A kind of glass mosaic and its preparation method and decoration material

A technology of glass mosaic and mosaic, applied in covering/lining, building, building structure, etc., can solve the problems of affecting the appearance of glass mosaic, changing the performance of glass mosaic, poor adhesion of electroplating layer, etc., achieving excellent visual effect and reliable Strong implementability and effect of improving adhesion

Active Publication Date: 2020-12-25
FOSHAN PAMASE BUILDING MATERIAL CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, grinding the bottom of the fired glass mosaic will change the performance of the glass mosaic, and the adhesion of the electroplating layer is poor, and it is easy to fade, which affects the appearance of the glass mosaic and reduces the product yield.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of glass mosaic and its preparation method and decoration material
  • A kind of glass mosaic and its preparation method and decoration material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] The invention provides a method for preparing a glass mosaic, comprising:

[0040] S101, pretreating the original glass to obtain a mosaic primary product;

[0041] Described pretreatment comprises:

[0042] Cut the original glass into the desired shape and size to obtain glass pieces;

[0043] modulation glaze;

[0044] Print the prepared glaze on the surface of the glass sheet and dry it to complete the printing process;

[0045] The printed glass sheet is opened and classified to obtain the initial mosaic product.

[0046] It should be noted that the glaze should be modulated according to the color and style of the finished product, and the modulation method can be according to the existing technology.

[0047] S102, firing the primary glass mosaic product at a firing temperature > 800°C;

[0048] Specifically, the primary glass mosaic is cleaned on a high-temperature backing plate, and then fired in a kiln. The firing temperature is preferably 800-850° C., and ...

Embodiment 1

[0089] (1) Prepare glass mosaics, including:

[0090] 1. Cut the original glass into the desired shape and size to obtain glass pieces;

[0091] 2. Prepare the glaze;

[0092] 3. Print the prepared glaze on the surface of the glass sheet and dry it to complete the printing process;

[0093] 4. Sorting the printed glass sheet to obtain the primary mosaic product;

[0094] 5. The primary glass mosaic is fired, the firing temperature is 850°C, and the firing time is 40 minutes;

[0095] 6. Cool the fired glass mosaic primary product;

[0096] 7. Grind the bottom of the cooled glass mosaic product according to the required shape;

[0097] 8. Soak the finished glass mosaic finished in a sodium hydroxide solution at a temperature of 26°C for 300 minutes;

[0098] 9. Clean the initial mosaic product after soaking in the alkaline solution with clean water;

[0099] 10. Electroplating the cleaned glass mosaic primary product, and coloring the bottom surface of the product;

[01...

Embodiment 2

[0102] 1. Cut the original glass into the desired shape and size to obtain glass pieces;

[0103] 2. Prepare the glaze;

[0104] 3. Print the prepared glaze on the surface of the glass sheet and dry it to complete the printing process;

[0105] 4. Sorting the printed glass sheet to obtain the primary mosaic product;

[0106] 5. The primary glass mosaic is fired, the firing temperature is 830°C, and the firing time is 42 minutes;

[0107] 6. Cool the fired glass mosaic primary product;

[0108] 7. Grind the bottom of the cooled glass mosaic product according to the required shape;

[0109] 8. Soak the ground-finished glass mosaic in a solution of sodium hydroxide and sodium carbonate at a temperature of 40°C for 60 minutes;

[0110] 9. Clean the initial mosaic product after soaking in the alkaline solution with clean water;

[0111] 10. Electroplating the cleaned glass mosaic primary product, and coloring the bottom surface of the product;

[0112] 11. Paint the back cove...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses glass mosaic, a preparation method thereof, and a decoration material. The preparation method of the glass mosaic comprises the steps that (1) an original glass sheet is preprocessed, and a primary finished mosaic product is obtained; (2) the primary finished glass mosaic product is sintered, and the sintering temperature is larger than 800 DEG C; (3) the sintered primary finished glass mosaic product is cooled; (4) the cooled primary finished glass mosaic product is subjected to bottom grinding processing according to the needed shape; (5) the primary finished glass mosaic product subjected to bottom grinding is soaked by an alkaline solution; (6) the soaked primary finished glass mosaic product is electroplated, and the bottom-ground face of the product is colored; and (7) the colored primary finished glass mosaic product is subjected to oil paint bottom sealing. Correspondingly, the invention further discloses the glass mosaic prepared through the method andthe decoration material comprising the glass mosaic. The glass mosaic shows the stereoscopic impression, the metallic impression and highlight and is rich in color, not prone to fading, and extremelygood in visual effect.

Description

technical field [0001] The invention relates to a building material decoration material, in particular to a glass mosaic, a method for preparing the glass mosaic, and a decoration material using the glass mosaic. Background technique [0002] Glass mosaic is also called glass mosaic tile or cellophane tile. It is a small format colored veneer glass. Made of natural minerals and glass powder, glass mosaic is the safest building material and an outstanding environmental protection material. It is resistant to acid and alkali, corrosion, and does not fade. It is the most suitable building material for decorating the walls and floors of bathroom rooms. The appearance of glass mosaics is generally colorless and transparent, colored and transparent, and translucent. In order to enrich the color of the glass mosaic and increase the diversity of the glass mosaic, the existing technology is to ground the fired glass mosaic, and then perform electroplating on the ground side to for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04F13/14
CPCE04F13/145
Inventor 梁天
Owner FOSHAN PAMASE BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com