Bentonite cat litter and preparation method thereof

A technology of bentonite and bentonite powder, applied in animal houses, applications, animal husbandry, etc., can solve the problems of not being reused, not paying too much attention to sterilization and deodorization in the cat living room, etc., achieving no secondary pollution, long-lasting antibacterial The effect of bactericidal ability and excellent photocatalytic activity

Inactive Publication Date: 2018-04-13
陈燕蓉
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Among the existing cat litters, most cat litters focus on the water absorption effect, and do not pay much attention to the problem of sterilization and deodorization in the cat’s living room, and most of the used cat litter materials are directly thrown away as garbage and cannot be reused

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bentonite cat litter and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Bentonite modification: get 78 parts of bentonite powder and 120 parts of ultrapure water to prepare bentonite suspension, stir evenly on a magnetic stirrer, then take anhydrous sodium carbonate and add it to the bentonite suspension to prepare a 20% slurry. Put the slurry into a water bath for heating and stirring reaction, the heating temperature is 76°C, the stirring speed is 20r / min, the stirring time is 85min, centrifuged and washed, dried and then roasted at a high temperature, the roasting temperature is 250°C, put into a ball mill after roasting Grinding and crushing to obtain modified bentonite powder.

[0029] Preparation of composite materials: take modified bentonite powder and place it in a reaction kettle, add 45 parts of tourmaline powder, nano-TiO 2 42 parts of hydroxyapatite powder, 35 parts of hydroxyapatite powder, 25 parts of bamboo charcoal powder, add 53 parts of glycerol, stir and mix evenly, raise the temperature to 270°C for oil bath reaction fo...

Embodiment 2

[0034] Bentonite modification: get 70 parts of bentonite powder and 150 parts of ultrapure water to prepare bentonite suspension, stir evenly on a magnetic stirrer, then take anhydrous sodium carbonate and add it to the bentonite suspension to prepare a 20% slurry. Put the slurry into a water bath for heating and stirring reaction. The heating temperature is 78°C, the stirring speed is 25r / min, and the stirring time is 60min. Then, it is washed by centrifugation. After drying, it is roasted at a high temperature at 200°C. After roasting, put it into a ball mill Grinding and crushing to obtain modified bentonite powder.

[0035] Preparation of composite materials: take modified bentonite powder and place it in a reaction kettle, add 35 parts of tourmaline powder, nano-TiO 2 45 parts of hydroxyapatite powder, 38 parts of hydroxyapatite powder, 24 parts of bamboo charcoal powder, add 51 parts of glycerol, stir and mix evenly, raise the temperature to 300 ° C for 2.0 h in an oil b...

Embodiment 3

[0040] Bentonite modification: take 80 parts of bentonite powder and 125 parts of ultrapure water to prepare bentonite suspension, stir evenly on a magnetic stirrer, then take anhydrous sodium carbonate and add it to the bentonite suspension to prepare a 20% slurry. Put the slurry into a water bath for heating and stirring reaction. The heating temperature is 79°C, the stirring speed is 35r / min, and the stirring time is 90min. Then, it is washed by centrifugation. After drying, it is roasted at a high temperature at 280°C. After roasting, put it into a ball mill Grinding and crushing to obtain modified bentonite powder.

[0041] Preparation of composite materials: take modified bentonite powder and place it in a reaction kettle, add 38 parts of tourmaline powder, nano-TiO 2 35 parts of hydroxyapatite powder, 42 parts of hydroxyapatite powder, 22 parts of bamboo charcoal powder, add 50 parts of glycerol, stir and mix evenly, raise the temperature to 250°C for oil bath reaction ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of pet supplies, and particularly relates to bentonite cat litter and a preparation method thereof. The bentonite cat litter is prepared from, by weight, 70-80 partsof bentonite powder, 35-45 parts of tourmaline powder, 35-45 parts of nanometer TiO2 powder, 30-45 parts of hydroxyapatite powder, 20-25 parts of bamboo charcoal powder, 10-15 parts of cinnamomum camphora leaves, 10-15 parts of flos buddlejae, 15-20 parts of rhizoma osmundae, 10-15 parts of downy ground cherry fruits or herbs, 8-12 parts of celastrus angulatus, 15-18 parts of herba polygoni avicularis, 20-25 parts of water and 2-3 parts of food colouring. The bentonite cat litter is high in water absorption effect, good in deodorization and sterilization effects, natural, free of pollution, capable of serving the organic fertilizer to be buried and high in utilization rate.

Description

technical field [0001] The invention belongs to the field of pet products, in particular to a bentonite cat litter and a preparation method thereof. Background technique [0002] Cat litter is an object used by the owner to bury the feces and urine of the cats raised by the owner. It has good water absorption and is generally used together with the cat litter box (or cat toilet). Pour an appropriate amount of cat litter on the In the litter box, a trained cat will walk into the litter box and excrete on it when it needs to excrete. The use of cat litter is convenient for cleaning cat excrement, which is conducive to the cleanliness and sanitation of the living environment. [0003] The original cat litter was mainly non-condensing cat litter, mainly for the convenience of collection. With the continuous improvement of cat litter technology, various cat litters appeared, such as sawdust cat litter, bentonite cat litter, crystal cat litter, etc. Sawdust cat litter has enviro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A01K1/015
CPCA01K1/0154A01K1/0155
Inventor 陈燕蓉
Owner 陈燕蓉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com