly lowered to room temperature at a cooling rate of 40-60 °C / h. The entire crystal growth process is carried ...

Embodiment 3

[0025] Select the raw material PbF that purity is greater than 99.99% in the present embodiment 2 , YbF 3 , ErF 3 and DyF 3 , using the Bridgeman method for crystal growth, successfully grown ytterbium erbium dysprosium three-doped PbF 2 Mid-infrared laser crystal, where Yb 3+ The doping concentration of ions is 10at.%, Er 3+ The doping concentration is 15at.%, Dy 3+ The doping concentration is 5 at.%. Before crystal growth, the raw materials are homogenized in a platinum crucible at a high temperature of 1050-1150°C for 8 hours, and kept warm for 3-5 hours to fully melt the raw materials; during the crystal growth period, the crucible is lowered at a rate of 1.5-3mm / h to enter the crystal growth After the crystal growth is completed, in order to prevent the crystal from cracking, the temperature is slowly lowered to room temperature at a cooling rate of 60-80°C / h. The entire crystal growth process is carried out in a closed state, and the grown PbF 2 The crystal is tr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a 2.7-3 micrometer band intermediate infrared Yb-Er-Dy tri-doped lead fluoride laser crystal and a preparation method thereof. Specifically, Er<3+> ions act as activation ions,and Dy<3+> ions have the dual functions that: (1) as the energy level coupling ions of Er<3+> ions, Dy<3+> ions can reduce the <4>I13 / 2 energy level lifetime of Er<3+> ions; and (2) a small energy band gap exists between the <6>H11 / 2 energy level of Dy<3+> ions and the <4>I13 / 2 energy level of Er<3+> ions, energy transfer from the <4>I13 / 2 energy level of Er<3+> ions to the <6>H11 / 2 energy levelof Dy<3+> ions can be realized, and the energy level transition of Dy<3+> ions from <6>H13 / 2 to <6>H15 / 2 is facilitated, therefore 2.9 micrometer band fluorescence can be emitted. At the same time, Yb<3+> ions are introduced to solve the problem of low absorption efficiency of Er<3+> ions and Dy<3+> ions at the 970nm position and improve the crystal absorption efficiency.

Description

technical field [0001] The invention relates to the technical field of mid-infrared laser materials, in particular to a mid-infrared ytterbium-erbium-dysprosium tri-doped lead fluoride (PbF2) laser crystal in the 2.7-3 micron band and a preparation method thereof. Background technique [0002] Mid-infrared lasers are widely used in atmospheric monitoring, medical surgery and scientific research, and can also be used in high-quality pump sources for long-wavelength pulsed lasers and optical parametric oscillators. Among many luminescent ions, Er 3+ Ion and Dy 3+ The ions are effective ions to realize the 2.7-3 micron ultra-wideband laser output. Er 3+ Ionic 4 I 11 / 2 → 4 I 13 / 2 Energy level transition and Dy 3+ Ionic 6 h 13 / 2 → 6 h 15 / 2 Energy level transitions can produce fluorescence in the 2.7-3μm band, but Er 3+ ion upper level 4 I 11 / 2 The fluorescence lifetime is much lower than the lower level 4 I 13 / 2 The fluorescence lifetime is difficult to form popu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C30B29/12C30B11/00H01S3/16
CPCC30B11/00C30B29/12H01S3/1606H01S3/1608H01S3/1618H01S3/1645
Inventor 张沛雄汪瑞陈振强朱思祁尹浩李真
Owner JINAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com