Aluminum profile surface modification method

A technology of surface modification and aluminum profiles, applied in the direction of coating, etc., can solve the problems of shortened service life of aluminum profiles, influence on aluminum profile processing, poor metal fatigue, etc., to prolong service life, improve poor fatigue resistance, and low equipment requirements Effect

Inactive Publication Date: 2018-08-03
广东星球铝业有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the metal fatigue of aluminum profiles is poor and prone to wear, so the service life of aluminum profiles will be shortened. Moreover, the aluminum in aluminum profiles is highly active and prone to oxidation in the air, forming an aluminum oxide film on the surface of aluminum profiles. Subsequent processing of aluminum profiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for modifying the surface of an aluminum profile proposed by the present invention comprises the following steps:

[0021] S1, preparation of surface treatment agent: according to 5 parts of oxalic acid, 8 parts of acetic acid, 0.3 parts of metal corrosion inhibitor, 1 part of polyethylene glycol oleate, 2 parts of sodium dodecylbenzenesulfonate, tetradecyl dimethyl 1.6 parts of base betaine, 30 parts of methyl etherified hexamethylolmelamine resin, 50 parts of water-based acrylic resin, 40 parts of mixed solvent Weigh each raw material of surface treatment agent, and methyl etherified hexamethylolmelamine resin and water-based acrylic The resin is heated and dissolved in a mixed solvent to obtain a mixture A, and then add polyethylene glycol oleate, sodium dodecylbenzenesulfonate and tetradecyldimethyl betaine to the mixture A, mix well and then add in sequence Acetic acid, oxalic acid and metal corrosion inhibitor, ultrasonic dispersion, after the metal corro...

Embodiment 2

[0027] A method for modifying the surface of an aluminum profile proposed by the present invention comprises the following steps:

[0028] S1, preparation of surface treatment agent: according to 8 parts of oxalic acid, 5 parts of acetic acid, 0.4 parts of metal corrosion inhibitor, 1.5 parts of polyethylene glycol oleate, 3 parts of sodium dodecylbenzenesulfonate, tetradecyl dimethyl 2.4 parts of base betaine, 40 parts of methyl etherified hexamethylolmelamine resin, 40 parts of water-based acrylic resin, 50 parts of mixed solvent Weigh each raw material of surface treatment agent, and methyl etherified hexamethylolmelamine resin and water-based acrylic acid The resin is heated and dissolved in a mixed solvent to obtain a mixture A, and then add polyethylene glycol oleate, sodium dodecylbenzenesulfonate and tetradecyldimethyl betaine to the mixture A, mix well and then add in sequence Acetic acid, oxalic acid and metal corrosion inhibitor, ultrasonic dispersion, after the met...

Embodiment 3

[0034] A method for modifying the surface of an aluminum profile proposed by the present invention comprises the following steps:

[0035] S1. Preparation of surface treatment agent: according to 3 parts of oxalic acid, 10 parts of acetic acid, 0.2 part of metal corrosion inhibitor, 0.5 part of polyethylene glycol oleate, 1 part of sodium dodecylbenzenesulfonate, tetradecyl dimethyl 0.8 parts of base betaine, 20 parts of methyl etherified hexamethylol melamine resin, 60 parts of water-based acrylic resin, 30 parts of mixed solvent. The resin is heated and dissolved in a mixed solvent to obtain a mixture A, and then add polyethylene glycol oleate, sodium dodecylbenzenesulfonate and tetradecyldimethyl betaine to the mixture A, mix well and then add in sequence Acetic acid, oxalic acid and metal corrosion inhibitor, ultrasonic dispersion, after the metal corrosion inhibitor is uniformly dispersed, the surface treatment agent is obtained;

[0036] S2. Surface treatment of aluminu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aluminum profile surface modification method. The method comprises the steps as follows: S1, preparing a surface treating agent; S2, washing an aluminum profile with distilled water, wiping the aluminum profile with deerskin cloth, treating the aluminum profile with the surface treating agent, introducing inert gas continuously, performing vacuum drying, and naturally cooling the aluminum profile to the room temperature to finish surface treatment of the aluminum profile; S3, preparing an aluminum profile modifier; S4, spraying the aluminum profile modifier on the surface of the aluminum profile subjected to surface treatment in the S2, and leveling, drying and cooling the aluminum profile to the room temperature to finish modification of the surface of the aluminum profile. The modification method is simple to operate, has low requirement for required equipment, can be applied to industrial production and has wide application ranges. The modified aluminum profile has good wear resistance and long service life.

Description

technical field [0001] The invention relates to the technical field of aluminum profile processing, in particular to a method for modifying the surface of an aluminum profile. Background technique [0002] Due to the advantages of light weight, easy forming, high strength, corrosion resistance, renewable, less pollution, and low maintenance costs, aluminum profiles are widely used in the fields of construction, automobiles, furniture, vehicles, and medical equipment. However, the metal fatigue of aluminum profiles is poor and prone to wear, so the service life of aluminum profiles will be shortened. Moreover, the aluminum in aluminum profiles is highly active and prone to oxidation in the air, forming an aluminum oxide film on the surface of aluminum profiles. Subsequent processing of aluminum profiles. Based on this, the present invention proposes a method for modifying the surface of an aluminum profile. Contents of the invention [0003] The purpose of the present inv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/00C09D7/63C09D7/61C09D7/65
Inventor 高国柱
Owner 广东星球铝业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com