High-toughness decomposable environment-friendly plastic packaging bag

An environmentally friendly plastic and packaging bag technology, applied in the field of plastic packaging, can solve the problems of increased air and moisture permeability, change of plastic, deterioration of tensile strength, etc., and achieve the effects of easy oxidative degradation, good strength and toughness, and good optical performance.

Inactive Publication Date: 2018-03-09
桐城市强峰包装有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, although there are various degradable plastic packaging bags on the market, tests have shown that most degradable plastic packaging bags generally begin to become thinner, lose weight, and lose strength after being exposed to the environment for 3 months, and gradually break into pieces. If these fragments are buried in garbage or soil, the degradation effect is not obvious
In addition, some additives in degradable plastics will change some characteristics of plastics, such as increased air permeability and moisture permeability, poor tensile strength, etc., which is not conducive to the promotion and application of degradable plastic packaging bags

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A high-toughness decomposable and environmentally friendly plastic packaging bag is composed of the following raw materials in parts by weight: 40 parts of polyolefin plastic, 35 parts of corn straw fiber, 5 parts of chitosan, 8 parts of fresh mulberry leaves, 4 parts of kudzu stems and leaves, poly 45 parts of hydroxybutyrate, 22 parts of polyvinyl butyral, 13 parts of polyethylene, 6 parts of lignin, 5 parts of cotton fiber, 6 parts of montmorillonite, 1 part of stabilizer, 2 parts of coupling agent, 1 part of plasticizer, 0.1 part of polyamide wax micropowder.

Embodiment 2

[0015] A high-toughness decomposable environmentally friendly plastic packaging bag, which is composed of the following raw materials in parts by weight: 65 parts of polyolefin plastic, 45 parts of corn straw fiber, 8 parts of chitosan, 10 parts of fresh mulberry leaves, 6 parts of kudzu stems and leaves, poly 65 parts of hydroxybutyrate, 35 parts of polyvinyl butyral, 20 parts of polyethylene, 11 parts of lignin, 12 parts of cotton fiber, 11 parts of montmorillonite, 3 parts of stabilizer, 4 parts of coupling agent, 5 parts of plasticizer, 0.2 part of polyamide wax micropowder.

Embodiment 3

[0017] A high-toughness decomposable environmentally friendly plastic packaging bag is composed of the following raw materials in parts by weight: 50 parts of polyolefin plastic, 40 parts of corn straw fiber, 6 parts of chitosan, 9 parts of fresh mulberry leaves, 5 parts of kudzu stems and leaves, poly 50 parts of hydroxybutyrate, 30 parts of polyvinyl butyral, 15 parts of polyethylene, 10 parts of lignin, 8 parts of cotton fiber, 10 parts of montmorillonite, 2 parts of stabilizer, 3 parts of coupling agent, 2 parts of plasticizer, 0.2 part of polyamide wax micropowder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-toughness decomposable environment-friendly plastic packaging bag. The high-toughness decomposable environment-friendly plastic packaging bag is prepared from the following raw materials in parts by weight: 40-65 parts of polyolefin plastic, 35-45 parts of corn straw fibers, 5-8 parts of chitosan, 8-10 parts of fresh folium mori, 4-6 parts of kudzu stems and leaves,45-65 parts of polyhydroxybutyrate, 22-35 parts of polyvinyl butyral, 13-20 parts of polyethylene, 6-11 parts of lignin, 5-12 parts of cotton and linen fibers, 6-11 parts of montmorillonite, 1-3 partsof a stabilizer, 2-4 parts of a coupling agent, 1-5 parts of a plasticizer and 0.1-0.2 part of polyamide wax micropowder. The compound plastic packaging bag disclosed by the invention has good strength and toughness, and meanwhile, is good in optical performance and easy for oxydative degradation.

Description

technical field [0001] The invention belongs to the field of plastic packaging, in particular to a high toughness decomposable environment-friendly plastic packaging bag. Background technique [0002] Plastic packaging bag is a kind of packaging bag that uses plastic as raw material to produce various supplies in daily life, and is widely used in daily life and industrial production. [0003] Plastic packaging bags are consumables in daily life, and a large amount of plastic packaging bags are consumed every year. While plastic packaging bags provide convenience, due to excessive use and inadequate recycling, they also cause serious waste of energy resources and environmental pollution. In particular, ultra-thin plastic packaging bags are easily damaged, and most of them are discarded at will, becoming the main source of "white pollution". More and more countries and regions have restricted the production, sale and use of plastic packaging bags. [0004] At present, altho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/00C08L97/02C08L5/08C08L1/02C08L67/04C08L29/14C08L23/06C08L97/00C08L77/00C08K3/34B65D30/02
CPCB65D31/00C08L23/00C08L2205/025C08L2205/035C08L2205/16C08L97/02C08L5/08C08L1/02C08L67/04C08L29/14C08L23/06C08L97/005C08L77/00C08K3/346Y02W90/10
Inventor 戴王强
Owner 桐城市强峰包装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products