Biomass polyethylene film and preparation method thereof

A technology of biomass polyethylene and polyethylene, which is applied in the field of film production, can solve problems such as degradation, and achieve the effects of good mechanical properties, wide application range, and excellent biodegradability

Inactive Publication Date: 2018-03-06
HEILONGJIANG XINDA ENTERPRISE GRP
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing plastic products are widely used because they are economical, practical, and easy to process. However, due to their own nature, traditional general-purpose polymer materials are difficult to be degraded by microorganisms, that is, they will not rot and mildew, which will lead to long-term retention in existing life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Example 1: Mix 25 parts of straw powder, 65 parts of polyethylene, 2 parts of wood-plastic coupling agent, 1.5 parts of calcium stearate, 4.5 parts of maleic anhydride, and 2.5 parts of white oil, and use a twin-screw extruder to carry out For melt extrusion granulation, the temperature of each zone of the twin-screw machine is: 160°C for zone 1, 160°C for zone 2, 160°C for zone 3, 165°C for zone 4, 170°C for zone 5, 175°C for zone 6, and 180°C for the head; 100rpm respectively.

[0015] The prepared modified masterbatch is added to a film blowing machine to obtain a biomass polyethylene film through heating, extrusion, blow molding, upper drawing, lower drawing and winding to form a film. The temperature of each zone of the film blowing machine: 160°C for the first zone, 170°C for the second zone, 180°C for the third zone, 180°C for the tee, and 170°C for the die head; the screw speed is 150rpm respectively.

[0016] Performance test results: tensile strength (MPa) 40...

Embodiment 2

[0017] Mix 20 parts of straw powder, 70 parts of polyethylene, 3 parts of wood-plastic coupling agent, 2 parts of calcium stearate, 5 parts of maleic anhydride, and 3 parts of white oil, and use a twin-screw extruder for melt extrusion and granulation , The temperature of each zone of the twin-screw machine is: 160°C in the first zone, 160°C in the second zone, 160°C in the third zone, 165°C in the fourth zone, 170°C in the fifth zone, 175°C in the sixth zone, and 180°C at the head; the screw speed is 150rpm respectively.

[0018] The prepared modified masterbatch is added to a film blowing machine to obtain a biomass polyethylene film through heating, extrusion, blow molding, upper drawing, lower drawing and winding to form a film. The temperature of each zone of the film blowing machine: 160°C for the first zone, 170°C for the second zone, 180°C for the third zone, 180°C for the tee, and 170°C for the die head; the screw speed is 130rpm respectively.

[0019] Performance tes...

Embodiment 3

[0020] Mix 30 parts of straw powder, 60 parts of polyethylene, 1 part of wood-plastic coupling agent, 2 parts of calcium stearate, 4 parts of maleic anhydride, and 3 parts of white oil, and use a twin-screw extruder for melt extrusion and granulation , The temperature of each zone of the twin-screw machine is: 160°C in the first zone, 160°C in the second zone, 160°C in the third zone, 165°C in the fourth zone, 170°C in the fifth zone, 175°C in the sixth zone, and 180°C at the head; the screw speed is 200rpm respectively.

[0021] The prepared modified masterbatch is added to a film blowing machine to obtain a biomass polyethylene film through heating, extrusion, blow molding, upper drawing, lower drawing and winding to form a film. The temperature of each zone of the film blowing machine: 160°C for the first zone, 170°C for the second zone, 180°C for the third zone, 180°C for the tee, and 170°C for the die head; the screw speed is 110rpm respectively.

[0022] Performance test...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
transmittivityaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention relates to a biomass polyethylene film and a preparation method thereof, which is characterized in that plant fiber powder, polyethylene and auxiliary agents are used. The product of the invention is non-toxic and can be used for agricultural film, food packaging, disposable plastic products in daily life and the like. This product can be partially degraded by microorganisms in the natural environment, which overcomes the environmental pollution problem caused by the existing general-purpose plastic waste.

Description

technical field [0001] The invention relates to the technical field of film production, in particular to a biodegradable plant fiber powder-polyethylene film and a preparation method thereof. Background technique [0002] Existing plastic products are widely used because they are economical, practical, and easy to process. However, due to their own nature, traditional general-purpose polymer materials are difficult to be degraded by microorganisms, that is, they will not rot and mildew, which will lead to long-term retention in existing life. . Therefore, the pollution problem of plastic garbage bags is becoming more and more serious, which has attracted widespread attention all over the world. [0003] Add a certain proportion of natural fiber materials that can be degraded by microorganisms to the existing general-purpose polymer materials that cannot be degraded by microorganisms, such as rice husk powder, straw powder, corn cob powder and wheat flour, etc., to obtain pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L97/02C08K5/098
CPCC08L23/06C08L2201/06C08L2203/16C08L2205/025C08L2205/035C08L2207/062C08L2207/066C08L97/02C08K5/098
Inventor 邵锐崔成杰谢众
Owner HEILONGJIANG XINDA ENTERPRISE GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap