Spherical iron phosphate and its preparation method and application

An iron phosphate, spherical technology, applied in chemical instruments and methods, phosphorus compounds, structural parts, etc., can solve the problem of iron phosphate particle size, particle morphology and particle size distribution difficult to control, poor crystallinity of iron phosphate, vibrating Low density and other problems, to achieve the effect of eliminating micro-component differences, good crystallinity, and high tap density

Active Publication Date: 2019-11-12
HUNAN YACHENG NEW MATERIAL CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a spherical ferric phosphate and its preparation method and application to solve the difficulty in controlling the particle size, particle morphology and particle size distribution of the ferric phosphate prepared by the existing method, and the iron phosphate has poor crystallinity and contains many impurities. , low tap density, and high energy consumption during dehydration and sintering

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spherical iron phosphate and its preparation method and application
  • Spherical iron phosphate and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The preparation method of spherical iron phosphate of the present invention comprises the following steps:

[0035] (1) Add a dispersant to the iron-phosphorus mixed solution containing iron ions and phosphate ions to obtain mixed solution A;

[0036] (2) Under heating conditions, add urea to the mixed solution A obtained in step (1) to adjust the pH value, and continue heating to obtain mixed solution B comprising crystalline ferric phosphate;

[0037] (3) Filter the mixed solution B prepared in step (2), add the filter cake into water to prepare mixed solution C, atomize the mixed solution C with a spray gun and introduce it into a roasting furnace, and heat it at a temperature of 550-750°C Roasting to obtain spherical iron phosphate.

[0038] In the above preparation method of spherical ferric phosphate, the application of the dispersant as the crystal form control agent in step (1) can weaken the molecular force between particles, reduce the tendency of primary par...

Embodiment 1

[0057] (1) The iron-phosphorus mixed solution obtained by mixing the ferric sulfate solution with an iron ion concentration of 1mol / L and the ammonium dihydrogen phosphate solution with a phosphate ion concentration of 1mol / L according to the iron-phosphorus molar ratio of 1:1, at 55°C, Under the condition of rotating speed of 180r / min, polyvinyl alcohol with a fraction of 10% of iron-phosphorus mixed liquid was added, stirred for 5 minutes, and mixed liquid A was obtained;

[0058] (2) Under the conditions of heating at 60°C and a stirring rate of 360r / min, add urea with a concentration of 0.2mol / L to the mixed solution A obtained in step (1) to adjust the pH value to 2.0, continue heating to 85°C, and keep warm 120min, obtain the mixed solution B that comprises crystalline ferric phosphate, i.e. ferric phosphate slurry;

[0059] (3) The mixed solution B obtained in step (2) is repeatedly washed with pure water and press-filtered until the conductivity of the filtrate is less...

Embodiment 2

[0063] (1) The iron-phosphorus mixed solution obtained by mixing the ferric sulfate solution with the iron ion concentration of 0.5mol / L and the ammonium dihydrogen phosphate solution with the phosphate ion concentration of 0.5mol / L according to the iron-phosphorus molar ratio of 1: 1.15, at 55 ℃, under the condition of rotating speed of 360r / min, add polyvinyl alcohol with a fraction of 5% of the iron-phosphorus mixed liquid, and stir for 10 minutes to obtain the mixed liquid A;

[0064] (2) Under the conditions of heating at 70°C and a stirring rate of 600r / min, add urea with a concentration of 0.2mol / L to the mixed solution A obtained in step (1) to adjust the pH value to 1.0, continue heating to 95°C, and keep warm 50min, obtain the mixed solution B that comprises crystalline ferric phosphate, i.e. ferric phosphate slurry;

[0065] (3) The mixed solution B obtained in step (2) is repeatedly washed with pure water and press-filtered until the conductivity of the filtrate is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses spherical iron phosphate and a preparation method and application thereof. The preparation method comprises the following steps: adding a disperser into iron-phosphorus mixed liquor containing iron ion and phosphate anion, thus obtaining mixed liquor A; under a heating condition, adding urea into the mixed liquor A to regulate a pH value, and continuously heating to obtainmixed liquor B containing crystal-form iron phosphate; filtering the mixed liquor B, adding a filter cake into water to prepare mixed liquor C, atomizing the mixed liquor C by a spray gun, leading into a roasting furnace, and roasting at a temperature of 550 to 750 DEG C to obtain the spherical iron phosphate. The spherical iron phosphate is pure in crystalline phase, good in crystallinity, spherical in shape, uniform in grain fineness distribution and high in tap density, and can serve as a precursor for synthesizing spherical lithium iron phosphate with high tap density; the spherical iron phosphate can eliminate microscopic composition difference caused by different diffusion paths in a reaction, so as to generate the lithium iron phosphate with a uniform structure, and thus the performance of the lithium iron phosphate is improved.

Description

technical field [0001] The invention relates to the technical field of lithium ion battery materials, in particular to a spherical iron phosphate and its preparation method and application. Background technique [0002] Olivine-structured lithium iron phosphate (LiFePO 4 ) has the advantages of abundant raw materials, stable discharge platform, good thermal stability, high safety, and environmental friendliness. It has attracted much attention in the fields of electric vehicles, power tools, and large-scale energy storage. However, LiFePO 4 It has the disadvantages of poor conductivity and low tap density. Poor electrical conductivity can be improved by coating conductive carbon material on its surface, doping high-valent metal ions in the bulk, or refining particles, etc., but the shortcoming of low tap density has not been effectively solved. [0003] After research, it is found that the preparation of high-density spherical precursors is one of the effective ways to obt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B25/37H01M4/58H01M10/0525
CPCC01B25/375C01P2002/72C01P2004/03C01P2004/32C01P2004/62C01P2006/11C01P2006/40H01M4/5825H01M10/0525Y02E60/10
Inventor 刘志成颜志雄
Owner HUNAN YACHENG NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com