Surface treatment agent capable of generating red stable rust layer

A surface treatment agent and a stable technology, applied in the field of surface treatment agents, can solve problems such as insufficient rust protection stability, and achieve the effects of excellent anti-rust liquid sag performance, excellent anti-corrosion performance, and excellent metal protection performance.

Inactive Publication Date: 2018-05-08
武汉钢铁有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a surface treatment agent that generates a red stable rust layer, which is suitable for bare rust, in view of the current steel surface treatment requirements for the appearance and color of different rust layers and the lack of protection stability of the rust layer obtained by the existing surface treatment agent. Steel coating that produces a red uniform and stable rust layer on bare steel surfaces with excellent, consistent anti-rust sag and anti-corrosion properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A surface treatment agent that generates a red stable rust layer. The components and their mass percentages are: 20% alcohol-soluble phenolic novolac, 2% nickel phosphate, 5% sodium tungstate, 2% sodium silicate, Fe(OH ) 3 5%, Fe 2 o 3 35%, n-butanol 31%, weigh each raw material according to the above ratio, and mix evenly to prepare a surface treatment agent that generates a red stable rust layer.

[0023] Coat the prepared surface treatment agent on the surface of weathering steel bare sample, and let it dry naturally; and accelerate the corrosion in distilled water environment for 10 days (spray distilled water every 3 hours), the surface of weathering steel bare sample without surface treatment The color of the rust layer is uneven, and the rust liquid hangs, and the corrosion rate increases with time; the rust layer on the surface of the bare weathering steel sample coated with the surface treatment agent is uniform red, the rust liquid does not flow, and durin...

Embodiment 2

[0026] A surface treatment agent that generates a red stable rust layer. The components and their mass percentages are: 20% alcohol-soluble phenolic novolac, 3% nickel phosphate, 4% sodium tungstate, 2% sodium silicate, Fe(OH ) 3 6%, Fe 2 o 3 34%, diethylene glycol ether 31%, weigh each raw material according to the above ratio, and mix evenly to prepare a surface treatment agent that generates a red stable rust layer.

[0027] Coat the prepared surface treatment agent on the surface of weathering steel bare sample, and let it dry naturally; and accelerate the corrosion in distilled water environment for 10 days (spray distilled water every 3 hours), the surface of weathering steel bare sample without surface treatment The color of the rust layer is uneven, and the rust liquid hangs, and the corrosion rate increases with time; the rust layer on the surface of the bare weathering steel sample coated with the surface treatment agent is uniform red, the rust liquid does not f...

Embodiment 3

[0029] A surface treatment agent that generates a red stable rust layer. The components and their mass percentages are: 25% alcohol-soluble novolak varnish, 4% nickel phosphate, 4% sodium tungstate, 2% sodium silicate, Fe(OH ) 3 7%, Fe 2 o 3 33%, n-butanol 25%, each raw material is weighed according to the above-mentioned ratio, and mixes evenly, is mixed with the surface treatment agent that generates red stable rust layer.

[0030] Coat the prepared surface treatment agent on the surface of weathering steel bare sample, and let it dry naturally; and accelerate the corrosion in distilled water environment for 10 days (spray distilled water every 3 hours), the surface of weathering steel bare sample without surface treatment The color of the rust layer is uneven, and the rust liquid hangs, and the corrosion rate increases with time; the rust layer on the surface of the bare weathering steel sample coated with the surface treatment agent is uniform red, the rust liquid does...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a surface treatment agent capable of generating a red stable rust layer. The surface treatment agent comprises the following components in percentage by mass: 20-30% of alcohol-soluble phenolic aldehyde varnish, 2-5% of nickel phosphate, 2-5% of sodium tungstate, 2-3% of sodium silicate, 5-10% of Fe(OH)3, 30-35% of Fe2O3 and 23-33% of one or more dilution solvents. The surface treatment agent disclosed by the invention is suitable for bare steel coating; after bare steel is coated with the surface treatment agent, the red uniform stable rust layer is generated on the surface of the bare steel, and has the long-term effective properties of rust liquid sagging prevention and corrosion prevention; and the adopted surface treatment agent has no strong irritating odor, contains no chromium and nitrite, and is safe and environmentally friendly.

Description

technical field [0001] The invention belongs to the technical field of metal protection, in particular to a surface treatment agent for forming a red stable rust layer. Background technique [0002] Metal corrosion is a failure process of metals under the action of environmental corrosive media. It is the inverse process of metallurgical production, and the entropy is constantly increasing. It is an inevitable natural phenomenon that occurs completely spontaneously. Atmospheric corrosion is an important cause of early failure and damage of products, equipment, devices, structural parts, etc., and the economic losses caused by atmospheric corrosion are serious every year. [0003] In the atmospheric natural environment, the formation of a stable protective rust layer on bare steel is a gradual process, which takes a long time, at least 3 years, and some bare steel surfaces form a dense and stable rust layer for more than 10 years. In the process of forming a stable rust laye...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/62C09D161/06C09D5/08
CPCC23C22/62C09D5/08C09D161/06
Inventor 黄先球彭浩郎丰军程鹏马颖庞涛宋建红黄菲何锐李安平
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products