Glaze capable of inducing to generate negative ions, ceramic tile and ceramic tile preparation process

A preparation process and negative ion technology, which is applied in the field of architectural ceramics, can solve the problems that cannot be applied and affect the color effect of the brick surface, etc., and achieve the effect of energetic, simple and easy-to-control preparation process steps, and promoting blood circulation

Active Publication Date: 2018-10-26
FOSHAN DONGPENG CERAMIC
View PDF7 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The negative ion tiles produced above are made of tourmaline, which has limited application and cannot be applied to the bricks of the inkjet infiltration process, because the added tourmaline reacts with the color aid of the ink, which affects the color development effect of the brick surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glaze capable of inducing to generate negative ions, ceramic tile and ceramic tile preparation process
  • Glaze capable of inducing to generate negative ions, ceramic tile and ceramic tile preparation process
  • Glaze capable of inducing to generate negative ions, ceramic tile and ceramic tile preparation process

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0044] A kind of preparation technology that can induce negative ion ceramic tile, comprises the following steps:

[0045] Prepare the bottom glaze slurry: mix the raw materials of the bottom glaze into the ball mill according to the ratio and carry out wet ball milling to obtain the bottom glaze slurry;

[0046] Preparation of surface glaze slurry: mix the raw materials of surface glaze into a ball mill according to the ratio and carry out wet ball milling to obtain surface glaze slurry,

[0047] Preparation of adobe: use existing adobe raw materials to make adobe;

[0048] Glazing: apply the bottom glaze slurry on the surface of the brick, and then apply the surface glaze slurry on the bottom glaze slurry;

[0049] It is fired in a kiln at a firing temperature of 1080-1200°C.

[0050] The conventional firing temperature can be used to complete the firing by using the existing firing temperature control, which is easier for process control. The preparation process steps of...

Embodiment 1

[0063] A kind of glaze that can induce negative ions, including bottom glaze and top glaze, the raw material formula in terms of mass percentage is shown in the following table:

[0064]

[0065] The firing temperature of bottom glaze and top glaze is 1080~1100℃.

[0066] The ceramic tile with the above-mentioned inducible negative ion glaze includes a green body, a bottom glaze layer and a top glaze layer arranged in sequence from bottom to top, the bottom glaze layer is formed by the bottom glaze, and the top glaze layer is formed by the top glaze. A decorative layer is arranged on the glaze layer by means of inkjet penetration process, inkjet printing, roller printing and / or screen printing.

[0067] The above-mentioned preparation technology that can induce negative ion ceramic tile comprises the following steps:

[0068] Preparation of bottom glaze slurry: Mix the raw materials of bottom glaze into ball mill according to the ratio and carry out wet ball milling to obt...

Embodiment 2

[0075] The preparation process of the inducible negative ion glaze of the present embodiment, the tiles of the above-mentioned inducible negative ion glaze, and the inducible negative ion ceramic tile is basically the same as that of Example 1, the difference is that the negative ion glaze can be induced The raw material formula in mass percent is as shown in the following table:

[0076]

[0077] The firing temperature of the glaze that can induce negative ions is 1080~1200°C. The firing temperature of ceramic tiles that can induce negative ions is 1080-1200°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glaze capable of inducing to generate negative ions. The glaze capable of inducing to generate the negative ions comprises ground glaze and cover glaze, the ground glaze comprises the following components in percentages by mass: 8-9% of sodium pyroxene, 6-7% of fluorite, 3-4% of barite and the balance of basic ground glaze; and the cover glaze comprises the following components in percentages by mass: 0.5-1% of titanium ores, 8-13% of alpha-Al2O3, 10-15% of titanium dioxide and the balance of basic cover glaze. The invention further discloses a ceramic tile with the glaze capable of inducing to generate negative ions and a preparation process of the ceramic tile. The sodium pyroxene, the fluorite and the barite are added on the ground glaze to trigger alpha-Al2O3of the cover glaze and titanium oxide in the titanium dioxide to generate an electric field on a tile surface, and substances such as water in air are ionized to generate the negative ions. The groundglaze does not have materials which affect color development of a color aid such as tourmaline, color development of ceramic ink is not affected, and the glaze can be applied to a ceramic tile by aninkjet penetrating technology.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a glaze capable of inducing negative ions, ceramic tiles and a preparation method for ceramic tiles. Background technique [0002] With the development of industry, the air pollution is becoming more and more serious, and the air contains various substances harmful to the human body, so the quality of the air has attracted more and more attention from the people. As well as the gradual improvement of people's living standards, the requirements for the quality of the air in the living environment are getting higher and higher. Therefore, the environmental protection and functional health of building materials have been paid more and more attention by people. In recent years, negative ion interior decoration materials and products have emerged at home and abroad, such as negative ion coatings, negative ion panels, and negative ion tiles. This kind of material produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/00C04B41/89B28B11/00B28B11/04
CPCB28B11/001B28B11/044C03C8/00C04B41/52C04B41/89C04B41/504C04B41/4535C04B41/5022
Inventor 祁明钟保民
Owner FOSHAN DONGPENG CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com