Manufacturing method of wear-resisting alloy steel guard sleeve

A manufacturing method and alloy steel technology, which are applied in the field of high manganese wear-resistant steel rolling sheath materials, can solve the problems of affecting production efficiency, short service life, insufficient strength, etc., and achieve long service life, good uniformity, The effect of good toughness

Inactive Publication Date: 2018-10-02
ZHENJIANG SUBAIXIN CONSTR MACHINERY CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The shot blasting machine uses a high-speed rotating shot blaster to spray the projectile at high speed, so that the projectile has a certain kinetic energy, and the high-speed linear motion projectile directly impacts on the surface of the workpiece to remove the rust on the surface of the workpiece, but the shot blasting machine is running During the shot blasting process, the projectile will bypass the workpiece and hit the roller in the shot blasting machine chamber. After a long time, the high-speed projectile will penetrate the roller. Therefore, in the prior art, it is often installed on the roller of the shot blasting machine room. Sheath, there are many types of existing protective plates, generally high-chromium cast iron or manganese steel materials, but in the face of high-speed jet projectiles, the strength of the existing sheath is still not good enough due to material problems, and the service life is not good enough Long, so it must be replaced after a period of use, which not only causes waste of cost but also delays the construction period and affects production efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The manufacturing method of the wear-resistant alloy steel sheath of the present invention will be described in further detail below in combination with specific embodiments.

[0017] The manufacture method of wear-resistant alloy steel sheath of the present invention, comprises the following steps:

[0018] A. Ingredients: In terms of weight percentage, according to the following chemical ingredients, carbon 2.3-2.9%, silicon 1.5-1.8%, manganese 13-15%, chromium 2.5-3.5%, nickel 0.7-0.9% , titanium 0.7-0.9%, silicon 0.2-0.3%, rare earth 0.7-1.5%, sulfur 0.02-0.04%, and the balance is iron;

[0019] B. Melting: Vacuumize the melting furnace so that the pressure in the melting furnace is 1.5-2.5Pa, put the ingredients obtained in step A into the vacuum melting furnace for melting; when melting, the melting temperature is 1600-1700°C, and the melting time is 30 ~45 min, and the temperature out of the furnace is 1300~1450℃.

[0020] C. Pouring: Pouring the solution obt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacturing method of a wear-resisting alloy steel guard sleeve applied to a shot blasting chamber. The manufacturing method includes the following steps of A, preparationof materials; B, smelting; C, pouring; D, cooling, wherein a casting obtained in step C is cooled by wind for 20-30 min, then cooled in water for 15-25 min and condensed for 10-15 min through a condensation device; E, annealing, wherein the casting obtained after cooling in step D is ground, machined and heated, the temperature is maintained constant, then raised and remained constant, and coolingthrough water is carried out quickly; F, quenching, wherein the casting is heated to 900-1,000 DEG C for quenching, and tempering is conducted in time after quenching. The method has the following advantages that since appropriate materials and an appropriate proportion are selected, vacuum pumping is conducted, then smelting is carried out, correspondingly the dissolution uniformity of a solution is high, cooling is carried out through three modes step by step after pouring, and the quality of casting is ensured; therefore, a guard board has high hardness, intensity and tenacity and achievesgreat mechanical performance, the service life is long, and better economic performance and comprehensive mechanical performance are achieved.

Description

technical field [0001] The invention relates to a high manganese wear-resistant steel rolling sheath material, in particular to a method for manufacturing a wear-resistant alloy steel sheath used in a shot blasting chamber. Background technique [0002] The shot blasting machine uses a high-speed rotating shot blaster to spray the projectile at high speed, so that the projectile has a certain kinetic energy, and the high-speed linear motion projectile directly impacts on the surface of the workpiece to remove the rust on the surface of the workpiece, but the shot blasting machine is running During the shot blasting process, the projectile will bypass the workpiece and hit the roller in the shot blasting machine chamber. After a long time, the high-speed projectile will penetrate the roller. Therefore, in the prior art, it is often installed on the roller of the shot blasting machine room. Sheath, there are many types of existing protective plates, generally high-chromium cas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/58C22C38/56C22C38/02C22C38/50C22C33/04C21D1/18C21D6/00B22D30/00
CPCC22C38/58B22D30/00C21D1/18C21D6/005C22C33/04C22C38/005C22C38/02C22C38/50C22C38/56
Inventor 张长凤
Owner ZHENJIANG SUBAIXIN CONSTR MACHINERY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products