High-yield-point white cast iron and manufacturing method thereof

A technology of white cast iron and manufacturing method, which is applied in the field of iron-carbon alloy, can solve problems such as failure, achieve the effect of improving yield point, improving mechanical properties, and meeting alternating loads

Inactive Publication Date: 2018-04-20
靖江市新东机械零部件制造有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the disadvantages of common white cast iron, such as low yield point and incapable of bearing large pressure and tension, especially under alternating loads, which tend to cause failure during use, the present invention proposes a white cast iron with high yield point and The manufacturing method, the composition of the white cast iron is more reasonable, the working life is longer, the manufacture is easier, the mechanical properties of the white cast iron can be greatly improved, and it can meet the use occasions such as alternating loads

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The present invention will be further described below:

[0021] High yield point white cast iron, the chemical composition of white cast iron is as follows: C 7.7%~18%, Si 3%~15%, Mn 3.5~6.5%, P<0.006%, S<0.005% , the rest is Fe.

[0022] Its manufacturing method of high yield point white cast iron comprises the following steps:

[0023] (1) Preparation materials: C is 15%, Si is 10%, Mn is 5%, P<0.006%, S <0.005%, and the rest is Fe;

[0024] (2) Prepare the pouring model and open the sprue;

[0025] (3) putting the Fe in the step (1) into an induction furnace to melt to obtain liquid molten iron with a melting temperature of 1460-1510°C;

[0026] (4) Put 15% of C, 10% of Si and 5% of Mn in the molten iron in order to form liquid white cast iron;

[0027] (5) Liquid white cast iron is injected into the model;

[0028] (6) Heat preservation of liquid white cast iron, the heat preservation temperature shall not be lower than 650°C, and the heat preservation time sha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-yield-point white cast iron and a manufacturing method thereof and belongs to the technical field of iron-carbon alloys. The high-yield-point white cast iron comprises chemical components including, by mass percent, 7.7%-18% of C, 3%-15% of Si, 3.5%-6.5% of Mn, not more than 0.006% of P, not more than 0.005% of S and the balance Fe. The components are novel, the manufacturing process is reasonable and clear, the chemical component proportion of the white cast iron is provided, the form of carbide is improved in an isothermal cooling and aging manner, the yield point of a cast is increased, the high-yield-point white cast iron is easier to manufacture, the mechanical performance of the white cast iron can be greatly improved, and alternating loads and other theusing occasions can be met.

Description

technical field [0001] The invention belongs to the technical field of iron-carbon alloys, and relates to a white cast iron, in particular to a white cast iron with a high yield point and a manufacturing method thereof. Background technique [0002] Cast iron in which carbon exists in the form of cementite, its cross-section is off-white. It is a good anti-wear material and works under abrasive wear conditions. White cast iron includes ordinary white cast iron, low alloy white cast iron, medium alloy white cast iron and high alloy white cast iron. [0003] Ordinary white cast iron White cast iron with good wear resistance was made in China as early as the Spring and Autumn Period, and was used as some wear-resistant parts. This kind of cast iron has the characteristics of high carbon and low silicon, and has high hardness, but the yield point is very low. It is suitable for manufacturing parts with small impact load, and is generally used in plowshares, grinding discs, gui...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C37/10C21D5/04
CPCC22C37/10C21D5/04
Inventor 毛立新
Owner 靖江市新东机械零部件制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products