A high baking hardenability aluminum alloy plate and its preparation method

An aluminum alloy sheet, bake hardening technology, applied in the field of aluminum alloy sheet manufacturing, can solve the problems of poor adhesion and corrosion resistance of automobile body panels, achieve excellent paint bake hardenability, prevent surface roughness, and increase strength Effect

Active Publication Date: 2020-07-17
YINGKOU ZHONGWANG ALUMINUM CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, the present invention solves the problem that MgO is easily formed on the surface of the aluminum alloy plate used in the automobile body covering in the prior art, making the adhesion of the automobile body covering and the corrosion resistance after painting poor. , providing a high bake-hardenable aluminum alloy plate and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high baking hardenability aluminum alloy plate and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method of an aluminum alloy sheet with high bake hardenability, comprising the following steps:

[0031] A. Calculate the amount of each aluminum alloy raw material and prepare the aluminum alloy raw material according to the ratio. The mass percentage ratio of each element of the aluminum alloy sheet raw material is as follows:

[0032] element Mg Si Ti B Fe Zn Cu Sn Mn Cr Al content 0.40 0.60 0.008 0.0005 0.30 0.06 0.30 0.03 0.01 0.1 margin

[0033] The prepared aluminum alloy raw materials are added to the melting furnace and evenly mixed and then smelted into liquid aluminum alloy, and the liquid aluminum alloy is smelted into aluminum alloy ingots. The aluminum alloy melting process is melting, stirring, slag removal, degassing and impurity removal, and filtering , the semi-continuous casting method of casting;

[0034] B. Carry out homogenization annealing to the aluminum alloy ingot fused and cast in...

Embodiment 2

[0042] The difference between embodiment 2 and embodiment 1 is that in step A, the mass percentage ratio of each element of the raw material of the aluminum alloy sheet is as follows:

[0043] element Mg Si Ti B Fe Zn Cu Sn Mn Cr Al content 0.70 0.80 0.10 0.01 0.04 1.0 0.50 0.20 0.1 0.1 margin

Embodiment 3

[0045] The difference between Example 3 and Example 2 is that in step B, the homogenization annealing temperature is 600° C., and the holding time is 4 h.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of manufacturing of aluminum alloy plates, and relates to an aluminum alloy plate with high bake hardenability and a preparation method thereof. The aluminum alloy plate with the high bake hardenability is prepared from, by weight, 0.4-0.9% of Mg, 0.6-1.4% of Si, 0.008-0.12% of Ti, 0.0005-0.04% of B, no more than 0.3% of Fe, 0.06-1.5% of Zn, 0.3-0.8% of Cu, 0.03-0.25% of Sn, no more than 0.15% of impurities and the balance Al, wherein the content of each the impurity is no more than 0.05%. By adoption of the aluminum alloy plate with the high bake hardenability and the preparation method thereof, the problem that MgO is likely to be formed on the surface of an aluminum alloy plate adopted by an automobile body covering part in the prior art, and consequentially, the binding property and corrosion resistance after painting of the automobile body covering part are poor is solved.

Description

technical field [0001] The invention belongs to the field of aluminum alloy plate manufacturing, and relates to an aluminum alloy plate with high bake hardenability and a preparation method thereof. Background technique [0002] Faced with the pressure to save energy and reduce environmental pollution, major automakers are increasingly focusing on lightweighting of automotive materials. Aluminum alloys have become the first choice for lightweight automobiles due to their low density, high specific strength, and excellent corrosion resistance, formability and impact energy absorption. Therefore, the application of aluminum alloy sheets in automotive hoods, trunk lids, doors and other coverings is becoming more and more common. [0003] At present, automotive aluminum sheets mainly include 5000 series and 6000 series. 5000 series aluminum alloys are non-heat treatable reinforced aluminum alloys, and their cost is lower than that of 6000 series aluminum alloys. However, becau...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/02C22C21/08C22C21/10C22C21/18C22F1/043C22F1/047C22F1/053C22F1/057C22F1/05
CPCC22C21/02C22C21/08C22C21/10C22C21/14C22C21/16C22C21/18C22F1/043C22F1/047C22F1/05C22F1/053C22F1/057
Inventor 迟壮田洪超李健刘贵军吕洪伟王志会
Owner YINGKOU ZHONGWANG ALUMINUM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com