Preparation method of surface modified titanium dioxide nano-particle polyimide fiber membrane

A polyimide fiber, titanium dioxide technology, applied in fiber processing, fiber type, textile and papermaking, etc., can solve the problems of limited improvement of wettability, damage of matrix fibers, etc., to achieve controllable thickness, high temperature resistant surface wettability , the effect of low cost

Active Publication Date: 2018-11-06
启鼎技术(北京)有限公司
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the biggest problem with this method is that most of the inorganic nanoparticles exist inside the matrix fiber, which not only has limited improvement in wettability, but also has a great destructive effect on the matrix fiber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of surface modified titanium dioxide nano-particle polyimide fiber membrane
  • Preparation method of surface modified titanium dioxide nano-particle polyimide fiber membrane
  • Preparation method of surface modified titanium dioxide nano-particle polyimide fiber membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034]The PMDA / ODA system polyamic acid fiber membrane is prepared, and after treatment and thermal imidization, a polyimide fiber membrane with a surface-modified titanium dioxide nanometer layer is obtained. (1) Weigh 2.0g of pyromellitic dianhydride (PMDA) and 1.8g of 4,4'-diaminodiphenyl ether (ODA) with a molar ratio of 1:1, and dissolve all ODA in 30ml of N,N - in dimethylformamide (DMF) solvent, mechanically stirred, after ODA is all dissolved in DMF, under the condition of ice-water bath, add PMDA step by step, after obtaining the polyamic acid solution with moderate viscosity, after mechanically stirring for 2h, put The polyamic acid solution is put into a 20ml syringe, and the polyamic acid fiber film is prepared by electrospinning technology. The specific parameters of the electrospinning machine are spinning voltage: 20kV; spinning temperature: room temperature; spinning humidity: 20%; Syringe needle diameter: No. 12; Receiving roller speed: 80.0m / min; Receiving di...

Embodiment 2

[0036] The PMDA / ODA system polyamic acid fiber membrane is prepared, and after treatment and thermal imidization, a polyimide fiber membrane with a surface-modified titanium dioxide nanometer layer is obtained. (1) Weigh 2.0g of pyromellitic dianhydride (PMDA) and 1.8g of 4,4'-diaminodiphenyl ether (ODA) with a molar ratio of 1:1, and dissolve all ODA in 30ml of N,N - in dimethylformamide (DMF) solvent, mechanically stirred, after ODA is all dissolved in DMF, under the condition of ice-water bath, add PMDA step by step, after obtaining the polyamic acid solution with moderate viscosity, after mechanically stirring for 2h, put The polyamic acid solution is put into a 20ml syringe, and the polyamic acid fiber film is prepared by electrospinning technology. The specific parameters of the electrospinning machine are spinning voltage: 20kV; spinning temperature: room temperature; spinning humidity: 20%; Syringe needle diameter: No. 12; Receiving roller speed: 80.0m / min; Receiving d...

Embodiment 3

[0038] The PMDA / ODA system polyamic acid fiber membrane is prepared, and after treatment and thermal imidization, a polyimide fiber membrane with a surface-modified titanium dioxide nanometer layer is obtained. (1) Weigh 2.0g of pyromellitic dianhydride (PMDA) and 1.8g of 4,4'-diaminodiphenyl ether (ODA) with a molar ratio of 1:1, and dissolve all ODA in 30ml of N,N - in dimethylformamide (DMF) solvent, mechanically stirred, after ODA is all dissolved in DMF, under the condition of ice-water bath, add PMDA step by step, after obtaining the polyamic acid solution with moderate viscosity, after mechanically stirring for 2h, put The polyamic acid solution is put into a 20ml syringe, and the polyamic acid fiber film is prepared by electrospinning technology. The specific parameters of the electrospinning machine are spinning voltage: 20kV; spinning temperature: room temperature; spinning humidity: 20%; Syringe needle diameter: No. 12; Receiving roller speed: 80.0m / min; Receiving d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Provided is a preparation method of a surface modified titanium dioxide nano-particle polyimide fiber membrane. Firstly, a polyimide fiber membrane prepared through electrostatic spinning is put in apotassium hydroxide solution for etching, washing is performed to make the membrane neutral, then the polyimide fiber membrane is soaked in a titanium compound water solution for treatment, and finally the surface modified titanium dioxide nano-particle polyimide fiber membrane is prepared through washing, drying and temperature rise thermal imidization treatment. The method is simple to carry out, a basic structures is kept well, the cost is low, the thickness of titanium dioxide nano-particle layer can be controlled within 10 nm, and application prospect is good.

Description

technical field [0001] The invention belongs to the technical field of polyimide fiber membranes, in particular to a method for preparing a surface-modified titanium dioxide nanoparticle polyimide fiber membrane. Background technique [0002] In recent years, with the increasingly prominent environmental problems and the rapid development of new energy vehicles, high-power lithium-ion batteries have become a current research hotspot. Among them, the battery separator, as an important part of the lithium-ion battery, directly affects the overall performance of the lithium-ion battery, especially the safety performance, so the separator is also called the third electrode of the battery. Currently, commercial Li-ion battery separators are mainly polyolefin separators: polyethylene (PE) and polypropylene (PP) separators. Although polyolefin separator has the advantages of good mechanical properties, chemical corrosion resistance and stable battery performance, its disadvantages...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M11/46D04H1/728D04H1/4334D06M101/30
CPCD04H1/4334D04H1/728D06M11/46D06M2101/30
Inventor 齐胜利董国庆汪晓东田国峰武德珍
Owner 启鼎技术(北京)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com