Anti-cracking and anti-aging connecting plate rubber material for transmission shaft of automobile
A connecting plate and transmission shaft technology, applied in the field of special processing and manufacturing of new automotive materials, can solve the problems of high pollution, harsh working environment, high energy consumption, etc., and achieve the effects of small agglomeration, good divergence effect, and reduced polarity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] An anti-cracking and anti-aging connecting disc rubber material for automobile transmission shafts,
[0023](1) Configure zinc oxide, anti-aging agent RD, anti-scorch agent CTP, stearic acid, anti-aging agent 4010NA, mobile dispersant RL-12, protective wax RW287, insoluble sulfur IS-60, accelerator TMTD, accelerator D, The auxiliary agent mixture composed of plasticizer glycerol was stirred at 800r / min for 8h, then the mixture of modified reed fiber particles and carbon black was added, and the stirring was continued for 1h;
[0024] (2) Mix natural rubber latex, polyvinyl chloride and styrene-butadiene latex, mix well at a stirring speed of 300r / min, keep stirring, slowly add the aforementioned auxiliary agent mixture into the latex, and disperse evenly.
[0025] The basic rubber material is made of the following weight (Kg) raw materials: natural rubber latex 100, styrene-butadiene latex 10, polyvinyl chloride 5, N550 carbon black 50, N744 carbon black 10, indirect zi...
Embodiment 2
[0029] An anti-cracking and anti-aging connecting disc rubber material for automobile transmission shafts,
[0030] (1) Configure zinc oxide, anti-aging agent RD, anti-scorch agent CTP, stearic acid, anti-aging agent 4010NA, mobile dispersant RL-12, protective wax RW287, insoluble sulfur IS-60, accelerator TMTD, accelerator D, The additive mixture composed of plasticizer glycerol was stirred at 900r / min for 7h, then the mixture of modified reed fiber particles and carbon black was added, and the stirring was continued for 1.5h;
[0031] (2) Mix natural rubber latex, polyvinyl chloride and styrene-butadiene latex, mix well at a stirring speed of 350r / min, keep stirring, slowly add the aforementioned auxiliary agent mixture into the latex, and disperse evenly.
[0032] The basic rubber material is made of the following weight (Kg) raw materials: natural rubber latex 110, styrene-butadiene latex 12.5, polyvinyl chloride 7.5, N550 carbon black 55, N744 carbon black 12, indirect me...
Embodiment 3
[0036] An anti-cracking and anti-aging connecting disc rubber material for automobile transmission shafts,
[0037] (1) Configure zinc oxide, anti-aging agent RD, anti-scorch agent CTP, stearic acid, anti-aging agent 4010NA, mobile dispersant RL-12, protective wax RW287, insoluble sulfur IS-60, accelerator TMTD, accelerator D, The auxiliary agent mixture composed of plasticizer glycerol was stirred at 1000r / min for 8h, then the mixture of modified reed fiber particles and carbon black was added, and the stirring was continued for 2h;
[0038] (2) Mix natural rubber latex, polyvinyl chloride and styrene-butadiene latex, mix well at a stirring speed of 400r / min, keep stirring, slowly add the aforementioned auxiliary agent mixture into the latex, and disperse evenly.
[0039] The basic rubber material is made of the following weight (Kg) raw materials: natural rubber latex 120, styrene-butadiene latex 15, polyvinyl chloride 10, N550 carbon black 60, N744 carbon black 15, indirect...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com