Temperature-sensitive hydrogel and preparation method thereof

A temperature-sensitive hydrogel and deionized water technology, applied in the direction of fire prevention equipment, etc., can solve the problems of high cost, difficulty in widespread promotion and application, complicated separation process, etc., achieve efficient fire extinguishing effect, improve cooling and sealing effect, the effect of increasing the amount of stay

Active Publication Date: 2018-05-18
SICHUAN POLICE COLLEGE
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to its complex preparation and separation process and high cost, it is currently difficult to be widely promoted and applied.
At present, no special temperature-sensitive hydrogel fire extinguishing agent has been developed at home and abroad. After the successful development, it can be widely equipped with fire departments above the county level and emergency rescue units.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A method for preparing a temperature-sensitive hydrogel includes the following steps:

[0026] (1) Pre-configured with methyl cellulose and 75°C deionized water into a reaction solution with a concentration of 39%, fully stirred, and put it in the refrigerator to stand for 55h until use;

[0027] (2) Use the above-mentioned reaction solution as a solvent, and each are configured into NaHCO with a concentration of 2mol / L 3 Solution and NaOH solution, then NaHCO 3 After mixing the solution and NaOH solution, use it to perform acid-base titration on a certain amount of acrylic acid to obtain a sodium acrylate monomer adjustment solution with a pH of 7.0; among them, methyl cellulose can form a better thickening effect with acrylic acid;

[0028] (3) Add N-isopropyl acrylamide to a 1000ml four-neck flask in a certain proportion, and slowly drop a certain amount of sodium acrylate monomer adjustment solution into the four-neck flask under nitrogen protection. The ratio of the amoun...

Embodiment 2

[0032] A method for preparing a temperature-sensitive hydrogel includes the following steps:

[0033] (1) Prepare a reaction solution with a concentration of 40% with methyl cellulose and 80°C deionized water in advance, stir it thoroughly, and put it in the refrigerator to stand for 60 hours until use;

[0034] (2) Use the above-mentioned reaction solution as a solvent, and each are configured into NaHCO with a concentration of 2mol / L 3 Solution and NaOH solution, then NaHCO 3 After mixing the solution and NaOH solution, use it to perform acid-base titration on a certain amount of acrylic acid to obtain a sodium acrylate monomer adjustment solution with a pH of 7.0; among them, methyl cellulose can form a better thickening effect with acrylic acid;

[0035] (3) Add N-isopropyl acrylamide to a 1000ml four-neck flask in a certain proportion, and slowly drop a certain amount of sodium acrylate monomer adjustment solution into the four-neck flask under nitrogen protection. The ratio of ...

Embodiment 3

[0039] A method for preparing a temperature-sensitive hydrogel includes the following steps:

[0040] (1) Pre-configured with methyl cellulose and 85°C deionized water into a 41% concentration reaction solution, fully stirred it, and put it in the refrigerator to stand for 65h until use;

[0041] (2) Use the above-mentioned reaction solution as a solvent, and each are configured into NaHCO with a concentration of 2mol / L 3 Solution and NaOH solution, then NaHCO 3 After mixing the solution and NaOH solution, use it to perform acid-base titration on a certain amount of acrylic acid to obtain a sodium acrylate monomer adjustment solution with a pH of 7.0; among them, methyl cellulose can form a better thickening effect with acrylic acid;

[0042] (3) Add N-isopropyl acrylamide to a 1000ml four-neck flask in a certain proportion, and slowly drop a certain amount of sodium acrylate monomer adjustment solution into the four-neck flask under nitrogen protection. The ratio of the amount of pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses temperature-sensitive hydrogel and a preparation method thereof, and belongs to the technical field of hydrogel. The preparation method of the hydrogel comprises the followingsteps: (1) preparing reaction solution by using methyl cellulose and deionized water; (2) by using the reaction solution as a solvent, respectively preparing NaHCO3 solution and NaOH solution, and then mixing the NaHCO3 solution and the NaOH solution to carry out acid-base titration on a certain amount of acrylic acid, thus obtaining sodium-acrylate monomeric correction liquid with a PH value being 7.0; (3) adding N-isopropylacrylamide into a four-port bottle according to a certain proportion, and slowly dripping a certain amount of the sodium-acrylate monomeric correction liquid into the four-port bottle under the condition of nitrogen protection, thus obtaining dissolving liquid; (4) adding a crosslinking agnet, an initiator and a catalyst into the dissolving liquid to prepare the temperature-sensitive hydrogel. The temperature-sensitive hydrogel disclosed by the invention has good fire-extinguishing performance.

Description

Technical field [0001] The invention relates to the technical field of hydrogels, in particular to a temperature-sensitive hydrogel and a preparation method thereof. Background technique [0002] Water is currently the most commonly used fire extinguishing agent. In recent years, scientific researchers have done a lot of innovative work on how to improve the efficiency of water fire extinguishing, which is mainly reflected in adding different chemical reagents to the water or changing the physical and chemical properties of the water to enhance the viscosity and adhesion of the water in the burning area. Extend the water retention time, improve the effective oxygen insulation and cooling capacity of the water, save water consumption, so as to give full play to the fire extinguishing performance of water and improve the fire extinguishing efficiency. Currently, the most researched are water-based fire extinguishing agents such as water mist, three-phase foam, aqueous film-forming...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/54C08F220/06C08F222/38C08F290/06A62D1/00
CPCA62D1/0064C08F220/54C08F290/062C08F220/06C08F222/385
Inventor 李克建
Owner SICHUAN POLICE COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com