High-strength high-temperature-resistance high borosilicate glass

A high-borosilicate glass, high-temperature-resistant technology, applied in the field of glass processing, can solve the problems of insufficient strength and high-temperature resistance, and achieve the effects of excellent anti-corrosion performance, prolonging service life and improving hardness

Inactive Publication Date: 2018-08-28
ANHUI DU HI TECH GLASS
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the strength and high temperature resistance of the currently prepared high borosilicate glass cannot meet the needs of some occasions in the market, and a high borosilicate glass with higher strength and better high temperature resistance is needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A high-strength and high-temperature-resistant borosilicate glass, which is made of the following components in parts by weight: 112 quartz sand, 35 sodium borate, 34 methyltrialkoxysilane modified silicon boride, 12 dolomite, and aluminum alum Soil 14, barium metaphosphate 1.8, dilanthanum trioxide 0.12, purple sand mud 5, boron oxide 3, silicon calcium slag 7, vanadium dioxide 1.

[0015] Further, the preparation method of the methyltrialkoxysilane modified silicon boride is:

[0016] Disperse silicon boride evenly in deionized water, prepare a silicon boride suspension with a mass fraction of 12.8%, add sodium dodecylbenzenesulfonate with a mass of 1.5% to the silicon boride suspension, stir evenly, Heat to 70°C, stir at 1200r / min for 32min, then stop stirring, continue to keep warm for 15min, then use ultrasonic treatment for 40s, then add 5% methyltrialkoxysilane and 15% of silicon boride suspension mass Absolute ethanol, adjust the temperature to 80°C, stir at 50...

Embodiment 2

[0021] A high-strength and high-temperature-resistant borosilicate glass, which is made of the following components in parts by weight: 112 quartz sand, 35 sodium borate, 38 methyl trialkoxysilane modified silicon boride, 12 dolomite, and aluminum alum Soil 14, barium metaphosphate 1.8, dilanthanum trioxide 0.12, purple clay 5, boron oxide 3, silicon calcium slag 7, vanadium dioxide 3.

[0022] Further, the preparation method of the methyltrialkoxysilane modified silicon boride is:

[0023] Disperse silicon boride evenly in deionized water, prepare a silicon boride suspension with a mass fraction of 12.8%, add sodium dodecylbenzenesulfonate with a mass of 1.5% to the silicon boride suspension, stir evenly, Heat to 70°C, stir at 1200r / min for 32min, then stop stirring, continue to keep warm for 15min, then use ultrasonic treatment for 40s, then add 5% methyltrialkoxysilane and 15% of silicon boride suspension mass Absolute ethanol, adjust the temperature to 80°C, stir at 500r / ...

Embodiment 3

[0028] A high-strength and high-temperature-resistant borosilicate glass, which is made of the following components in parts by weight: 112 quartz sand, 35 sodium borate, 36 methyltrialkoxysilane modified silicon boride, 12 dolomite, and aluminum alum Soil 14, barium metaphosphate 1.8, dilanthanum trioxide 0.12, purple sand mud 5, boron oxide 3, silicon calcium slag 7, vanadium dioxide 2.

[0029] Further, the preparation method of the methyltrialkoxysilane modified silicon boride is:

[0030] Disperse silicon boride evenly in deionized water, prepare a silicon boride suspension with a mass fraction of 12.8%, add sodium dodecylbenzenesulfonate with a mass of 1.5% to the silicon boride suspension, stir evenly, Heat to 70°C, stir at 1200r / min for 32min, then stop stirring, continue to keep warm for 15min, then use ultrasonic treatment for 40s, then add 5% methyltrialkoxysilane and 15% of silicon boride suspension mass Absolute ethanol, adjust the temperature to 80°C, stir at 50...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-strength high-temperature-resistant high borosilicate glass, and relates to the technical field of glass processing. The glass is prepared from the following components:112 parts of quartz sand, 35 parts of sodium borate, 34-38 parts of methyltrioxysilane modified boride silicon, 12 parts of dolomite, 14 parts of bauxite, 1.8 parts of barium metaphosphate, 0.12 parts of lanthanum trioxide, 5 parts of purple sand mud, 3 parts of boron oxide, 7 parts of calcium silicon slag and 1-3 parts of vanadium dioxide; The high-strength high-temperature-resistance high borosilicate glass has excellent anti-corrosion performance, high strength and high temperature resistance.

Description

technical field [0001] The invention belongs to the technical field of glass processing, and in particular relates to high-strength and high-temperature-resistant high borosilicate glass. Background technique [0002] High borosilicate glass (also known as hard glass), because the linear thermal expansion coefficient is (3.3 ± 0.1) × 10-6 / K, it is also called "borosilicate glass 3.3". It is a special glass material with low expansion rate, high temperature resistance, high strength, high hardness, high light transmittance and high chemical stability. Because of its excellent performance, it is widely used in solar energy, chemical industry, pharmaceutical packaging, electric light source , craft jewelry and other industries. Its good performance has been widely recognized by all walks of life in the world, especially in the field of solar energy, and developed countries such as Germany and the United States have carried out extensive promotion. [0003] However, the streng...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C6/04
CPCC03C1/002
Inventor 乔业全
Owner ANHUI DU HI TECH GLASS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap