Reproducible temperature-sensitive textile fabric and preparation method thereof

A textile fabric and temperature-sensitive technology, applied in the field of renewable temperature-sensitive textile fabric and its preparation, can solve the problems of poor flame retardant effect, pollute the environment, reduce the practicability of renewable fabrics, etc., and achieve the effect of antistatic ability

Inactive Publication Date: 2018-08-07
JIANGSU SHENGLAN CLOTHING CREATIVE
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Among the existing fabrics, most of them are made of chemical fabrics, which not only pollute the environment, but also cause harm to the human body, and there are also non-renewable problems; so renewable fabrics appear, but because of these recycled fabrics, flame retardant Ineffective and does not adjust to ambient temperature, which reduces the utility of renewable fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A renewable temperature-sensitive textile fabric, characterized in that: the fabric is composed of warp threads and weft threads, and the warp threads or weft threads include bamboo fibers, wood fibers, cotton fibers, flame-retardant fibers, temperature-sensitive antibacterial nanofibers, and polylactic acid fibers The warp thread or weft thread forms a temperature-sensitive adhesion layer after being dipped and dried in a temperature-sensitive mixed solution, and the temperature-sensitive mixed solution includes chitin, acrylic fiber, propyl gallate, ammonium polyphosphate, kaempferol, methyl acrylate Esters, coupling agents, dispersants, heat stabilizers and antistatic suspensions.

[0028] Preferably, the coupling agent is selected from 3-acrylpropyltrimethoxysilane.

[0029] Preferably, the dispersant includes polyacrylamide and lignosulfonate in a mass ratio of 1:0.5.

[0030] Preferably, the thermal stabilizer is selected from zinc palmitate.

[0031] Preferably...

Embodiment 2

[0047] A renewable temperature-sensitive textile fabric, characterized in that: the fabric is composed of warp threads and weft threads, and the warp threads or weft threads include bamboo fibers, wood fibers, cotton fibers, flame-retardant fibers, temperature-sensitive antibacterial nanofibers, and polylactic acid fibers The warp thread or weft thread forms a temperature-sensitive adhesion layer after being dipped and dried in a temperature-sensitive mixed solution, and the temperature-sensitive mixed solution includes chitin, acrylic fiber, propyl gallate, ammonium polyphosphate, kaempferol, methyl acrylate Esters, coupling agents, dispersants, heat stabilizers and antistatic suspensions.

[0048]Preferably, the coupling agent is selected from N-2(aminoethyl)3-aminopropylmethyltriethoxysilane.

[0049] Preferably, the dispersant includes polyacrylamide and lignosulfonate in a mass ratio of 1:0.5.

[0050] Preferably, the heat stabilizer is selected from cadmium ricinoleate....

Embodiment 3

[0067] A renewable temperature-sensitive textile fabric, characterized in that: the fabric is composed of warp threads and weft threads, and the warp threads or weft threads include bamboo fibers, wood fibers, cotton fibers, flame-retardant fibers, temperature-sensitive antibacterial nanofibers, and polylactic acid fibers The warp thread or weft thread forms a temperature-sensitive adhesion layer after being dipped and dried in a temperature-sensitive mixed solution, and the temperature-sensitive mixed solution includes chitin, acrylic fiber, propyl gallate, ammonium polyphosphate, kaempferol, methyl acrylate Esters, coupling agents, dispersants, heat stabilizers and antistatic suspensions.

[0068] Preferably, the coupling agent is selected from N-2(aminoethyl)3-aminopropylmethyldimethoxysilane.

[0069] Preferably, the dispersant includes polyacrylamide and lignosulfonate in a mass ratio of 1:0.5.

[0070] Preferably, the thermal stabilizer is selected from calcium lauricat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a reproducible temperature-sensitive textile fabric and a preparation method thereof. The fabric is prepared from warp yarns and weft yarns, the warp yarns or the weft yarns are prepared from bamboo fiber, wood fiber, cotton fibre, fire resistant fibre, temperature-sensitive antibacterial nanofiber and polylactic acid fiber; the warp yarns or the weft yarns are soaked by atemperature-sensitive mixed solution and subjected to drying treatment to form a temperature-sensitive adhesive layer, wherein the temperature-sensitive mixed solution is prepared from chitin, acrylicfiber, propyl gallate, ammonium polyphosphate, kaempferol, methyl acrylate, a coupling reagent, a dispersing agent, a heat stabilizer and antistatic suspension liquid. According to the reproducible temperature-sensitive textile fabric and the preparation method thereof, the fuse of the reproducible fabric is realized through the mixing of the bamboo fiber, the wood fiber, the cotton fibre, the fire resistant fibre and the temperature-sensitive antibacterial nanofiber and combining with the coupling reagent, the dispersing agent and the heat stabilizer, meanwhile, the functions of inflaming retarding and temperature-sensitive adjustment are realized. Furthermore, through the antistatic suspension liquid, the antistatic capacity of the fabric is realized. The reproducible temperature-sensitive textile fabric is reasonable in design and is suitable for promotion and use.

Description

technical field [0001] The invention relates to the technical field of garment processing, in particular to a regenerated temperature-sensitive textile fabric and a preparation method thereof. Background technique [0002] Among the existing fabrics, most of them are made of chemical fabrics, which not only pollute the environment, but also cause harm to the human body, and there are also non-renewable problems; so renewable fabrics appear, but because of these recycled fabrics, flame retardant Poorly effective and does not adjust to ambient temperature, which reduces the utility of recycled fabrics. Contents of the invention [0003] In order to overcome the above-mentioned shortcomings, the present invention provides a regenerable, antistatic, flame-retardant and adjustable temperature-sensitive textile fabric according to the environment and a preparation method thereof. [0004] The present invention achieves the above object through the following technical solutions:...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/00D03D15/12D06M15/03D06M13/224D06M11/72D06M13/152D06M11/46D01F6/54D01F1/10D01F1/09D03D15/217D03D15/283D03D15/50D03D15/513
CPCD01F1/09D01F1/10D01F6/54D06M11/46D06M11/72D06M13/152D06M13/224D06M13/2246D06M15/03D10B2201/10D10B2201/01D10B2201/02D10B2331/04D06M2101/32D06M2101/06D03D15/533D03D15/513
Inventor 王秋芬
Owner JIANGSU SHENGLAN CLOTHING CREATIVE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap