Super wear-resistant, fire-resistant and flame-retardant mineral floor coating and preparation method thereof

A floor coating, fire-resistant and flame-retardant technology, applied in the direction of alkali metal silicate coatings, etc., can solve problems such as not being able to meet fire-resistant requirements

Active Publication Date: 2020-06-02
河南华彩无机涂料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, after many tests, the highest fire protection level of the above patented products can only reach A2 level, which still cannot meet the increasing fire resistance demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A floor coating, consisting of the following raw materials in mass percentage: dispersant 4%, cellulose 2%, bentonite 2%, defoamer 3%, leveling agent 2%, wetting agent 3%, titanium dioxide 10% , aluminum hydroxide 10%, wollastonite powder 10%, silicon dioxide 10%, fumed silica 2%, nano silicate 15%, thickener 2% and water 25%.

[0030] The dispersant is TiloSperse6003, the defoamer is Zhongya NXZ, the leveling agent is BYK333, the wetting agent is OT75, the titanium dioxide is R706, and the thickener is TT935. The cellulose is B30K, and the bentonite is ATTAGEL50.

[0031] The preparation method of this floor paint comprises the steps,

[0032] (1) Weigh the raw materials according to the above mass percentages;

[0033] (2) Turn on the dispersing equipment, slowly add the water, cellulose, bentonite, dispersant, defoamer, leveling agent, and wetting agent in sequence, and continue to disperse for 10 minutes to obtain a coarse mixture;

[0034] (3) Add the titanium d...

Embodiment 2

[0038] A floor coating, consisting of the following raw materials in mass percentage: 2% dispersant, 4% cellulose, 1% bentonite, 1% defoamer, 1% leveling agent, 2% wetting agent, 15% titanium dioxide , aluminum hydroxide 5%, wollastonite powder 5%, silicon dioxide 20%, fumed silicon dioxide 5%, nano silicate 20%, thickener 3%, and the balance is water.

[0039] The dispersant is TiloSperse6003, the defoamer is Zhongya NXZ, the leveling agent is BYK333, the wetting agent is OT75, the titanium dioxide is R706, and the thickener is TT935. The cellulose is B30K, and the bentonite is ATTAGEL50.

[0040] The preparation method of this floor paint comprises the steps,

[0041] (1) Weigh the raw materials according to the above mass percentages;

[0042] (2) Turn on the dispersing equipment, slowly add the water, cellulose, bentonite, dispersant, defoamer, leveling agent, and wetting agent in sequence, and continue to disperse for 10 minutes to obtain a coarse mixture;

[0043] (3)...

Embodiment 3

[0047] A floor coating, consisting of the following raw materials in mass percentage: 1% dispersant, 3% cellulose, 3% bentonite, 2% defoamer, 5% leveling agent, 1% wetting agent, 5% titanium dioxide , aluminum hydroxide 5%, wollastonite powder 10%, silicon dioxide 20%, fumed silica 5%, nano silicate 20%, thickener 3% and water 17%.

[0048] The dispersant is TiloSperse6003, the defoamer is Zhongya NXZ, the leveling agent is BYK333, the wetting agent is OT75, the titanium dioxide is R706, and the thickener is TT935. The cellulose is B30K, and the bentonite is ATTAGEL50.

[0049] The preparation method of this floor paint comprises the steps,

[0050] (1) Weigh the raw materials according to the above mass percentages;

[0051] (2) Turn on the dispersing equipment, slowly add the water, cellulose, bentonite, dispersant, defoamer, leveling agent, and wetting agent in sequence, and continue to disperse for 10 minutes to obtain a coarse mixture;

[0052] (3) Add the titanium dio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
wear resistanceaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of coatings, in particular to a novel inorganic super abrasion-resistant, fireproof and flame-retardant mineral floor coating. The novel inorganic super abrasion-resistant, fireproof and flame-retardant mineral floor coating is prepared from the following raw materials in percentage by mass: 1 to 10% of dispersant, 0 to 5% of cellulose, 0 to 5% of bentonite, 0 to 3% of defoaming agent, 0 to 5% of flatting agent, 0 to 4% of wetting agent, 1 to 15% of titanium dioxide powder, 0 to 15% of aluminum hydroxide, 0 to 10% of wollastonite powder, 15 to 30% of silicon dioxide, 0 to 5% of fused silicon dioxide, 0 to 40% of nanometer silicate, 0 to 5% of thickener, and the balance of water. The novel inorganic super abrasion-resistant, fireproof and flame-retardant mineral floor coating has the advantage that the mineral (silicate) is used as a filming matter, so that the characteristics of the traditional floor coating are realized, and the super abrasion-resistant, fireproof and flame-retardant characteristics are also realized.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a novel inorganic super wear-resistant, fire-resistant and flame-retardant mineral floor coating and a preparation method thereof. Background technique [0002] Floor coatings are ground decoration materials that use epoxy resin as the main agent and add pigments, solvents, and curing agents. They have good mechanical properties, electrical insulation, and chemical corrosion resistance. They are used to protect the ground. It has the effects of dustproof, wear-resistant, clean and moisture-proof, and is widely used and promoted by modern industrial floors, commercial floors, garage floors, etc. At present, about 70% of domestic floor coatings are solvent-based coatings, which are flammable and explosive, while the proportion of safer water-based coatings is small. [0003] In recent years, with the development of the economy, higher requirements have been put forwar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/02
CPCC04B28/188C04B2111/00482C04B2111/2038C04B2111/28C04B2103/408C04B24/383C04B14/104C04B14/305C04B14/06C04B14/064C04B22/00C04B2103/50C04B2103/0068C04B2103/40C04B2103/44
Inventor 任鑫王献峰张志洲冯冠奇许鹏王彦伟
Owner 河南华彩无机涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap