Heat preservation type inner wall plastering anhydrite and method

A technology for plastering plaster and interior walls, applied in the field of plaster plastering, which can solve the problems of not being too thick, poor water resistance, easy cracking, etc., and achieve the effects of less overcooling or overheating, good reversibility, and extended service life

Inactive Publication Date: 2018-07-24
青岛恒基伟业建材有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, gypsum-based products also have many shortcomings, such as one-time construction thickness should not be too large, easy to crack, hollow, poor water resistance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat preservation type inner wall plastering anhydrite and method
  • Heat preservation type inner wall plastering anhydrite and method
  • Heat preservation type inner wall plastering anhydrite and method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A heat-preserving plaster for interior walls, which consists of the following substances in parts by weight:

[0037]

[0038] The preparation method of above-mentioned stucco plaster is:

[0039] 1. Prepare raw materials:

[0040] Weigh the following materials in order according to parts by mass: 400 parts of α-type hemihydrate gypsum, 300 parts of microcapsule phase change material, 50 parts of 325 mesh heavy calcium, 70 parts of 70-140 mesh quartz sand, vitrified microparticles with a particle size of less than 1.5mm. 50 parts of beads, 20 parts of redispersible latex powder, 0.5 parts of starch ether, 2.5 parts of cellulose ether, and 0.4 part of retarder; among them, the whiteness of 325 mesh heavy calcium is 95%, and the content of calcium carbonate is 98%.

[0041] 2. Mixed production:

[0042] After the raw materials are ready, add the above-mentioned α-type hemihydrate gypsum, microcapsule phase change material, heavy calcium, quartz sand, and vitrified mi...

Embodiment 2

[0052] A thermal insulation type interior wall plastering plaster, which is composed of the following parts by weight:

[0053]

[0054] Except for the different parts of raw materials, the manufacturing method and using method of plastering gypsum in this embodiment are the same as those in the first embodiment.

[0055] It has been verified that the product performance of this product meets the technical indicators of GB / T28627-2012, and the main technical parameters are shown in Table 2.

[0056] Table 2

[0057] parameter

Embodiment 3

[0059] A thermal insulation type interior wall plastering plaster, which is composed of the following parts by weight:

[0060]

[0061] Except for the different parts of raw materials, the manufacturing method and using method of plastering gypsum in this embodiment are the same as those in the first embodiment.

[0062] It has been verified that the product performance of this product meets the technical indicators of GB / T28627-2012, and the main technical parameters are shown in Table 3.

[0063] table 3

[0064] parameter

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses heat preservation type inner wall plastering anhydrite and a method. The heat preservation type inner wall plastering anhydrite is prepared from the following matters in partsby weight: 400 to 450 parts of alpha type hemihydrates gypsum, 200 to 300 parts of a microcapsule phase-change material, 50 to 100 parts of calcium triple superphosphate, 20 to 70 parts of quartz sand, 50 to 60 parts of glass beads, 15 to 20 parts of redispersible emulsion powder, 0.5 part of starch ether, 2.5 parts of cellulose ether and 0.4 part of retarder. A preparation method of the heat preservation type inner wall plastering anhydrite comprises the following steps: weighing all raw materials in parts by mass, sequentially adding the raw materials in weightlessness dry blending equipment, and starting the weightlessness dry blending equipment for blending after completing addition of all the raw materials; discharging and packaging after uniformly stirring. The heat preservation typeinner wall plastering anhydrite disclosed by the invention is mainly applied to inner wall plastering, the thickness which is 1 to 2 cm can be achieved through one-time construction, and the heat preservation type inner wall plastering anhydrite has a good heat preservation and heat insulation function except the technical effects of common plastering anhydrite construction.

Description

technical field [0001] The invention relates to a plaster for plastering and a method thereof, in particular to a plaster for plastering a heat-retaining interior wall and a method for plastering. Background technique [0002] The traditional material used for interior wall plastering is mainly interior wall plastering mortar, but with the increase in the number of building developments year by year, the demand for interior wall plastering mortar is also increasing, and the supply has been in short supply. [0003] Plastering gypsum is a new type of interior wall leveling material compounded with gypsum as the cementitious material by adding lightweight inorganic materials, aggregates or other additives. It has been widely used as a substitute for interior wall plastering mortar. This material has the functions of being environmentally friendly, improving construction efficiency, sound insulation and humidity control, etc., and it can be initially set in a few minutes at roo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14E04F13/04C04B111/20
CPCC04B28/146C04B2111/00508C04B2111/20C04B2201/32E04F13/04C04B14/06C04B14/28C04B18/027C04B2103/0057C04B24/38C04B24/383C04B2103/22C04B2103/0071
Inventor 闫枫
Owner 青岛恒基伟业建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com